Mixing ratio (Parts by weight) : 100 : 38 | Mix viscosity @ 25oC (mPa s) : 600 – 700 | Pot life @ 25oC (minutes) : 110 – 160 | Glass transition temperature (Tg) (o) : 115 – 130
Updates
Month: August 2017
Lapox ARD-57 (XR-104) | aerospace, aromatic-difunctional, aniline based reactive diluent, high performance composite
Colour (Gardner) : Max 16 | Epoxy value (Eq/kg) : 8.15 – 9.50 | Viscosity @ 25oC (mPa s) : 100 – 200
Posted in PO PM Industry
Lapox P-3 (ARP-11) | Bisphenol-A based solid resins. Type 1, protective coating, enamels
Epoxy value (Eq/kg) : 2.15 – 2.22 | Viscosity @ 25oC (mPa s) : 160 – 190 | Softening point (oC) : 65 – 75 |
Posted in PO PM Industry
Lapox ARCH-13 | AH-215
Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio (Parts by weight) : 100 : 70 | Glass transition temperature (Tg) (oC) : 100 – 110 | Thermal class : F
Posted in PO PM Industry
Lapox ARC-16 | AH-118 | ADP-11 | Electrical and Electronics, Bushings, Conventional Vacuum Casting, Pre-filled, Hot cure Indoor
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (parts by weight) : 100 : 80 : 0 – 8 | Glass transition temperature (Tg) (oC) : 105 – 115 | Thermal class :…
Posted in PO PM Industry
Lapox ARL-135 LV | AH-334 | automotive, RTM, hand lay-up and infusion systems, low viscosity system, variable pot life
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 600 – 750 | Pot life @ 25oC (minutes) : 25 – 35 | Glass transition temperature (Tg) (oC) : 75 – 85
Posted in PO PM Industry
Lapox AH-618 (K-5200) | Aromatic amine; long pot life; Elevated temperature curing curing agent; high glass transition temperature; high Tg
Appearance : Yellow to brown liquid | Colour (Gardner) : Max 15 | Viscosity @ 25oC (mPa.s) : 100 – 300 | Amine value (mg KOH/g) : 628 – 634 | Mixing ratio (Parts by weight) : 24
Posted in PO PM Product
Lapox AH-315 | adhesives; casting; coating; composite applications; protective coatings; unmodified polyamine curing agent
Colour (Gardner) : Max 1 | Viscosity @ 25oC (mPa.s) : 5 – 15 | Pot life @ 25oC (hours) : 7 – 9 | Mixing ratio (Parts by weight) : 32
Posted in PO PM Product