Lapox ARPN-36 | K-86
Mixing ratio (Parts by weight) : 100 : 3-6 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (Tg) (oC) : 165 – 180
Lapox ARPN-42 | AH-105
Mixing ratio (Parts by weight) : 100 : 100 | Mix viscosity @ 25oC (mPa s) : 2,000 – 4,000 | Pot life @ 25oC (minutes) : 30 – 40
Lapox ARPN-54 | K-41 | K-42
Mixing ratio (Parts by weight) : 100 : 65 | Mix viscosity @ 25oC (mPa s) : 8,000 – 10,000 | Pot life @ 25oC (minutes) : 15 – 330
Lapox ART-21 | AH-326
Mixing ratio (Parts by weight) : 100 : 14 | Mix viscosity @ 25oC (mPa s) : Paste (white) | Pot life @ 25oC (minutes) : 25 – 30 | Glass transition temperature (Tg) (oC) : 75 – 85
Lapox ART-22 | AH-326
Mixing ratio (Parts by weight) : 100 : 6 | Mix viscosity @ 25oC (mPa s) : Paste (grey) | Pot life @ 25oC (minutes) : 15 – 20 | Glass transition temperature (Tg) (oC) : 85 – 95
Lapox ART-23 | AH-326
Mixing ratio (Parts by weight) : 100 : 10 | Mix viscosity @ 25oC (mPa s) : Paste (blue) | Pot life @ 25oC (minutes) : 15 – 20 | Glass transition temperature (Tg) (oC) : 75 – 85
Lapox ART-24 | AH-326
Mixing ratio (Parts by weight) : 100 : 20 | Mix viscosity @ 25oC (mPa s) : Paste (colourless) | Pot life @ 25oC (minutes) : 15 – 20 | Glass transition temperature (Tg) (oC) : 95 – 115
Lapox B-11 | AH-428
Mixing ratio (Parts by weight) : 100 : 45 | Mix viscosity @ 25oC (mPa s) : 800 – 1,200 | Pot life @ 25oC (minutes) : 30 – 40
Lapox B-11 | AH-543
Mixing ratio (Parts by weight) : 100 : 66 | Mix viscosity @ 25oC (mPa s) : 4,500 – 5,500 | Pot life @ 25oC (minutes) : 40 – 50
Lapox B-11 | K-41 | K-42
Mixing ratio (Parts by weight) : 100 : 60 | Mix viscosity @ 25oC (mPa s) : 6,000 – 8,000 | Pot life @ 25oC (minutes) : 15 – 300
Lapox B-11 | K-48
Mixing ratio (Parts by weight) : 100 : 18 | Mix viscosity @ 25oC (mPa s) : 5,000 – 7,000 | Pot life @ 25oC (minutes) : 15 – 25
Lapox B-11 | K-49
Mixing ratio (Parts by weight) : 100 : 60 | Mix viscosity @ 25oC (mPa s) : 3,000 – 4,000 | Pot life @ 25oC (minutes) : 100 – 110
Lapox B-47 | AH-416
Mixing ratio (Parts by weight) : 100 : 60 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : 40 – 50
Lapox B-47 | AH-714
Mixing ratio (Parts by weight) : 100 : 50 | Mix viscosity @ 25oC (mPa s) : 600 – 1,000 | Pot life @ 25oC (minutes) : 130 – 150
Lapox B-47 | K-41 | K-42
Mixing ratio (Parts by weight) : 100 : 60 | Mix viscosity @ 25oC (mPa s) : 3,000 – 6,000 | Pot life @ 25oC (minutes) : 35 – 330
Lapox B-47 | K-48
Mixing ratio (Parts by weight) : 100 : 18 | Mix viscosity @ 25oC (mPa s) : 600 – 700 | Pot life @ 25oC (minutes) : 15 – 25
Lapox C-1 | K-1
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (Parts by weight) : 100 : 30 | Glass transition temperature (Tg) (oC) : 115 – 130 | Thermal class : F | Applications : Instrument Transformers, Switchgears, Bushings
Lapox C-17 | K-12 | K-13 | K-14
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (Parts by weight) : 100 : 100 : 0.5 – 1.5 : 0 – 20 | Glass transition temperature (Tg) (oC) : 85 – 95 | Thermal class : F | Applications : Insulators, Bushings, Switchgears, Instrument Transformers, Dry Distribution Transformers
Lapox C-2 | K-1
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (Parts by weight) : 100 : 30 | Glass transition temperature (Tg) (oC) : 115 – 130 | Thermal class : F | Applications : Insulators, Bushings, Instrument Transformers
Lapox C-50 | K-225
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (Parts by weight) : 100 : 80 | Glass transition temperature (Tg) (oC) : 90 – 105 | Thermal class : H | Applications : Switchgears, Insulators, Bushings
Lapox C-50 | K-61
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (Parts by weight) : 100 : 80 | Glass transition temperature (Tg) (oC) : 105 – 125 | Thermal class : H | Applications : Switchgears, Insulators, Bushings
Lapox C-51 | K-6
Type of system : Unfilled | Nature : Cold cure / Indoor | Mixing ratio (Parts by weight) : 100 : 10 | Glass transition temperature (Tg) (oC) : 60 – 70 | Thermal class : B | Applications : Adhesives, Electronic assembly
Lapox C-59 | K-1
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (Parts by weight) : 100 : 30 | Glass transition temperature (Tg) (oC) : 115 – 130 | Thermal class : F | Applications : Insulators, Bushings, Switchgears, Instrument Transformers, Dry Distribution Transformers
Lapox L-12 | AH-113 | K-13
Mixing ratio (Parts by weight) : 100 : 95 : 0.5-2.0 | Mix viscosity @ 25oC (mPa s) : 1,900 – 2,100 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 165 – 185
Lapox L-12 | AH-315
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 500 – 800 | Pot life @ 25oC (hours) : 7 – 9 hr | Glass transition temperature (Tg) (oC) : 85 – 95
Lapox L-12 | AH-335
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 600 – 1,200 | Pot life @ 25oC (minutes) : 50 – 60 | Glass transition temperature (Tg) (oC) : 90 – 105
Lapox L-12 | AH-336
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 600 – 1,200 | Pot life @ 25oC (minutes) : 80 – 100 | Glass transition temperature (Tg) (oC) : 90 – 105
Lapox L-12 | AH-337
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 400 – 700 | Pot life @ 25oC (minutes) : 300 – 380 | Glass transition temperature (Tg) (oC) : 90 – 105
Lapox L-12 | AH-411
Mixing ratio (Parts by weight) : 100 : 22 | Mix viscosity @ 25oC (mPa s) : 800 – 1,200 | Pot life @ 25oC (minutes) : 90 – 120 | Glass transition temperature (Tg) (oC) : 140 – 155
Lapox L-12 | AH-422
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 1,500 – 2,500 | Pot life @ 25oC (minutes) : 300 – 350 | Glass transition temperature (Tg) (oC) : 130 – 140
Lapox L-12 | AH-667
Mixing ratio (Parts by weight) : 100 : 27 | Mix viscosity @ 50oC : 3,000 – 5,000 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 150 – 160
Lapox L-12 | K-10 | K-86
Mixing ratio (Parts by weight) : 100 : 35 : 1-3 | Pot life @ 25oC (weeks) : 6 – 8 | Glass transition temperature (Tg) (oC) : 150 – 160
Lapox L-12 | K-12 | K-13
Mixing ratio (Parts by weight) : 100 : 100 : 1-3 | Mix viscosity @ 25oC (mPa s) : 400 – 700 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 95 – 105
Lapox L-12 | K-24
Mixing ratio (Parts by weight) : 100 : 34 | Mix viscosity @ 25oC (mPa s) : 3,500 – 5,000 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 145 – 155
Lapox L-12 | K-5
Mixing ratio (Parts by weight) : 100 : 27 | Pot life @ 25oC (hours) : > 4 | Glass transition temperature (Tg) (oC) : 150 – 160
Lapox L-12 | K-5200
Mixing ratio (Parts by weight) : 100 : 24 | Mix viscosity @ 25oC (m Pas) : 4,000 – 6,000 | Pot life @ 25oC (days) : 2 – 3 | Glass transition temperature (Tg) (oC) : 180 – 190
Lapox L-12 | K-918 | K-13
Mixing ratio (Parts by weight) : 100 : 85 : 1-3 | Mix viscosity @ 25oC (m Pas) : 600 – 900 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 130 – 140
Lapox L-247 | K-918 | K-13
Mix viscosity @ 25oC : 100 : 64 : 1-3 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 110 – 120
Lapox L-67 | K-66 | K-13
Mixing ratio (Parts by weight) : 100 : 23 : 0.5-3.0 | Pot life @ 25oC (weeks) : 2 – 3 | Glass transition temperature (Tg) (oC) : 130 – 140
Lapox L-68 | K-66 | K-13
Mixing ratio (Parts by weight) : 100 : 32 : 1-3 | Pot life @ 25oC (weeks) : 2 – 3 | Glass transition temperature (Tg) (oC) : 130 – 140
Lapox XR-110 | XH-68
Mixing ratio (Parts by weight) : 100 : 100 | Mix viscosity @ 25oC (mPa s) : 3,000 – 4,000 | Pot life @ 25oC (minutes) : 25 – 35