Found 103 results for Formulations group

Lapox A-16 | AH-717

Mixing ratio (Parts by weight) : 100 : 80 | Mix viscosity @ 25oC (mPa s) : 15,000 – 20,000 | Pot life @ 25oC (minutes) : 150 – 200

Lapox A-16 | AH-800

Mixing ratio (Parts by weight) : 100 : 100 | Mix viscosity @ 25oC (mPa s) : Thixotropic | Pot life @ 25oC (minutes) : 3 – 7

Lapox A-16 | K-5

Mixing ratio (Parts by weight) : 100 : 27 | Pot life @ 25oC (minutes) : 170 – 190

Lapox A-16 | K-6

Mixing ratio (Parts by weight) : 100 : 10 | Mix viscosity @ 25oC (mPa s) : 4,000 – 6,000 | Pot life @ 25oC (minutes) : 20 – 30

Lapox A-31 AH-717

Mixing ratio (Parts by weight) : 100 : 80 | Mix viscosity @ 25oC (mPa s) : 25,000 – 40,000 | Pot life @ 25oC (minutes) : 130 – 150

Lapox A-35 | K-35

Mixing ratio (Parts by weight) : 100 : 30 | Mix viscosity @ 25oC (mPa s) : 400 – 500 | Pot life @ 25oC (minutes) : > 60

Lapox A-38 | K-99

Mixing ratio (Parts by weight) : 100 : 40 | Mix viscosity @ 25oC (mPa s) : 50,000 – 1,00,000 | Pot life @ 25oC (minutes) : 20 – 25

Lapox A-53 | K-6

Mixing ratio (Parts by weight) : 100 : 10 | Mix viscosity @ 25oC (mPa s) : 600 – 800 | Pot life @ 25oC (minutes) : 30 – 60

Lapox A-555 | K-555

Mixing ratio (Parts by weight) : 100 : 80 | Mix viscosity @ 25oC (mPa s) : 75,000 – 1,25,000 | Pot life @ 25oC (minutes) : 8 – 10

Lapox A-83 | K-83

Mixing ratio (Parts by weight) : 100 : 40 | Mix viscosity @ 25oC (mPa s) : Thixotropic | Pot life @ 25oC (minutes) : 35 – 45

Lapox ARA-12 | AH-718

Mixing ratio (Parts by weight) : 100 : 80 | Mix viscosity @ 25oC (mPa s) : 32,000 – 37,000 | Pot life @ 25oC (minutes) : 90 – 105

Lapox ARA-17 | AH-354

Mixing ratio (Parts by weight) : 100 : 80 | Mix viscosity @ 25oC (mPa s) : 75,000 – 1,25,000 | Pot life @ 25oC (minutes) : 8 – 10

Lapox ARA-30 | AH-735

Mixing ratio (Parts by weight) : 100 : 50 | Mix viscosity @ 25oC (mPa s) : 50,000 – 1,00,000 | Pot life @ 25oC (minutes) : 35 – 50

Lapox ARB-22 | AH-416

Mixing ratio (Parts by weight) : 100 : 55 | Mix viscosity @ 25oC (mPa s) : 500 – 700 | Pot life @ 25oC (minutes) : 45 – 60

Lapox ARB-22 | AH-428

Mixing ratio (Parts by weight) : 100 : 43 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : 30 – 35

Lapox ARB-26 | AH-416

Mixing ratio (Parts by weight) : 100 : 60 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : 40 – 50

Lapox ARC-15 | AH-122

Type of system : Pre-filled | Nature : Hot cure / Indoor| Mixing ratio (Parts by weight) : 100 : 100 | Glass transition temperature (Tg) (oC) : 110 – 120 | Thermal class : H | Applications : Switchgears, Insulators, Bushings

Lapox ARC-16 | AH-118 | ADP-11

Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (Parts by weight) : 100 : 80 : 0 – 8 |  Glass transition temperature (Tg) (oC) : 105 – 115 | Thermal class : F | Applications : Switchgears, Insulators, Bushings, Instrument Transformers, Dry Distribution Transformers

Lapox ARC-18 | AH-123

Type of system : Pre-filled | Nature : Hot cure / Indoor | Mixing ratio (Parts by weight) : 100 : 25 | Glass transition temperature (Tg) (oC) : 122 – 132 | Thermal class : F | Applications : Switchgears, Insulators, Bushings

Lapox ARC-30 | AH-714

Type of system : Pre-filled | Nature : Cold cure / Indoor | Mixing ratio (Parts by weight) : 100 : 25 | Glass transition temperature (Tg) (oC) : 60 – 70 | Thermal class : B | Applications : Instrument Transformers, Electronic assembly

Lapox ARC-31 | AH-114 | AC-13

Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (Parts by weight) : 100 : 100 : 0.0 – 0.2 | Glass transition temperature (Tg) (oC) : 90 – 100 | Thermal class : F | Applications : Dry Distribution Transformers, Electronic assembly, Rotating machines

Lapox ARC-35 | AH-676

Type of system : Pre-filled | Nature : Hot cure / Indoor | Mixing ratio (Parts by weight) : 100 : 26 | Glass transition temperature (Tg) (oC) : 70 – 80 | Thermal class : F | Applications : Electronic assembly

Lapox ARCH-11 | AH-214 | K-13

Type of system : Unfilled | Nature : Hot cure Outdoor | Mixing ratio (Parts by weight) : 100 : 90 : 0.5 – 2.0 | Glass transition temperature (Tg) (oC) : 100 – 110 | Thermal class : F | Applications : Switchgears, Insulators, Bushings, Instrument Transformers

Lapox ARCH-11 | AH-215

Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio (Parts by weight): 100 : 90 |  Glass transition temperature (Tg) (oC) : 100 – 110 | Thermal class : F | Applications : Switchgears, Insulators, Bushings, Instrument Transformers

Lapox ARCH-11 | K-3 | K-13

Mixing ratio (Parts by weight) : 100 : 85 : 1-3 | Mix viscosity @ 25oC (mPa s) : 200 – 500 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) oC : 105 – 115

Lapox ARCH-12 | AH-214 | K-13

Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio (Parts by weight) : 100 : 80 : 0.5 : 2.0 | Glass transition temperature (Tg) (oC) : 75 – 85 | Thermal class : F | Applications : Switchgears, Insulators, Bushings

Lapox ARCH-12 | AH-215

Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio (Parts by weight) : 100 : 80 | Glass transition temperature (Tg) (oC) : 75 – 85 | Thermal class : F | Applications : Switchgears, Insulators, Bushings

Lapox ARCH-13 | AH-215

Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio (Parts by weight) : 100 : 70 | Glass transition temperature (Tg) (oC) : 100 – 110 | Thermal class : F | Applications : Switchgears, Insulators, Bushings

Lapox ARF-11 | K-918 | K-13

Mixing ratio (Parts by weight) : 100 : 90 : 1-3 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 115 – 130

Lapox ARL-111 | AH-358 | ARS-101

Type of system : Unfilled | Nature : Hot cure Indoor | Mixing ratio (Parts by weight) : 100 : 15 | Glass transition temperature (Tg) (oC) : 80 – 90 | Thermal class : F | Applications : Paper coating

Lapox ARL-12 | AH-714

Mixing ratio (Parts by weight) : 100 : 50 | Mix viscosity @ 25oC (mPa s) : 1,200 – 1,500 | Pot life @ 25oC (minutes) : 120 – 150 | Glass transition temperature (Tg) (oC) : 55 – 65

Lapox ARL-125 | AH-365GL

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 200 – 300 | Pot life @ 25oC (minutes) : 50 – 60 | Glass transition temperature (Tg) (oC) : 75 – 85

Lapox ARL-125 | AH-367GL

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 300 – 700 | Pot life @ 25oC (minutes) : 300 – 380 | Glass transition temperature (Tg) (oC) : 75 – 85

Lapox ARL-135 | AH-332

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (m Pas) : 700 – 1,200 | Pot life @ 25oC (minutes) : 8 – 14 | Glass transition temperature (Tg) (oC) : 80 – 90

Lapox ARL-135 | AH-333

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (m Pas) : 700 – 1,200 | Pot life @ 25oC (minutes) : 14 – 20 | Glass transition temperature (Tg) (oC) : 80 – 90

Lapox ARL-135 | AH-334GL

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 700 – 1,200 | Pot life @ 25oC (minutes) : 25 – 35 | Glass transition temperature (Tg) (oC) : 80 – 90

Lapox ARL-135 | AH-335

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 500 – 700 | Pot life @ 25oC (minutes) : 50 – 60 | Glass transition temperature (Tg) (oC) : 75 – 85

Lapox ARL-135 | AH-336

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 500 – 700 | Pot life @ 25oC (minutes) : 80 – 100 | Glass transition temperature (Tg) (oC) : 75 – 85

Lapox ARL-135 | AH-337

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : 300 – 380 | Glass transition temperature (Tg) (oC) : 75 – 85

Lapox ARL-135 LV | AH-332

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (m Pas) : 600 – 800 | Pot life @ 25oC (minutes) : 8 – 14 | Glass transition temperature (Tg) (oC) : 75 – 85

Lapox ARL-135 LV | AH-333

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 700 – 1,200 | Pot life @ 25oC (minutes) : 14 – 20 | Glass transition temperature (Tg) (oC) : 80 – 90

Lapox ARL-135 LV | AH-334

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (m Pas) : 600 – 750 | Pot life @ 25oC (minutes) : 25 – 35 | Glass transition temperature (Tg) (oC) : 75 – 85

Lapox ARL-135 LV | AH-337

Mix viscosity @ 25oC : 200 – 300 | Pot life @ 25oC (minutes) : 300 – 380 | Glass transition temperature (Tg) (oC) : 75 – 85

Lapox ARL-135 LV | AH-335

Mix viscosity @ 25oC (mPa s) : 300 – 700 | Pot life @ 25oC (minutes) : 50 – 60 | Glass transition temperature (Tg) (oC) : 75 – 85

Lapox ARL-135 LV | AH-336

Mix viscosity @ 25oC (mPa s) : 300 – 700 | Pot life @ 25oC (minutes) : 80 – 100 | Glass transition temperature (Tg) (oC) : 75 – 85

Lapox ARL-135LV | AH-411

Mixing ratio (Parts by weight) : 100 : 24 | Mix viscosity @ 25oC (mPa s) : 250 – 400 | Pot life @ 25oC (minutes) : 90 – 120 | Glass transition temperature (Tg) (oC) : 125 – 135

Lapox ARL-135LV | AH-422

Mixing ratio (Parts by weight) : 100 : 35 | Mix viscosity @ 25oC (mPa s) : 400 – 600 | Pot life @ 25oC (minutes) : 300 – 350 | Glass transition temperature (Tg) (oC) : 110 – 120

Lapox ARL-136 | AH-126

Mixing ratio (Parts by weight) : 100 : 90 | Mix viscosity @ 25oC (mPa s) : 300 – 600 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 115 – 125

Lapox ARL-138 | AH-339

Mixing ratio (Parts by weight) : 100 : 30 | Mix viscosity @ 25oC (mPa s) : 400 – 600 | Pot life @ 25oC (minutes) : 120 – 180 | Glass transition temperature (Tg) (oC) : 130 – 140

Lapox ARL-138 | AH-417

Mix viscosity @ 25oC : 200 – 300 | Pot life @ 25oC (minutes) : 90 – 120 | Glass transition temperature (Tg) (oC) : 100 – 110