Composites Industry

Appearance : White crystal | Melting point (^oC) : 154 – 156

Appearance : White crystal | Melting point (^oC) : Min 127 – 134

Appearance : Clear liquid | Colour (Gardner) : Max 2 | Viscosity @ 25^oC (mPa s) : Max 10

Appearance : Clear liquid | Colour (Gardner) : Max 1 | Viscosity @ 25^oC (mPa s) : 10 – 30

Appearance : Brown liquid or solid | Viscosity @ 25^oC (mPa s) : Max 100 | Melting point (^oC) : 36 – 42

Chemistry : 3,3’-Dimethyl-4,4’-diaminodicyclohexyl methane | Viscosity @ 25^oC (mPa s) : 100 – 140

Chemistry : 4,4′-Diaminodicyclohexyl methane | Appearance : Colourless transparent liquid | Melting point (^oC) : 35 – 37

Appearance : Light yellow to brown liquid | Viscosity @ 25^oC (mPa s) : 100 – 300

Chemistry : 4,4′-Diaminodiphenyl methane | Appearance : Viscous brownish liquid | Viscosity @ 60^oC (mPa s) : 1,200 – 2,200

Colour (Gardner) : Yellow powder | Melting point (^oC) : 155 – 158

Colour (Gardner) : Yellow solid | Viscosity @ 100^oC (mPa s) : 1,000 – 7,000 | Softening point (^oC) : 60 – 80

Colour (Gardner) : Yellowish liquid | Solid content (%) : 74 – 76 | Viscosity @ 25^oC (mPa s) : 100 – 400

Colour (Gardner) : Yellow solid | Viscosity @ 125^oC (mPa s) : 50 – 500

Mixing ratio (Parts by weight) : 100 : 85 : 1-3 | Mix viscosity @ 25^oC (mPa s) : 200 – 500 | Pot life @ 25^oC (minutes) : > 8 | Glass transition temperature (Tg) ^oC : 105 – 115

Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 6.20 – 6.80 | Viscosity @ 25^oC (mPa s) : 15 – 30 | HyCl (%) : Max 0.15

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 2.90 – 3.20 | Viscosity @ 25^oC (mPa s) : 40 – 90 | HyCl (%) : Max 0.15

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 7.00 – 8.00 | Viscosity @ 25^oC (mPa s) : 100 – 200 | HyCl (%) : Max 0.15

Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 6.90 – 8.00 | Viscosity @ 25^oC (mPa s) : 12 – 18 | HyCl (%) : Max 0.10

Colour (Gardner) : Max 16 | Epoxy value (Eq/kg) : 8.15 – 9.50 | Viscosity @ 25^oC (mPa s) : 100 – 200

Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 5.20 – 6.20 | Viscosity @ 25^oC (mPa s) : 20 – 50 | HyCl (%) : Max 0.20

Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 7.00 – 7.80 | Viscosity @ 25^oC (mPa s) : 10 – 22 | HyCl (%) : Max 0.15

Mixing ratio (Parts by weight) : 100 : 90 : 1-3 | Mix viscosity @ 25^oC (mPa s) : 300 – 500 | Pot life @ 25^oC (minutes) : > 8 | Glass transition temperature (Tg) ^oC : 115 – 130

Mixing ratio (Parts by weight) : 100 : 50 | Mix viscosity @ 25^oC (mPa s) : 1,200 – 1,500 | Pot life @ 25^oC (minutes) : 120 – 150 | Glass transition temperature (Tg) ^oC : 55 – 65

Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 5.26 – 5.55 | Viscosity @ 25^oC (mPa s) : 9,000 – 12,000

Mixing ratio (Parts by weight) : 100:32 | Mix viscosity @ 25^oC (mPa s) : 600 – 800 | Pot life @ 25^oC (minutes) : 8 – 14 | Glass transition temperature (Tg) ^oC : 80 – 90

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25^oC (mPa s) : 600 – 750 | Pot life @ 25^oC (minutes) : 14 – 20 | Glass transition temperature (Tg) (^oC) : 80 – 90

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25^oC (mPa s) : 600 – 750 | Pot life @ 25^oC (minutes) : 25 – 35 | Glass transition temperature (Tg) (^oC) : 80 – 90

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25^oC (mPa s) : 300 – 700 | Pot life @ 25^oC (minutes) : 50 – 60 | Glass transition temperature (Tg) (^oC) : 75 – 85

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25^oC (mPa s) : 300 – 700 | Pot life @ 25^oC (minutes) : 80 – 100 | Glass transition temperature (Tg) (^oC) : 75 – 85

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25^oC (mPa s) : 300 – 700 | Pot life @ 25^oC (minutes) : 50 – 60 | Glass transition temperature (Tg)(^oC) : 75 – 85

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25^oC (mPa s) : 200 – 300 | Pot life @ 25^oC (minutes) : 300 – 380 | Glass transition temperature (Tg) (^oC) : 75 – 85

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25^oC (mPa s) : 200 – 300 | Pot life @ 25^oC (minutes) : 350 – 450 | Glass transition temperature (Tg) (^oC) : 75 – 85

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25^oC (mPa s) : 700 – 1200 | Pot life @ 25^oC (minutes) : 8 – 14 | Glass transition temperature (Tg) (^oC) : 80 – 90

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25^oC (mPa s) : 700 – 1200 | Pot life @ 25^oC (minutes) : 14 – 20 | Glass transition temperature (Tg) (^oC) : 80 – 90

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25^oC (mPa s) : 700 – 1200 | Pot life @ 25^oC (minutes) : 25 – 35 | Glass transition temperature (Tg) (^oC) : 80 – 90

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25^oC (mPa s) : 500 – 700 | Pot life @ 25^oC (minutes) : 50 – 60 | Glass transition temperature (Tg) (^oC) : 75 – 85

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25^oC (mPa s) : 500 – 700 | Pot life @ 25^oC (minutes) : 80 – 100 | Glass transition temperature (Tg) (^oC) : 75 – 85

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25^oC (mPa s) : 300 – 500 | Pot life @ 25^oC (minutes) : 300 – 380 | Glass transition temperature (Tg) (^oC) : 75 – 85

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25^oC (mPa s) : 600 – 750 | Pot life @ 25^oC (minutes) : 25 – 35 | Glass transition temperature (Tg) (^oC) : 75 – 85

Mixing ratio (Parts by weight) : 100 : 35 | Mix viscosity @ 25^oC (mPa s) : 400 – 600 | Pot life @ 25^oC (minutes) : 300 – 350 | Glass transition temperature (Tg) (^oC) : 110 – 120

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25^oC (mPa s) : 600 – 800 | Pot life @ 25^oC (minutes) : 8 – 14 | Glass transition temperature (Tg) (^oC) : 75 – 85

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25^oC (mPa s) : 600 – 750 | Pot life @ 25^oC (minutes) : 14 – 20 | Glass transition temperature (Tg) (^oC) : 75 – 85

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25^oC (mPa s) : 300 – 700 | Pot life @ 25^oC (minutes) : 50 – 60 | Glass transition temperature (Tg) (^oC) : 75 – 85

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25^oC (mPa s) : 300 – 700 | Pot life @ 25^oC (minutes) : 80 – 100 | Glass transition temperature (Tg) (^oC) : 75 – 85

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25^oC (mPa s) : 200 – 300 | Pot life @ 25^oC (minutes) : 300 – 380 | Glass transition temperature (Tg) (^oC) : 75 – 85

Mixing ratio (Parts by weight) : 100 : 24 | Mix viscosity @ 25^oC (mPa s) : 250 – 400 | Pot life @ 25^oC (minutes) : 90 – 120 | Glass transition temperature (Tg) (^oC) : 125 – 135

Mixing ratio (Parts by weight) : 100 : 90 | Mix viscosity @ 25^oC (mPa s) : 300 – 600 | Pot life @ 25^oC (minutes) : > 8 | Glass transition temperature (Tg) (^oC) : 115 – 125

Mixing ratio (Parts by weight) : 100 : 30 | Mix viscosity @ 25^oC (mPa s) : 400 – 600 | Pot life @ 25^oC (minutes) : 120 – 180 | Glass transition temperature (Tg) (^oC) : 130 – 140

Mixing ratio (Parts by weight) : 100 : 30 | Mix viscosity @ 25^oC (mPa s) : 200 – 300 | Pot life @ 25^oC (minutes) : 90 – 120 | Glass transition temperature (Tg) (^oC) : 100 – 110

Mixing ratio (Parts by weight) : 100 : 42 | Mix viscosity @ 25^oC (mPa s) : 2,500 – 3,000 | Pot life @ 25^oC (minutes) : 600 – 700 | Glass transition temperature (Tg) (^oC) : 190 – 220

Mixing ratio (Parts by weight) : 100 : 15 | Mix viscosity @ 25oC (mPa s) : 3,500 – 5,000 | Pot life @ 25^oC (minutes) : 20 – 25 | Glass transition temperature (Tg) (^oC) : 95 – 105

Mixing ratio (Parts by weight) : 100 : 15 | Mix viscosity @ 25oC (mPa s) : 3,500 – 5,000 | Pot life @ 25^oC (minutes) : 85 – 95 | Glass transition temperature (Tg) (^oC) : 95 – 105

Colour (APHA) : Max 50 | Epoxy value (Eq/kg) : 5.71 – 5.95 | Viscosity @ 25^oC (mPa s) : 4,000 – 5,000

Mixing ratio (Parts by weight) : 100 : 42 | Mix viscosity @ 25^oC (mPa s) : 300 – 500 | Pot life @ 25^oC (minutes) : 600 – 700 | Glass transition temperature (Tg) (^oC) : 170 – 200

Mixing ratio (Parts by weight) : 100 : 15 : 2 | Pot life @ 25^oC (hours) : > 8 | Glass transition temperature (Tg) (^oC) : 155 – 165

Mixing ratio (Parts by weight) : 100 : 40 | Pot life @ 25^oC (hours) : > 8 | Glass transition temperature (Tg) (^oC) : 180 – 200

Mixing ratio (Parts by weight) : 100 : 15 : 1-3 | Pot life @ 25^oC (hours) : > 8 | Glass transition temperature (Tg) (^oC) : 110 – 120

Mixing ratio (Parts by weight) : 100 : 5 | Pot life @ 25^oC (hours) : > 8 | Glass transition temperature (Tg) (^oC) : 110 – 120

Colour (Gardner) : Max 16 | Epoxy value (Eq/kg) : 6.50 – 7.50 | Viscosity @ 50^oC (mPa s) : 1,000 – 2,500

Colour (Gardner) : Max 3 | Epoxy value (Eq/kg) : 5.59 – 5.81 | Viscosity @ 52^oC (mPa s) : 1,100 – 1,700

Mixing ratio (Parts by weight) : 100 : 32-40 : 1-3 | Pot life @ 25^oC (hours) : > 8 | Glass transition temperature (Tg) (^oC) : 170 – 185

Mixing ratio (Parts by weight) : 100 : 3-6 | Pot life @ 25^oC (hours) : > 8 | Glass transition temperature (Tg) (^oC) : 165 – 180

Colour (Gardner) : Max 4 | Epoxy value (Eq/kg) : 5.12 – 6.10 | Viscosity @ 50^oC (mPa s) : 100 – 350

Mixing ratio (Parts by weight) : 100 : 14 | Mix viscosity @ 25^oC (mPa s) : Paste (white) | Pot life @ 25^oC (minutes) : 25 – 30 | Glass transition temperature (Tg) (^oC) : 75 – 85

Mixing ratio (Parts by weight) : 100 : 6 | Mix viscosity @ 25^oC (mPa s) : Paste (grey) | Pot life @ 25^oC (minutes) : 15 – 20 | Glass transition temperature (Tg) (^oC) : 85 – 95

Mixing ratio (Parts by weight) : 100 : 10 | Mix viscosity @ 25^oC (mPa s) : Paste (blue) | Pot life @ 25^oC (minutes) : 15 – 20 | Glass transition temperature (Tg) (^oC) : 75 – 85

Mixing ratio (Parts by weight) : 100 : 20 | Mix viscosity @ 25^oC (mPa s) : Paste (colourless) | Pot life @ 25^oC (minutes) : 15 – 20 | Glass transition temperature (Tg) (^oC) : 95 – 115

Colour (Gardner) : Max 12 | Epoxy value (Eq/kg) : 7.46 – 8.55 | Viscosity @ 50^oC (mPa s) : 7,000 – 11,000

Colour (Gardner) : Max 12 | Epoxy value (Eq/kg) : 7.46 – 8.55 | Viscosity @ 50^oC (mPa s) : 10,000 – 12,000

Colour (Gardner) : Max 12 | Epoxy value (Eq/kg) : 7.46 – 8.55 | Viscosity @ 50^oC (mPa s) : 111,000 – 13,000

Colour (Gardner) : Max 12 | Epoxy value (Eq/kg) : 7.46 – 8.55 | Viscosity @ 50^oC (mPa s) : 13,000-15,000

Colour (Gardner) : Max 12 | Epoxy value (Eq/kg) : 7.46 – 8.55 | Viscosity @ 50^oC (mPa s) : 17,000-19,000

Colour (Gardner) : Max 12 | Epoxy value (Eq/kg) : 7.46 – 8.55 | Viscosity @ 50^oC (mPa s) : 7,000-19,000

Colour (Gardner) : Max 12 | Epoxy value (Eq/kg) : 8.55 – 9.00 | Viscosity @ 50^oC (mPa s) : 3,000 – 6,000

Colour (Gardner) : Max 7 | Epoxy value (Eq/kg) : 7.52 – 8.47 | Viscosity @ 25^oC (mPa s) : 7,000 – 12,000

Colour (Gardner) : Max 13 | Epoxy value (Eq/kg) : 5.88 – 6.66 | Viscosity @ 150^oC (mPa s) : 30 – 50

Epoxy value (Eq/kg) : 8.70 – 9.50 | Viscosity @ 25^oC (mPa s) : 2,000 – 5,000

Epoxy value (Eq/kg) : 9.40 – 10.50 | Viscosity @ 25^oC (mPa s) : 550 – 850

Epoxy value (Eq/kg) : 9.10 – 9.80 | Viscosity @ 25^oC (mPa s) : 7,000 – 13,000

Epoxy value (Eq/kg) : 9.80 – 10.6 | Viscosity @ 25^oC (mPa s) : 1,500 – 4,800

Colour (Gardner) : Max 16 | Epoxy value (Eq/kg) : 4.17 – 4.44 | Viscosity @ 85^oC (mPa s) : 1,000 – 1,500

Chemistry : 4,4′-Diaminodiphenyl sulfone | Appearance : White to off-white powder | Melting point (^oC) : 176 – 185

Chemistry : 4,4′-Diaminodiphenyl sulfone Free Flow | Appearance : White to off-white powder | Melting point (^oC) : 176 – 185

Chemistry : 4,4′-Diaminodiphenyl sulfone Micronised | Appearance : White to off-white powder | Melting point (^oC) : 176 – 180

Chemistry : 3,3′-Diaminodiphenyl sulfone | Appearance : White to brownish white powder | Melting point (^oC) : 167 – 175

Chemistry : 3,3′-Diaminodiphenyl sulfone Micronised | Appearance : Off-white to yellowish brown powder | Melting point (^oC) : 167 – 175

Appearance : Clear brown liquid | Viscosity @ 25^oC (mPa s) : 1,000 – 1,800

Chemistry : 3,3′-Diethyl-4,4′-diaminodiphenyl methane| Appearance : Dark brown liquid | Viscosity @ 40^oC (mPa s) : 250 – 400

Chemistry : 4,4′-Diaminodiphenyl methane | Appearance : Off-white to brown pastilles | Melting point (^oC) : 88 – 92

Appearance : White crystalline powder | Melting point (^oC) : Min 75

Mixing ratio (Parts by weight) : 100 : 95 : 0.5-2.0 | Mix viscosity @ 25^oC (mPa s) : 1,900 – 2,100 | Pot life @ 25^oC (minutes) : > 8 | Glass transition temperature (Tg) (^oC) : 165 – 185

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25^oC (mPa s) : 500 – 800 | Pot life @ 25^oC (minutes) : 7 – 9 hr | Glass transition temperature (Tg) ^oC : 85 – 95

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25^oC (mPa s) : 600 – 1,200 | Pot life @ 25^oC (minutes) : 50 – 60 | Glass transition temperature (Tg) ^oC : 90 – 105

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25^oC (mPa s) : 600 – 1,200 | Pot life @ 25^oC (minutes) : 80 – 100 | Glass transition temperature (Tg) ^oC : 90 – 105

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25^oC (mPa s) : 400 – 700 | Pot life @ 25^oC (minutes) : 300 – 380 | Glass transition temperature (Tg) ^oC : 90 – 105

Mixing ratio (Parts by weight) : 100 : 22 | Mix viscosity @ 25^oC (mPa s) : 800 – 1,200 | Pot life @ 25^oC (minutes) : 90 – 120 | Glass transition temperature (Tg) (^oC) : 140 – 155

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25^oC (mPa s) : 1,500 – 2,500 | Pot life @ 25^oC (minutes) : 300 – 350 | Glass transition temperature (Tg) (^oC) : 130 – 140

Mixing ratio (Parts by weight) : 100 : 27 | Mix viscosity @ 50^oC (mPa s) : 3,000 – 5,000 | Pot life @ 25^oC (minutes) : > 8 | Glass transition temperature (Tg) (^oC) : 150 – 160

Mixing ratio (Parts by weight) : 100 : 35 : 1-3 | Pot life @ 25^oC (weeks) : 6 – 8 weeks | Glass transition temperature (Tg) (^oC) : 150 – 160

Mixing ratio (Parts by weight) : 100 : 100 : 1-3 | Mix viscosity @ 25^oC (mPa s) : 400 – 700 | Pot life @ 25^oC (minutes) : > 8 | Glass transition temperature (Tg) (^oC) : 95 – 105

Mixing ratio (Parts by weight) : 100 : 34 | Mix viscosity @ 25^oC (mPa s) : 3,500 – 5,000 | Pot life @ 25^oC (minutes) : > 8 | Glass transition temperature (Tg) ^oC : 145 – 155

Mixing ratio (Parts by weight) : 100 : 27 | Pot life @ 25^oC (hours) : > 4 | Glass transition temperature (Tg) (^oC) : 150 – 160

Mixing ratio (Parts by weight) : 100 : 85 : 1-3 | Mix viscosity @ 25^oC (mPa s) : 600 – 900 | Pot life @ 25^oC (minutes) : > 8 | Glass transition temperature (Tg) (^oC) : 130 – 140

Mixing ratio (Parts by weight) : 100 : 64 : 1-3 | Pot life @ 25^oC (minutes) : > 8 | Glass transition temperature (Tg) (^oC) : 110 – 120

Mixing ratio (Parts by weight) : 100 : 38 | Mix viscosity @ 25^oC (mPa s) : 600 – 700 | Pot life @ 25^oC (minutes) : 110 – 160 | Glass transition temperature (Tg) (^o) : 115 – 130

Mixing ratio (Parts by weight) : 100 : 23 : 0.5-3.0 | Pot life @ 25^oC (weeks) : 2 – 3 | Glass transition temperature (Tg) (^oC) : 130 – 140

Mixing ratio (Parts by weight) : 100 : 32 : 1-3 | Pot life @ 25^oC (weeks) : 2 – 3 | Glass transition temperature (Tg) (^oC) : 130 – 140