Type of system : Pre-filled | Nature : Hot cure Indoor | Voltage class : MV / HV | Mixing ratio (parts by weight) : 100 : 100 | Glass transition temperature (Tg) (oc) : 110 – 120 | Thermal class : H


Type of system : Unfilled | Nature : Hot cure / Indoor | Voltage class : MV / HV | Mixing ratio (parts by weight) : 100 : 80 : 0 – 8 | Glass transition temperature (Tg) (oc) : 105 – 115 | Thermal class : F


Type of system : Unfilled | Nature : Hot cure / Indoor | Voltage class : MV / HV | Mixing ratio (parts by weight) : 100 : 25 | Glass transition temperature (Tg) (o>C) : 122 – 132 | Thermal class : F


Type of system : Pre-filled | Nature : Cold cure / Indoor | Voltage class : LV | Mixing ratio (Parts by weight) : 100 : 25 | Glass transition temperature (Tg) (oC) : 60 – 70 | Thermal class : B


Type of system : Unfilled | Nature : Hot cure / Indoor | Voltage class : MV / HV | Mixing ratio (Parts by weight) : 100 : 100 : 0.0 – 0.2 | Glass transition temperature (Tg) (oC) : 90 – 100 | Thermal class : F


Type of system : Pre-filled | Nature : Hot cure / Indoor | Voltage class : MV / HV | Mixing ratio (parts by weight) : 100 : 26 | Glass transition temperature (Tg) (oC) : 70 – 80 | Thermal class : F


Type of system : Unfilled | Nature : Hot cure / Outdoor | Voltage class : MV / HV | Mixing ratio : 100 : 90 : 0.5 – 2.0 | Mix viscosity : 1,000/80 | Glass transition temperature : 100 – 110 | Thermal class : F


Type of system : Unfilled | Nature : Hot cure / Outdoor | Voltage class : MV / HV | Mixing ratio (Parts by weight) : 100 : 90 | Glass transition temperature (Tg) (oC): 100 – 110 | Thermal class : F


Type of system : Unfilled | Nature : Hot cure / Outdoor | Voltage class : MV / HV | Mixing ratio : 100 : 80 : 0.5 – 2.0 | Glass transition temperature (Tg) : 75 – 85 | Thermal class : F


Type of system : Unfilled | Nature : Hot cure / Outdoor | Voltage class : MV / HV | Mixing ratio : 100 : 80 | Glass transition temperature (Tg) : 75 – 85 | Thermal class : F


Type of system : Unfilled | Nature : Hot cure / Outdoor | Voltage class : MV | Mixing ratio (Parts by weight) : 100 : 70 | Glass transition temperature (Tg) : 100 – 110 | Thermal class : F


Type of system : Unfilled | Nature : Hot cure Indoor | Voltage class : MV / HV | Mixing ratio (parts by weight) : 100 : 15 | Glass transition temperature (Tg) (oC) : 80 – 90 | Thermal class : F


Type of system : Unfilled | Nature : Hot cure / Indoor | Voltage class : MV / HV | Mixing ratio (parts by weight) : 100 : 30 | Glass transition temperature (Tg) (oC) : 115 – 130 | Thermal class : F


Type of system : Unfilled | Nature : Hot cure / Indoor | Voltage class : MV / HV | Mixing ratio : 100 : 100 : 0.5 – 1.5 : 0 – 20 | Glass transition temperature (Tg) (oC): 85 – 95 | Thermal class : F


Type of system : Unfilled | Nature : Hot cure / Indoo | Voltage class : MV / HV | Mixing ratio (parts by weight) : 100 : 30 | Glass transition temperature (Tg) (oC) : 115 – 130 | Thermal class : F


Type of system : Unfilled | Nature : Hot cure / Indoor | Voltage class : MV / HV | Mixing ratio : 100 : 80 | Glass transition temperature (Tg) (oC) : 90 – 105 | Thermal class : H


Type of system : Unfilled | Nature : Hot cure / Indoor | Voltage class : MV / HV | Mixing ratio : 100 : 80 | Glass transition temperature (Tg) (oC): 105 – 125 | Thermal class : H


Type of system : Unfilled | Nature : Hot cure / Indoor | Voltage class : MV / HV | Mixing ratio (Parts by weight) : 100 : 30 | Glass transition temperature (Tg) (oC) : 115 – 130 | Thermal class : F