Found 29 results for Electrical and Electronics
Lapox ARC-15 / AH-122
Type of system : Pre-filled | Nature : Hot cure Indoor | Mixing ratio (parts by weight) : 100 : 100 | Glass transition temperature (Tg) (oC) : 110 - 120 | Thermal class : H
Lapox ARC-16 / AH-118 / ADP-11
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (parts by weight) : 100 : 80 : 0 - 8 | Glass transition temperature (Tg) (oC) : 105 - 115 | Thermal class : F
Lapox ARC-18 / AH-123
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (parts by weight) : 100 : 25 | Glass transition temperature (Tg) (oC) : 122 - 132 | Thermal class : F
Lapox ARC-30 / AH-714
Type of system : Pre-filled | Nature : Cold cure / Indoor | Mixing ratio (Parts by weight) : 100 : 25 | Glass transition temperature (Tg) (oC) : 60 - 70 | Thermal class : B
Lapox ARC-31 / AH-114 / AC-13
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (Parts by weight) : 100 : 100 : 0.0 - 0.2 | Glass transition temperature (Tg) (oC) : 90 - 100 | Thermal class : F
Lapox ARC-35 AH-676
Type of system : Pre-filled | Nature : Hot cure / Indoor | Mixing ratio (parts by weight) : 100 : 26 | Glass transition temperature (Tg) (oC) : 70 - 80 | Thermal class : F
Lapox ARCH-11 / AH-214 / K-13
Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio : 100 : 90 : 0.5 - 2.0 | Mix viscosity : 1,000/80 | Glass transition temperature (Tg) (oC): 100 - 110 | Thermal class : F
Lapox ARCH-11 / AH-215
Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio (Parts by weight) : 100 : 90 | Glass transition temperature (Tg) (oC): 100 - 110 | Thermal class : F
Lapox ARCH-11 / K-3 / K-13
Mixing ratio (Parts by weight) : 100 : 85 : 1-3 | Mix viscosity @ 25oC (mPa s) : 200 - 500 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 105 - 115
Lapox ARCH-12 / AH-214 / K-13
Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio : 100 : 80 : 0.5 - 2.0 | Glass transition temperature (Tg) (oC) : 75 - 85 | Thermal class : F
Lapox ARCH-12 / AH-215
Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio : 100 : 80 | Glass transition temperature (Tg) (oC) : 75 - 85 | Thermal class : F
Lapox ARCH-13 / AH-215
Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio (Parts by weight) : 100 : 70 | Glass transition temperature (Tg) (oC) : 100 - 110 | Thermal class : F
Lapox ARF-11 / K-918 / K-13
Mixing ratio (Parts by weight) : 100 : 90 : 1-3 | Mix viscosity @ 25oC (mPa s) : 300 - 500 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 115 - 130
Lapox ARL-111 / AH-358 / ARS-101
Type of system : Unfilled | Nature : Hot cure Indoor | Voltage class : MV / HV | Mixing ratio (parts by weight) : 100 : 15 | Glass transition temperature (Tg) (oC) : 80 - 90 | Thermal class : F
Lapox ARPN-36 / K-10 / K-86
Mixing ratio (Parts by weight) : 100 : 32-40 : 1-3 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (Tg) (oC) : 170 - 185
Lapox ARPN-36 / K-86
Mixing ratio (Parts by weight) : 100 : 3-6 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (Tg) (oC) : 165 - 180
Lapox C-1 / K-1
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (parts by weight) : 100 : 30 | Glass transition temperature (Tg) (oC) : 115 - 130 | Thermal class : F
Lapox C-17 / K-12 / K-13 / K-14
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio : 100 : 100 : 0.5 - 1.5 : 0 - 20 | Glass transition temperature (Tg) (oC): 85 - 95 | Thermal class : F
Lapox C-2 / K-1
Type of system : Unfilled | Nature : Hot cure / Indoo | Mixing ratio (parts by weight) : 100 : 30 | Glass transition temperature (Tg) (oC) : 115 - 130 | Thermal class : F
Lapox C-50 / K-225
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio : 100 : 80 | Glass transition temperature (Tg) (oC) : 90 - 105 | Thermal class : H