Lapox ARC-15 | AH-122
Type of system : Pre-filled | Nature : Hot cure Indoor | Mixing ratio (parts by weight) : 100 : 100 | Glass transition temperature (Tg) (oC) : 110 – 120 | Thermal class : H
Lapox ARC-16 | AH-118 | ADP-11
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (parts by weight) : 100 : 80 : 0 – 8 | Glass transition temperature (Tg) (oC) : 105 – 115 | Thermal class : F
Lapox ARC-18 | AH-123
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (parts by weight) : 100 : 25 | Glass transition temperature (Tg) (oC) : 122 – 132 | Thermal class : F
Lapox ARC-30 | AH-714
Type of system : Pre-filled | Nature : Cold cure / Indoor | Mixing ratio (Parts by weight) : 100 : 25 | Glass transition temperature (Tg) (oC) : 60 – 70 | Thermal class : B
Lapox ARC-31 | AH-114 | AC-13
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (Parts by weight) : 100 : 100 : 0.0 – 0.2 | Glass transition temperature (Tg) (oC) : 90 – 100 | Thermal class : F
Lapox ARC-35 AH-676
Type of system : Pre-filled | Nature : Hot cure / Indoor | Mixing ratio (parts by weight) : 100 : 26 | Glass transition temperature (Tg) (oC) : 70 – 80 | Thermal class : F
Lapox ARCH-11 | AH-214 | K-13
Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio : 100 : 90 : 0.5 – 2.0 | Mix viscosity : 1,000/80 | Glass transition temperature (Tg) (oC): 100 – 110 | Thermal class : F
Lapox ARCH-11 | AH-215
Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio (Parts by weight) : 100 : 90 | Glass transition temperature (Tg) (oC): 100 – 110 | Thermal class : F
Lapox ARCH-11 | K-3 | K-13
Mixing ratio (Parts by weight) : 100 : 85 : 1-3 | Mix viscosity @ 25oC (mPa s) : 200 – 500 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 105 – 115
Lapox ARCH-12 | AH-214 | K-13
Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio : 100 : 80 : 0.5 – 2.0 | Glass transition temperature (Tg) (oC) : 75 – 85 | Thermal class : F
Lapox ARCH-12 | AH-215
Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio : 100 : 80 | Glass transition temperature (Tg) (oC) : 75 – 85 | Thermal class : F
Lapox ARCH-13 | AH-215
Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio (Parts by weight) : 100 : 70 | Glass transition temperature (Tg) (oC) : 100 – 110 | Thermal class : F
Lapox ARF-11 | K-918 | K-13
Mixing ratio (Parts by weight) : 100 : 90 : 1-3 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 115 – 130
Lapox ARL-111 | AH-358 | ARS-101
Type of system : Unfilled | Nature : Hot cure Indoor | Voltage class : MV / HV | Mixing ratio (parts by weight) : 100 : 15 | Glass transition temperature (Tg) (oC) : 80 – 90 | Thermal class : F
Lapox ARPN-36 | K-10 | K-86
Mixing ratio (Parts by weight) : 100 : 32-40 : 1-3 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (Tg) (oC) : 170 – 185
Lapox ARPN-36 | K-86
Mixing ratio (Parts by weight) : 100 : 3-6 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (Tg) (oC) : 165 – 180
Lapox C-1 | K-1
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (parts by weight) : 100 : 30 | Glass transition temperature (Tg) (oC) : 115 – 130 | Thermal class : F
Lapox C-17 | K-12 | K-13 | K-14
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio : 100 : 100 : 0.5 – 1.5 : 0 – 20 | Glass transition temperature (Tg) (oC): 85 – 95 | Thermal class : F
Lapox C-2 | K-1
Type of system : Unfilled | Nature : Hot cure / Indoo | Mixing ratio (parts by weight) : 100 : 30 | Glass transition temperature (Tg) (oC) : 115 – 130 | Thermal class : F
Lapox C-50 | K-225
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio : 100 : 80 | Glass transition temperature (Tg) (oC) : 90 – 105 | Thermal class : H
Lapox C-50 | K-61
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio : 100 : 80 | Glass transition temperature (Tg) (oC): 105 – 125 | Thermal class : H
Lapox C-51 | K-6
Type of system : Unfilled | Nature : Cold cure / Indoor | Mixing ratio (Parts by weight) : 100 : 10 | Glass transition temperature (Tg) (oC) : 60 – 70
Lapox C-59 | K-1
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (Parts by weight) : 100 : 30 | Glass transition temperature (Tg) (oC) : 115 – 130 | Thermal class : F
Lapox L-12 | AH-113 | K-13
Mixing ratio (Parts by weight) : 100 : 95 : 0.5-2.0 | Mix viscosity @ 25oC (mPa s) : 1,900 – 2,100 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 165 – 185
Lapox L-12 | K-10 | K-86
Mixing ratio (Parts by weight) : 100 : 35 : 1-3 | Pot life @ 25oC (weeks) : 6 – 8 weeks | Glass transition temperature (Tg) (oC) : 150 – 160
Lapox L-12 | K-918 | K-13
Mixing ratio (Parts by weight) : 100 : 85 : 1-3 | Mix viscosity @ 25oC (mPa s) : 600 – 900 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 130 – 140
Lapox L-247 | K-918 | K-13
Mixing ratio (Parts by weight) : 100 : 64 : 1-3 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 110 – 120
Lapox L-67 | K-66 | K-13
Mixing ratio (Parts by weight) : 100 : 23 : 0.5-3.0 | Pot life @ 25oC (weeks) : 2 – 3 | Glass transition temperature (Tg) (oC) : 130 – 140
Lapox L-68 | K-66 | K-13
Mixing ratio (Parts by weight) : 100 : 32 : 1-3 | Pot life @ 25oC (weeks) : 2 – 3 | Glass transition temperature (Tg) (oC) : 130 – 140