Product Catalogue

SOLVENT CUT RESINS Atul offers solid resin solutions in various solvents. Major applications include FRP composites, industrial maintenance coatings, marine coatings, protective coatings, stoving enamels and varnishes. Lapox® EEW Viscosity1 @ 25°C Non-volatile content2 Recommendations g/eq mPa∙s % ARL-148 – 50 - 350 50 - 55 A low viscosity epoxy resin recommended for polyester film coatings along with melamine formaldehyde curing agent (AH-343). ARL-154 – 50 - 350 50 - 55 A low viscosity epoxy resin recommended for polyester film coatings to achieve high gloss and adhesion. B-7 X 80 294 - 323 600 - 850 79 - 81 (150°C/1h) A solvent cut epoxy resin recommended for high solids coatings to achieve excellent adhesion, gloss and flexibility. P-101 606 - 702 9,000 - 13,000 74 - 76 (105°C/2h) A Type 1 epoxy resin solution in xylene recommended for paint and coatings. P-101 HV 606 - 741 14,000 - 20,000 74 - 76 (105°C/2h) XR-128 12,500 2,000 - 5,000 49 - 51 (160°C/2h) A high molecular weight epoxy resin solution recommended for primers and enamels. The product improves flexibility in coating formulations. ARP-24 X 80 300 - 336 3,500 - 7,000 79 - 81 A Type 1 epoxy resin solution in xylene recommended for high solids coatings and paints. 1Brookfield viscosity 2120°C/2h *Method: EEW - ASTM D1652; Viscosity - ASTM D2196; Non-volatile content - Atul RESINS RESINS Lapox® Colour EEW Viscosity1 @ 25°C Recommendations APHA g/eq mPa∙s ARCH-11 (XR-34) Max 100 159 - 182 500 - 1,100 A cycloaliphatic epoxy resin based on HHPA recommended for electrical component castings, potting and outdoor coatings. CAS # 1395383-69-32 | 5493-45-8 ARCH-12 Max 100 180 - 200 350 - 750 A modified cycloaliphatic epoxy resin based on HHPA with low viscosity which offers good thermal shock resistance in electrical cast components. ARCH-13 Max 100 220 - 240 2,000 - 4,000 A cycloaliphaticepoxy resin based on hydrogenated Bis-A. The product is recommended for outdoor coatings, flooring, electrical castings and composite parts with high toughness. CAS # 30583-72-3 ARCH-13 LV Max 100 210 - 230 1,300 - 2,500 A high purity cycloaliphatic epoxy resin based on hydrogenated Bis-A. The product is recommended for outdoor coatings, flooring, electrical castings and composite parts with high toughness. CAS # 30583-72-3 ARCH-18 Max 100 130 - 143 250 - 450 A low viscosity cycloaliphatic epoxy resin recommended for electrical component castings, potting and outdoor coatings. CAS # 2386-87-0 CYCLOALIPHATIC RESINS Cycloaliphatic resins offer UV resistance if cured with cycloaliphatic curing agents. They are recommended for outdoor coatings, electrical castings and flooring. Diglycidyl ester of HHPA Diglycidyl ether of HBPA 3,4-Epoxycyclohexylmethyl-3,4-epoxycyclohexane carboxylate 1Brookfield viscosity 2105°C/2h 3ASTM D1544 *Method: Colour - ASTM D1209; EEW - ASTM D1652; Viscosity - ASTM D2196 Lapox® Colour EEW Viscosity1 @ 25°C Non-volatile content2 Recommendations APHA g/eq mPa∙s % ARPN-25 Max 250 172 - 179 1,100 - 1,700 @ 52°C – A low viscosity EPN resin with average 2.5 functionality recommended for composites, electrical and coating applications. ARPN-36 (L-238) Max 250 175 - 182 20,000 - 50,000 @ 52°C – A standard semi-solid EPN resin having average 3.6 functionality recommended for composites, electrical, chemical resistant coatings and flooring. ARPN-36 M 80 Max 23 (Gardner) 215 - 231 150 - 350 79 - 81 A solution of EPN resin ARPN-36 in MEK recommended for chemical resistant coatings, electrical and composite applications. ARPN-36 X 80 Max 23 (Gardner) 215 - 231 800 - 1,500 79 - 81 (150°C/1h) A solution of EPN resin ARPN-36 in xylene recommended for chemical resistant coatings, electrical and composite applications. ARPN-53 (XR-55) Max 43 (Gardner) 167 - 179 35,000 - 55,000 – A modified EPN resin with average 2.2 functionality recommended for composites, electrical and coating applications. ARPN-54 Max 33 (Gardner) 167 - 182 25,000 - 35,000 – EPOXY PHENOL NOVOLAC RESINS Epoxy phenol novolac (EPN) resins are available in varying functionalities and are recommended to achieve higher chemical and thermal resistance in various applications including adhesives, coatings, composites, electrical and flooring. Epoxy phenol novolac (EPN) 1Brookfield viscosity 2CAS # of Europe as per REACH *Method: Colour - ASTM D1209; EEW - ASTM D1652; Viscosity - ASTM D2196 ALKYL PHENOLIC RESINS Lapox® Appearance Colour Methylol content Softening point Recommendations – Gardner % °C APR-101 Pale yellow lumps Max 42 8 - 12 65 - 80 A pTBP phenolic resin offers variable open time in rubber based adhesive formulations. APR-102 Pale yellow lumps Max 62 14 - 17 90 - 100 APR-103 Dark violet lumps – 12 - 16 85 - 105 APR-104 Pale yellow lumps Max 7 8 - 12 70 - 90 An alkyl phenolic resin suitable for high temprature resistant adhesive formulations. 1Brookfield viscosity 260% solution in toluene *Method: Colour - ASTM D1544; Methylol content - ISO 354-3:1986; Softening point - ISO 1205:1978 8 9

RkJQdWJsaXNoZXIy MjA2MDI2