Lapox B-42 (ARB-19)
Colour (APHA) : Max 100 | Epoxy equivalent weight (g/eq) : 182 – 200 | Viscosity @ 25oC (mPa.s) : 5,000 – 6,500
Lapox B-47 (ARB-18)
Colour (APHA) : Max 100 | Epoxy equivalent weight (g/eq) : 177 – 187 | Viscosity @ 25oC (mPa.s) : 450 – 650
Lapox B-47 | AH-416
Mixing ratio (Parts by weight) : 100 : 60 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : 40 – 50
Lapox B-47 | AH-714
Mixing ratio (Parts by weight) : 100 : 50 | Mix viscosity @ 25oC (mPa s) : 600 – 1,000 | Pot life @ 25oC (minutes) : 130 – 150
Lapox B-47
Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 5.20 – 5.50 | Viscosity @ 25oC (mPa s) : 450 – 650
Lapox B-47 | K-41 | K-42
Mixing ratio (Parts by weight) : 100 : 60 | Mix viscosity @ 25oC (mPa s) : 3,000 – 6,000 | Pot life @ 25oC (minutes) : 35 – 330
Lapox B-47 | K-48
Mixing ratio (Parts by weight) : 100 : 18 | Mix viscosity @ 25oC (mPa s) : 600 – 700 | Pot life @ 25oC (minutes) : 15 – 25
Lapox B-7
Colour (APHA) : Max 100 | Epoxy equivalent weight (g/eq) : 225 – 280 | Viscosity @ 25oC (mPa.s) : 450 – 800
Lapox B-7 X 80
Epoxy equivalent weight (g/eq) : 294 – 323 | Viscosity @ 25oC (mPa.s) : 600 – 850 | Non-volatile content (%) : 79 – 81 (150oC/1h)
Lapox B-770
Colour (APHA) : Max 100 | Epoxy equivalent weight (g/eq) : 280 – 300 | Viscosity @ 25oC (mPa.s) : 500 – 1,500
Lapox B-9
Colour (APHA) : Max 100 | Epoxy equivalent weight (g/eq) : 180 – 187 | Viscosity @ 25oC (mPa.s) : 8,000 – 11,000 | CAS # : 1675-54-3 | 25068-38-6
Lapox C-1 | K-1
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (Parts by weight) : 100 : 30 | Glass transition temperature (Tg) (oC) : 115 – 130 | Thermal class : F | Applications : Instrument Transformers, Switchgears, Bushings
Lapox C-17 | K-12 | K-13 | K-14
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (Parts by weight) : 100 : 100 : 0.5 – 1.5 : 0 – 20 | Glass transition temperature (Tg) (oC) : 85 – 95 | Thermal class : F | Applications : Insulators, Bushings, Switchgears, Instrument Transformers, Dry Distribution Transformers
Lapox C-2 | K-1
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (Parts by weight) : 100 : 30 | Glass transition temperature (Tg) (oC) : 115 – 130 | Thermal class : F | Applications : Insulators, Bushings, Instrument Transformers
Lapox C-50 | K-225
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (Parts by weight) : 100 : 80 | Glass transition temperature (Tg) (oC) : 90 – 105 | Thermal class : H | Applications : Switchgears, Insulators, Bushings
Lapox C-50 | K-61
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (Parts by weight) : 100 : 80 | Glass transition temperature (Tg) (oC) : 105 – 125 | Thermal class : H | Applications : Switchgears, Insulators, Bushings
Lapox C-51 | K-6
Type of system : Unfilled | Nature : Cold cure / Indoor | Mixing ratio (Parts by weight) : 100 : 10 | Glass transition temperature (Tg) (oC) : 60 – 70 | Thermal class : B | Applications : Adhesives, Electronic assembly
Lapox C-59 | K-1
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (Parts by weight) : 100 : 30 | Glass transition temperature (Tg) (oC) : 115 – 130 | Thermal class : F | Applications : Insulators, Bushings, Switchgears, Instrument Transformers, Dry Distribution Transformers
Lapox K-105
Colour (Gardner) : Black | Viscosity @ 25oC (mPa.s) : 3,000 – 6,000 | Pot life @ 25oC (minutes) : Min 20 | Mixing ratio (Parts by weight) : 100 (with resin ARB-28)
Lapox K-112
Appearance : Clear brown liquid | Viscosity @ 25oC (mPa.s) : 1,000 – 1,800
Lapox K-302
Colour (Gardner) : Max 2 | Viscosity @ 25oC (mPa.s) : 300 – 600 | Amine value (mg KOH/g) : 260 – 310 | Pot life @ 25oC (minutes) : 40 – 50 | Mixing ratio (Parts by weight) : 50
Lapox K-306
Colour (Gardner) : Clear liquid | Viscosity @ 25oC (mPa.s) : 850 – 1,200 | Mixing ratio (Parts by weight) : 100 (with resin ARL-148)
Lapox K-41
Appearance : Brown liquid | Colour (Gardner) : Max 13 | Viscosity @ 25oC (mPa.s): 3,800 – 5,800 | Amine value (Eq/kg) : 4.70 – 5.10| Mixing ratio (Parts by weight) : 60
Lapox K-42
Appearance : Dark brown liquid | Colour (Gardner) : Max 16 | Viscosity @ 25oC (mPa.s) : 15,000 – 21,000 | Amine value (Eq/kg) : 4.40 – 4.80 | Mixing ratio (Parts by weight) : 60
Lapox K-450
Appearance : Dark brown liquid (solidifies upon storage) | Viscosity @ 40oC (mPa.s) : 250 – 400 | Amine value (mg KOH/g) : 430 – 450 | Mixing ratio (Parts by weight) : 34
Lapox K-49
Appearance : Brown liquid | Colour (Gardner) : Max 13 | Viscosity @ 25oC (mPa.s) : 700 – 900 | Amine value (Eq/kg) : 4.70 – 5.00 | Mixing ratio (Parts by weight) : 60
Lapox K-5
Appearance : White to tan pastilles | Mixing ratio (Parts by weight) : 26
Lapox K-54 (AH-356)
Colour (Gardner) : Max 2 | Viscosity @ 25oC (mPa.s) : 2,900 – 3,600 | Amine value (mg KOH/g) : 398 – 415
|Pot life @ 25oC (minutes) : 15 – 30 | Mixing ratio (Parts by weight) : 35
Lapox K-6
Colour (Gardner) : Max 3 | Viscosity @ 25oC (mPa.s) : – | Pot life @ 25oC (minutes) : 30 – 40 | Mixing ratio (Parts by weight) : 10 – 12
Lapox K-7
Colour (Gardner) : Max 5 | Viscosity @ 25oC (mPa.s) : Max 10 | Pot life @ 25oC (minutes) : 20 – 25 | Mixing ratio (Parts by weight) : 10 – 12
Lapox K-86
Appearance : White crystalline powder | Melting Point (oC) : Min 75
Lapox K-92
Appearance : Brown liquid | Colour (Gardner) : Max 13 | Viscosity @ 25oC (mPa.s) : 5,000 – 7,500 | Amine value (Eq/kg) : 4.40 – 5.10 | Mixing ratio (Parts by weight) : 60
Lapox L-12 | AH-113 | K-13
Mixing ratio (Parts by weight) : 100 : 95 : 0.5-2.0 | Mix viscosity @ 25oC (mPa s) : 1,900 – 2,100 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 165 – 185
Lapox L-12 | AH-315
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 500 – 800 | Pot life @ 25oC (hours) : 7 – 9 hr | Glass transition temperature (Tg) (oC) : 85 – 95
Lapox L-12 | AH-335
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 600 – 1,200 | Pot life @ 25oC (minutes) : 50 – 60 | Glass transition temperature (Tg) (oC) : 90 – 105
Lapox L-12 | AH-336
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 600 – 1,200 | Pot life @ 25oC (minutes) : 80 – 100 | Glass transition temperature (Tg) (oC) : 90 – 105
Lapox L-12 | AH-337
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 400 – 700 | Pot life @ 25oC (minutes) : 300 – 380 | Glass transition temperature (Tg) (oC) : 90 – 105
Lapox L-12 | AH-411
Mixing ratio (Parts by weight) : 100 : 22 | Mix viscosity @ 25oC (mPa s) : 800 – 1,200 | Pot life @ 25oC (minutes) : 90 – 120 | Glass transition temperature (Tg) (oC) : 140 – 155
Lapox L-12 | AH-422
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 1,500 – 2,500 | Pot life @ 25oC (minutes) : 300 – 350 | Glass transition temperature (Tg) (oC) : 130 – 140
Lapox L-12 | AH-667
Mixing ratio (Parts by weight) : 100 : 27 | Mix viscosity @ 50oC : 3,000 – 5,000 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 150 – 160
Lapox L-12 | K-10 | K-86
Mixing ratio (Parts by weight) : 100 : 35 : 1-3 | Pot life @ 25oC (weeks) : 6 – 8 | Glass transition temperature (Tg) (oC) : 150 – 160
Lapox L-12 | K-12 | K-13
Mixing ratio (Parts by weight) : 100 : 100 : 1-3 | Mix viscosity @ 25oC (mPa s) : 400 – 700 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 95 – 105
Lapox L-12 | K-24
Mixing ratio (Parts by weight) : 100 : 34 | Mix viscosity @ 25oC (mPa s) : 3,500 – 5,000 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 145 – 155
Lapox L-12 | K-5
Mixing ratio (Parts by weight) : 100 : 27 | Pot life @ 25oC (hours) : > 4 | Glass transition temperature (Tg) (oC) : 150 – 160
Lapox L-12 | K-5200
Mixing ratio (Parts by weight) : 100 : 24 | Mix viscosity @ 25oC (m Pas) : 4,000 – 6,000 | Pot life @ 25oC (days) : 2 – 3 | Glass transition temperature (Tg) (oC) : 180 – 190
Lapox L-12 | K-918 | K-13
Mixing ratio (Parts by weight) : 100 : 85 : 1-3 | Mix viscosity @ 25oC (m Pas) : 600 – 900 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 130 – 140
Lapox L-247
Epoxy equivalent weight (g/eq) : 250 – 280 | Viscosity @ 25oC (mPa.s) : 700 – 1,100 | Bromine content (%) : 21 – 26
Lapox L-247 | K-918 | K-13
Mix viscosity @ 25oC : 100 : 64 : 1-3 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 110 – 120
Lapox L-249
Epoxy equivalent weight (g/eq) : 319 – 410 | Bromine content (%) : 44 – 48
Lapox L-67 | K-66 | K-13
Mixing ratio (Parts by weight) : 100 : 23 : 0.5-3.0 | Pot life @ 25oC (weeks) : 2 – 3 | Glass transition temperature (Tg) (oC) : 130 – 140