Updates

Month: June 2017

Lapox XR-110 | XH-68 | cable joints; composite adhesive

Mixing ratio (Parts by weight) : 100 : 100 | Mix viscosity @ 25oC (mPa s) : 3,000 – 4,000 | Pot life @ 25oC (minutes) : 25 – 35

Posted in PO PM Product

Lapox A-16 | AH-800 | rapid cure; similar substrate; dissimilar substrate; composite adhesive

Mixing ratio (Parts by weight) : 100 : 100 | Mix viscosity @ 25oC (mPa s) : Thixotropic | Pot life @ 25oC (minutes) : 3 – 7

Posted in PO PM Product

Lapox ARCH-11 | K-3 | K-13 | industrial; filament winding and pultrusion; hot cure system; out door application; UV resistance

Mixing ratio (Parts by weight) : 100 : 85 : 1-3 | Mix viscosity @ 25oC (mPa s) : 200 – 500 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) oC : 105 –

Posted in PO PM Product

Lapox A-83 | K-83 | gap filling; standard adhesive; composite adhesive

Mixing ratio (Parts by weight) : 100 : 40 | Mix viscosity @ 25oC (mPa s) : Thixotropic | Pot life @ 25oC (minutes) : 35 – 45

Posted in PO PM Product

Lapox B-11 | K-48 | construction; Maintenance; repair; crack-filling; quick setting

Mixing ratio (Parts by weight) : 100 : 18 | Mix viscosity @ 25oC (mPa s) : 5,000 – 7,000 | Pot life @ 25oC (minutes) : 15 – 25

Posted in PO PM Product

Lapox B-47 | K-48 | construction; Maintenance; grouting; quick setting. excellent adhesion; good strength

Mixing ratio (Parts by weight) : 100 : 18 | Mix viscosity @ 25oC (mPa s) : 600 – 700 | Pot life @ 25oC (minutes) : 15 – 25

Posted in PO PM Product

Lapox B-11 | K-49 | construction; Maintenance; chemical resistant flooring; protection of metal structures; protection from corrosive chemicals; protection from alkali; protection from solvents

Mixing ratio (Parts by weight) : 100 : 60 | Mix viscosity @ 25oC (mPa s) : 3,000 – 4,000 | Pot life @ 25oC (minutes) : 100 – 110

Posted in PO PM Product

Lapox B-11 | K-41 | K-42 | construction; Maintenance; chemical resistant flooring; variable potlife system; excellent acid and alkali resistance

Mixing ratio (Parts by weight) : 100 : 60 | Mix viscosity @ 25oC (mPa s) : 6,000 – 8,000 | Pot life @ 25oC (minutes) : 15 – 300

Posted in PO PM Product

Lapox ARPN-54 | K-41 | K-42 | construction; Maintenance; chemical resistant flooring; high viscosity system; variable pot life system; chemical resistance; industrial flooring

Mixing ratio (Parts by weight) : 100 : 65 | Mix viscosity @ 25oC (mPa s) : 8,000 – 10,000 | Pot life @ 25oC (minutes) : 15 – 330

Posted in PO PM Product

Lapox ARPN-42 | AH-105 | construction; Maintenance; chemical resistant flooring; coal tar modified system; coating of pipes; vehile chassis; concrete structure

Mixing ratio (Parts by weight) : 100 : 100 | Mix viscosity @ 25oC (mPa s) : 2,000 – 4,000 | Pot life @ 25oC (minutes) : 30 – 40

Posted in PO PM Product

Lapox B-47 | AH-416 | Maintenance; self-leveling system; low viscosity system; excellent gloss; excellent hardness; moderate chemical resistance

Mixing ratio (Parts by weight) : 100 : 60 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : 40 – 50

Posted in PO PM Product

Lapox B-11 | AH-428 | Maintenance; self-leveling system; moderate viscosity system; excellent gloos; good chemical resistance; construction

Mixing ratio (Parts by weight) : 100 : 45 | Mix viscosity @ 25oC (mPa s) : 800 – 1,200 | Pot life @ 25oC (minutes) : 30 – 40

Posted in PO PM Product

Lapox ARB-26 | AH-416 | Maintenance; self-leveling system; low viscosity system; high gloss finish

Mixing ratio (Parts by weight) : 100 : 60 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : 40 – 50

Posted in PO PM Product

Lapox ARB-22 | AH-428 | Maintenance; self-leveling system; long pot life; excellent mechanical properties; construction

Mixing ratio (Parts by weight) : 100 : 43 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : 30 – 35

Posted in PO PM Product

Lapox ARB-22 | AH-416 | Maintenance; self-leveling system; long pot life; excellent mechanical properties; construction

Mixing ratio (Parts by weight) : 100 : 55 | Mix viscosity @ 25oC (mPa s) : 500 – 700 | Pot life @ 25oC (minutes) : 45 – 60

Posted in PO PM Product

Lapox B-47 | K-41 | K-42 | Maintenance; mortar; screed; varying pot life; excellent chemical resistance; construction

Mixing ratio (Parts by weight) : 100 : 60 | Mix viscosity @ 25oC (mPa s) : 3,000 – 6,000 | Pot life @ 25oC (minutes) : 35 – 330

Posted in PO PM Product

Lapox B-47 | AH-714 | Maintenance; primer; low viscosity primer system; general application; construction

Mixing ratio (Parts by weight) : 100 : 50 | Mix viscosity @ 25oC (mPa s) : 600 – 1,000 | Pot life @ 25oC (minutes) : 130 – 150

Posted in PO PM Product

Lapox B-11 | AH-543 | Maintenance; primer; very low temperature curing; curing in high humidity; moist surface; construction

Mixing ratio (Parts by weight) : 100 : 66 | Mix viscosity @ 25oC (mPa s) : 4,500 – 5,500 | Pot life @ 25oC (minutes) : 40 – 50

Posted in PO PM Product

Lapox ARA-30 | AH-735 | structural adhesive; high lap shear strength; composite adhesive

Mixing ratio (Parts by weight) : 100 : 50 | Mix viscosity @ 25oC (mPa s) : 50,000 – 1,00,000 | Pot life @ 25oC (minutes) : 35 – 50

Posted in PO PM Product

Lapox ARA-17 | AH-354 | toughness; quick; composite adhesive

Mixing ratio (Parts by weight) : 100 : 80 | Mix viscosity @ 25oC (mPa s) : 75,000 – 1,25,000 | Pot life @ 25oC (minutes) : 8 – 10

Posted in PO PM Product

Lapox ARL-140 | AH-419 | industrial; tooling; laminating system; high Tg; high glass transition temperature; dimensional stability

Mixing ratio (Parts by weight) : 100 : 42 | Mix viscosity @ 25oC (mPa s) : 2,500 – 3,000 | Pot life @ 25oC (minutes) : 600 – 700 | Glass transition temperature (Tg) (oC) : 190 – 220

Posted in PO PM Product

Lapox ARL-138 | AH-339 | industrial; tooling; laminating system; standard tooling system; excellent Tg; excellent glass transition temperature

Mixing ratio (Parts by weight) : 100 : 30 | Mix viscosity @ 25oC (mPa s) : 400 – 600 | Pot life @ 25oC (minutes) : 120 – 180 | Glass transition temperature (Tg) (oC) : 130 – 140

Posted in PO PM Product

Lapox ART-24 | AH-326 | industrial; tooling; gel coat system; colourless gel coat system

Mixing ratio (Parts by weight) : 100 : 20 | Mix viscosity @ 25oC (mPa s) : Paste (colourless) | Pot life @ 25oC (minutes) : 15 – 20 | Glass transition temperature (Tg) (oC) : 95 – 115

Posted in PO PM Product

Lapox ART-23 | AH-326 | industrial; tooling; gel coat system; high hardness; high abrasion resistance; good finish

Mixing ratio (Parts by weight) : 100 : 10 | Mix viscosity @ 25oC (mPa s) : Paste (blue) | Pot life @ 25oC (minutes) : 15 – 20 | Glass transition temperature (Tg) (oC) : 75 – 85

Posted in PO PM Product

Lapox ART-22 | AH-326 | industrial; tooling; gel coat system; high thermal conductivity; excellent hardness; excellent surface finish

Mixing ratio (Parts by weight) : 100 : 6 | Mix viscosity @ 25oC (mPa s) : Paste (grey) | Pot life @ 25oC (minutes) : 15 – 20 | Glass transition temperature (Tg) (oC) : 85 – 95

Posted in PO PM Product

Lapox ART-21 | AH-326 | industrial; tooling; gel coat system; general purpose

Mixing ratio (Parts by weight) : 100 : 14 | Mix viscosity @ 25oC (mPa s) : Paste (white) | Pot life @ 25oC (minutes) : 25 – 30 | Glass transition temperature (Tg) (oC) : 75 – 85

Posted in PO PM Product

Lapox ARTF-15 | aerospace, multifunctional resin, medium viscosity, specialty resin, MDA based

Colour (Gardner) : Max 12 | Epoxy value (Eq/kg) : 7.46 – 8.55 | Viscosity @ 50oC (mPa s) : 111,000 – 13,000

Posted in PO PM Industry

Cresol mixture | Phenol mixture

A cost effective substitute for cresylic acid and phenol.

Posted in Aromatics

TULACTV Navy CC | CAS No. Reactive Blue 250

An economical trichromatic navy dye with good dischargeability. The product is used to develop medium to dark shades.

Posted in Colors

TULACTIV Blue CC

A trichromatic blue dye with good dischargeability.

Posted in Colors

TULACTIV Ultra Carmine CC

A deep red dye used for scarlet, dark red, brown and burgundy shades.

Posted in Colors

TULACTIV Ultra Red CC

A red dye with high tinctorial strength and excellent build-up properties. The product is used to develop medium to dark shades.

Posted in Colors

TULACTIV Deep Red CC

A bluish red dye with high tinctorial strength.

Posted in Colors

TULACTIV Red CC

An economical bluish red dye used in trichromatic combinations.

Posted in Colors

TULACTIV Ultra Yellow CC

A golden yellow dye with high tinctorial strength used to develop deep shades with good all round fastness properties.

Posted in Colors

TULACTIV Yellow CC

A basic trichromatic golden yellow dye with good dischargeability.

Posted in Colors

TULAREVS Blue LF-R

A blue dye with good light fastness properties used for pale to medium shades.

Posted in Colors

TULAREVS Red LF-2B

A red dye with good light fastness properties used for pale to medium shades.

Posted in Colors

TULAREVS Yellow LF-2R

A yellow dye with good light fastness properties used for pale to medium shades.

Posted in Colors

TULAREVS Black B Conc (133%) | CAS No. Reactive Black 5

An economical navy dye with good build-up properties.

Posted in Colors

TULACTIV Black RL | CAS No. Reactive Black 31

A black dye used to develop black to grey shades. The product has good light fastness properties.

Posted in Colors

TULACTIV Turquoise H2GP | CAS No. Reactive Blue 77

A turquoise dye with good build-up properties.

Posted in Colors

TULACTIV Turquoise G (90%) | CAS No. Reactive Blue 21 133

A turquoise dye with good build-up properties.

Posted in Colors

TULACTIV Blue R (100%) | CAS No. Reactive Blue 19

A brilliant reddish blue dye used to develop bright royal blue shades.

Posted in Colors

TULACTIV Blue BB | CAS No. Reactive Blue 220

A trichromatic blue dye with good fastness properties. The product has good dischargeability.

Posted in Colors

TULACTIV Violet 5R | CAS No. Reactive Violet 5

A bright violet dye used for various shades of violet.

Posted in Colors

TULACTIV Red BS | CAS No. Reactive Red 111

An economical bluish red dye used for medium and dark shades.

Posted in Colors

TULACTIV Red RB | CAS No. Reactive Red 198

An economical trichromatic red dye.

Posted in Colors

TULACTIV Red 5 B | CAS No. Reactive Red 35

An economical trichromatic red dye with high tinctorial strength.

Posted in Colors

TULACTIV Orange 3R | CAS No. Reactive Orange 16

A bright orange dye used for orange and scarlet shades.

Posted in Colors

TULACTIV Orange 2R

An economical orange dye.

Posted in Colors

TULACTIV Yellow RNL | CAS No. Reactive Yellow 107

An economical golden yellow dye used in trichromatic combinations.

Posted in Colors

TULACTIV Yellow R | CAS No. Reactive Orange 201

A bright yellow dye used in tertiary combinations with good light fastness properties.

Posted in Colors

TULACTIV Yellow FG | CAS No. Reactive Yellow 42

A yellow dye with all round fastness properties.

Posted in Colors

NOVATIC Grey 2305 MD

An ideal grey component with excellent performance in Exhaust and Continuous dyeing applications by Soft flow and Pad Dry Pad steam techniques. The product has good all round fastness properties. It is available in Microperle and Micro disperse varieties.

Posted in Colors

NOVATIC Navy DS MD

A navy dye with excellent build-up properties used for coloration of workwear and institutional wear. The product is used in combination with Yellow 3R and Jade Green XBN for Exhaust application. It shows minimum shade change when used with flame

Posted in Colors

Xantho – Hexaconazole 5% EC | Xantho; Hexaconazole

A systemic fungicide with protective and curative action used to control broad spectrum fungal diseases in various field crops and fruits.

Posted in Crop Protection Brands

Rugo – 2,4-D Ethyl Ester 38% EC | 2,4-D | 2,4-D Ethyl ester | Rugo

A selective and systemic post-emergence herbicide readily absorbed by leaves. The product is used to control annual and perennial broad-leaved weeds in a range of crops.

Posted in Crop Protection Brands

para Cresol (UHP- Ultra high purity) | CAS No. 106-44-5 | 4-Methylphenol; p-Hydroxytoluene; p-Methylphenol; 4-Hydroxytoluene

A high purity grade of para Cresol for niche applications.

Posted in Aromatics

para Cresol | CAS No. 106-44-5 | 4-Methylphenol; p-Hydroxytoluene; p-Methylphenol; 4-Hydroxytoluene

A starting ingredient in most versatile phenolic group antioxidants.

Posted in Aromatics

Ambrettolide | CAS No. 28645-51-4 | 9-Hexadecenoic acid; 16-hydroxy-; o-lactone; Oxacycloheptadec-10-en-2-one

A naturally sourced aroma ingredient with a musk-like profile.

Posted in Aromatics

Skatole | CAS No. 83-34-1 | 3-Methyl-1H indole; Beta-methyl indole; 3-Methyl-4; 5-benzopyrrole

A key ingredient in specialty fragrance formulations.

Posted in Aromatics

Phenyl acetic acid | CAS No. 103-82-2 | Phenylethanoic acid; 2-Phenylacetic acid; α-Toluic acid; Benzeneacetic acid

An intermediate widely used by the Pharmaceuticals and Crop Protection Chemicals industry.

Posted in Aromatics

para Anisyl propanal | CAS No. 5462-06-6 | Hydrocinnamaldehyde p-methoxy- α –methyl 4-Methoxy-α-Methylbenzenepropanal 3-(4-methoxyphenyl)-2-methylpropanal 2-Methyl-3-(4-methoxyphenyl)propanal

An aroma ingredient with sweet, floral, fennel and basil-like, mildly fruity odour. The product finds a major application in oral care products, flavours and fragrances.

Posted in Aromatics

para Methoxy phenyl acetic acid | CAS No. 104-01-8 | 4-Methoxybenzeneacetic acid; Homoanisic acid; p-Anisylacetic acid

A key building block for Dextromethorphan, a widely used formulation to treat cough and cold.

Posted in Aromatics

Lapox B-47 | AH-714 | Maintenance, primer , low viscosity primer system, general application, construction

Mixing ratio (Parts by weight) : 100 : 50 | Mix viscosity @ 25oC (mPa s) : 600 – 1,000 | Pot life @ 25oC (minutes) : 130 – 150

Posted in PO PM Industry

Lapox B-11 | AH-543 | Maintenance, primer , very low temperature curing, curing in high humidity, moist surface, construction

Mixing ratio (Parts by weight) : 100 : 66 | Mix viscosity @ 25oC (mPa s) : 4,500 – 5,500 | Pot life @ 25oC (minutes) : 40 – 50

Posted in PO PM Industry

Lapox AH-725 | polyamide curing agent, bonding, fast reactivity

Colour (Gardner) : Max 8 | Viscosity @ 25oC (mPa s) : 7,000 – 11,000 | Amine value (mg KOH/g) : 400 – 450 | Pot life @ 25oC (minutes) : 40 – 50 | Mixing ratio (Parts by weight)

Posted in PO PM Industry

Lapox ARC-35 AH-676 | Electrical and Electronics, Electronics, Encapsulation, Pre-filled, “Hot cure Indoor”

Type of system : Pre-filled | Nature : Hot cure / Indoor | Mixing ratio (parts by weight) : 100 : 26 | Glass transition temperature (Tg) (oC) : 70 – 80 | Thermal class : F

Posted in PO PM Industry

Lapox ARC-30 | AH-714 | Electrical and Electronics, Vacuum potting, Pre-filled, “Cold cure Indoor”

Type of system : Pre-filled | Nature : Cold cure / Indoor | Mixing ratio (Parts by weight) : 100 : 25 | Glass transition temperature (Tg) (oC) : 60 – 70 | Thermal class : B

Posted in PO PM Industry

Lapox ARL-111 | AH-358 | ARS-101

Type of system : Unfilled | Nature : Hot cure Indoor | Voltage class : MV / HV | Mixing ratio (parts by weight) : 100 : 15 | Glass transition temperature (Tg) (oC) : 80 – 90 | Thermal

Posted in PO PM Industry

Lapox K-24 | Aromatic amine, curing agent, construction, composite, coatings

Appearance : Yellow liquid | Colour (Gardner) : Max 8 | Viscosity @ 25oC (mPa s) : 1,000 – 2,500 | Amine value (Eq/kg) : 8.00 – 9.00 | Mixing ratio (Parts by weight) : 34

Posted in None

Lapox ARC-31 | AH-114 | AC-13 | Electrical and Electronics, Dry type Distribution Transformer, Encapsulation, Unfilled, “Hot cure Indoor”

Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (Parts by weight) : 100 : 100 : 0.0 – 0.2 | Glass transition temperature (Tg) (oC) : 90 – 100 | Thermal class :

Posted in PO PM Industry

Lapox ARD-58 | aromatic – monofunctional, reactive diluent, cardanol, coating, adhesives, electrical applications

Colour (Gardner) : Max 10 | Epoxy value (Eq/kg) : 2.20 – 2.60 | Viscosity @ 25oC (mPa s) : 20 – 50 | HyCl (%) : Max 1.00

Posted in PO PM Industry

Lapox ARD-15 (K-513) | aromatic – monofunctional, reactive diluent, cardanol, coating, adhesives, electrical applications

Colour (Gardner) : Max 13 | Epoxy value (Eq/kg) : 1.80 – 2.40 | Viscosity @ 25oC (mPa s) : 40 – 70 | HyCl (%) : Max 1.00

Posted in PO PM Industry

Lapox ARD-12 (XR-59) | aromatic – monofunctional, reactive diluent, p-tertiary butyl phenol, high chemical resistance, flooring

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 4.10 – 4.50 | Viscosity @ 25oC (mPa s) : 20 – 35 | HyCl (%) : Max 0.20

Posted in PO PM Industry

Lapox ARD-11 (K-103) | aromatic – monofunctional, reactive diluent, phenol, flooring, electrical application

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 5.90 – 6.30 | Viscosity @ 25oC (mPa s) : 6 – 8 | HyCl (%) : Max 0.20

Posted in PO PM Industry

Lapox ARD-10 (K-100) | aromatic – monofunctional, reactive diluent, o-Cresol, high gloss, high mechanical strength, flooring, electrical application

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 5.30 – 6.00 | Viscosity @ 25oC (mPa s) : 6 – 8 | HyCl (%) : Max 0.20

Posted in PO PM Industry

Lapox C-1 | K-1 | Electrical and Electronics, Bushings, Conventional Vacuum Casting, Unfilled, “Hot cure Indoor”

Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (parts by weight) : 100 : 30 | Glass transition temperature (Tg) (oC) : 115 – 130 | Thermal class : F

Posted in PO PM Industry

Lapox C-59 | K-1 | Electrical and Electronics, Bushings, Conventional Vacuum Casting, Unfilled, Hot cure Indoor

Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (Parts by weight) : 100 : 30 | Glass transition temperature (Tg) (oC) : 115 – 130 | Thermal class : F

Posted in PO PM Industry

Lapox C-2 | K-1 | Electrical and Electronics, Bushings, Conventional Vacuum Casting, Unfilled, “Hot cure Indoor”

Type of system : Unfilled | Nature : Hot cure / Indoo | Mixing ratio (parts by weight) : 100 : 30 | Glass transition temperature (Tg) (oC) : 115 – 130 | Thermal class : F

Posted in PO PM Industry

Lapox ARC-18 | AH-123 | Electrical and Electronics, Bushings, Conventional Vacuum Casting, Prefilled, “Hot cure Indoor”

Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (parts by weight) : 100 : 25 | Glass transition temperature (Tg) (oC) : 122 – 132 | Thermal class : F

Posted in PO PM Industry

Lapox C-50 | K-225 | Electrical and Electronics, Bushings, Conventional Vacuum Casting, Unfilled, “Hot cure Indoor”

Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio : 100 : 80 | Glass transition temperature (Tg) (oC) : 90 – 105 | Thermal class : H

Posted in PO PM Industry

Lapox C-50 | K-61 | Electrical and Electronics, Bushings, Conventional Vacuum Casting, Unfilled, “Hot cure Indoor”

Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio : 100 : 80 | Glass transition temperature (Tg) (oC): 105 – 125 | Thermal class : H

Posted in PO PM Industry

Lapox C-17 | K-12 | K-13 | K-14 | Electrical and Electronics, Bushings, Conventional Vacuum Casting, Unfilled, “Hot cure Indoor”

Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio : 100 : 100 : 0.5 – 1.5 : 0 – 20 | Glass transition temperature (Tg) (oC): 85 – 95 | Thermal class :

Posted in PO PM Industry

Lapox ARCH-12 | AH-215 | Electrical and Electronics, Bushings, Conventional Vacuum Casting, Unfilled, “Hot cure Indoor”

Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio : 100 : 80 | Glass transition temperature (Tg) (oC) : 75 – 85 | Thermal class : F

Posted in PO PM Industry

Lapox ARD-65 | aliphatic – trifunctional, reactive diluent, castor oil, concrete, flooring, thermal shock resistance

Colour (Gardner) : Max 6 | Epoxy value (Eq/kg) : 1.54 – 2.00 | Viscosity @ 25oC (mPa s) : 250 – 500

Posted in PO PM Industry

Lapox ARCH-12 | AH-214 | K-13 | Electrical and Electronics, Bushings, Conventional Vacuum Casting, Unfilled, “Hot cure Indoor”

Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio : 100 : 80 : 0.5 – 2.0 | Glass transition temperature (Tg) (oC) : 75 – 85 | Thermal class : F

Posted in PO PM Industry

Lapox ARCH-11 | AH-215 | Electrical and Electronics, Bushings, Conventional Vacuum Casting, Unfilled, “Hot cure Indoor”

Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio (Parts by weight) : 100 : 90 | Glass transition temperature (Tg) (oC): 100 – 110 | Thermal class : F

Posted in PO PM Industry

Lapox ARCH-11 | AH-214 | K-13 | Electrical and Electronics, Bushings, Conventional Vacuum Casting, Unfilled, “Hot cure Indoor”

Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio : 100 : 90 : 0.5 – 2.0 | Mix viscosity : 1,000/80 | Glass transition temperature (Tg) (oC): 100 – 110 | Thermal class

Posted in PO PM Industry

Lapox ARD-55 (XR-85) | aerospace, reactive diluent, aliphatic-trifunctional, Trimethylol propane based reactive diluent

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 7.00 – 8.00 | Viscosity @ 25oC (mPa s) : 100 – 200 | HyCl (%) : Max 0.15

Posted in None

Lapox ARC-15 | AH-122 | Electrical and Electronics, Bushings, Conventional Vacuum Casting, Pre-filled, “Hot cure Indoor”

Type of system : Pre-filled | Nature : Hot cure Indoor | Mixing ratio (parts by weight) : 100 : 100 | Glass transition temperature (Tg) (oC) : 110 – 120 | Thermal class : H

Posted in PO PM Industry

Lapox ARD-56 (XR-87)

Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 6.90 – 8.00 | Viscosity @ 25oC (mPa s) : 12 – 18 | HyCl (%) : Max 0.15

Posted in PO PM Industry

Lapox ARD-54 (XR-19)

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 2.90 – 3.20 | Viscosity @ 25oC (mPa s) : 40 – 90 | HyCl (%) : Max 0.15

Posted in PO PM Industry

Lapox ARD-52 (XR-86) | aliphatic – difunctional, reactive diluent, 1,6-hexane diol, aerospace

Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 6.20 – 6.80 | Viscosity @ 25oC (mPa s) : 15 – 30 | HyCl (%) : Max 0.15

Posted in PO PM Industry

Lapox ARD-51 (K-77) | aliphatic – difunctional, reactive diluent, 1,4-butane diol

Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 7.00 – 7.80 | Viscosity @ 25oC (mPa s) : 10 – 22 | HyCl (%) : Max 0.15

Posted in PO PM Industry

Lapox ARD-14 (XR-83) | aliphatic – monofunctional, reactive diluent, extreme low viscosity, construction, flooring

Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 6.20 – 7.30 | Viscosity @ 25oC (mPa s) : Max 2 | HyCl (%) : Max 0.10

Posted in PO PM Industry

Lapox ARD-13 (XR-80) | aliphatic – monofunctional, reactive diluent, excellent wetting, excellent flexibility, flooring, coating

Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 3.35 – 3.70 | Viscosity @ 25oC (mPa s) : 4 – 12 | HyCl (%) : Max 0.10

Posted in PO PM Industry

Lapox ARCH-11 (XR-34) | Cycloaliphatic resins, electrical casting, potting, UV resistance, outdoor coating

Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 5.50 – 6.30 | Viscosity @ 25oC (mPa s) : 500 – 1,100

Posted in PO PM Industry

Lapox ARFM-14 (XR-106) | Bisphenol-A/F blends, solids coating, construction, floor coating

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 5.10 – 5.40 | Viscosity @ 25oC (mPa s) : 860 – 960

Posted in PO PM Industry

Lapox A-38 | K-99 | joints, moisture resistance, high adhesion, chemical resistant, construction adhesive

Mixing ratio (Parts by weight) : 100 : 40 | Mix viscosity @ 25oC (mPa s) : 50,000 – 1,00,000 | Pot life @ 25oC (minutes) : 20 – 25

Posted in PO PM Industry

Lapox ARPN-54 | K-41 | K-42 | Maintenance, mortar, screed, excellent chemical resistance, varying pot life, construction

Mixing ratio (Parts by weight) : 100 : 65 | Mix viscosity @ 25oC (mPa s) : 8,000 – 10,000 | Pot life @ 25oC (minutes) : 15 – 330

Posted in PO PM Industry

Lapox ARL-135 LV | Bisphenol-A based modified liquid epoxy resin, FRP , composites

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 5.40 – 5.90 | Viscosity @ 25oC (mPa s) : 1,000 – 1,500

Posted in PO PM Industry

Lapox ARL-135 | Bisphenol-A based modified liquid epoxy resin, FRP , composites

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 5.40 – 5.90 | Viscosity @ 25oC (mPa s) : 1,700 – 2,500

Posted in PO PM Industry

Lapox B-11 | K-48 | construction, Maintenance, repair, crack-filling, quick setting

Mixing ratio (Parts by weight) : 100 : 18 | Mix viscosity @ 25oC (mPa s) : 5,000 – 7,000 | Pot life @ 25oC (minutes) : 15 – 25

Posted in PO PM Industry

Lapox B-47 | K-48 | construction, Maintenance, grouting, quick setting, excellent adhesion, good strength

Mixing ratio (Parts by weight) : 100 : 18 | Mix viscosity @ 25oC (mPa s) : 600 – 700 | Pot life @ 25oC (minutes) : 15 – 25

Posted in PO PM Industry

Lapox B-11 | K-49 | construction, Maintenance, chemical resistant flooring, protection of metal structure, protection from corrossive chemicals, protection from alkali, protection from solvents

Mixing ratio (Parts by weight) : 100 : 60 | Mix viscosity @ 25oC (mPa s) : 3,000 – 4,000 | Pot life @ 25oC (minutes) : 100 – 110

Posted in PO PM Industry

Lapox B-11 | K-41 | K-42 | construction, Maintenance, chemical resistant flooring, variable potlife system, excellent acid and alkali resistance

Mixing ratio (Parts by weight) : 100 : 60 | Mix viscosity @ 25oC (mPa s) : 6,000 – 8,000 | Pot life @ 25oC (minutes) : 15 – 300

Posted in PO PM Industry

Lapox ARPN-54 | AH-351 | Maintenance, mortar, screed, fast reactive system, excellent chemical resistance, construction

Mixing ratio (Parts by weight) : 100 : 30 | Mix viscosity @ 25oC (mPa s) : 5,000 – 7,000 | Pot life @ 25oC (minutes) : 25 – 35

Posted in PO PM Industry

Lapox ARPN-42 | AH-105 | construction, Maintenance, chemical resistant flooring, coal tar modified system, coating of pipes, vehile chassis, concrete structure

Mixing ratio (Parts by weight) : 100 : 100 | Mix viscosity @ 25oC (mPa s) : 2,000 – 4,000 | Pot life @ 25oC (minutes) : 30 – 40

Posted in PO PM Industry

Lapox B-47 | AH-416 | Maintenance, self-leveling system, low viscosity system, excellent gloss, excellent hardness, moderate chemical resistance

Mixing ratio (Parts by weight) : 100 : 60 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : 40 – 50

Posted in PO PM Industry

Lapox B-11 | AH-428 | Maintenance, self-leveling system, moderate viscosity system, excellent gloos, good chemical resistance, construction

Mixing ratio (Parts by weight) : 100 : 45 | Mix viscosity @ 25oC (mPa s) : 800 – 1,200 | Pot life @ 25oC (minutes) : 30 – 40

Posted in PO PM Industry

Lapox ARB-26 | AH-416 | Maintenance, self-leveling system, low viscosity system, high gloss finish

Mixing ratio (Parts by weight) :100 : 60 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : 40 – 50

Posted in PO PM Industry

Lapox ARB-22 | AH-428 | Maintenance, self-leveling system, long pot life, excellent mechanical properties, construction

Mixing ratio (Parts by weight) : 100 : 43 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : 30 – 35

Posted in PO PM Industry

Lapox ARB-22 | AH-416 | Maintenance, self-leveling system, long pot life, excellent mechanical properties, construction

Mixing ratio (Parts by weight) : 100 : 55 | Mix viscosity @ 25oC (mPa s) : 500 – 700 | Pot life @ 25oC (minutes) : 45 – 60

Posted in PO PM Industry

Lapox B-47 | K-41 | K-42 | Maintenance, mortar, screed, varying pot life, excellent chemical resistance, construction

Mixing ratio (Parts by weight) : 100 : 60 | Mix viscosity @ 25oC (mPa s) : 3,000 – 6,000 | Pot life @ 25oC (minutes) : 35 – 330

Posted in PO PM Industry

Lapox B-47 | AH-713 | Maintenance, mortar, screed, standard system, system for extreme condition, screed lining, construction

Mixing ratio (Parts by weight) : 100 : 50 | Mix viscosity @ 25oC (mPa s) : 3,500 – 4,500 | Pot life @ 25oC (minutes) : 110 – 130

Posted in PO PM Industry

Lapox B-47 | AH-546 | Maintenance, mortar, screed, standard system, system for extreme condition, moist surface, construction

Mixing ratio (Parts by weight) : 100 : 50 | Mix viscosity @ 25oC (mPa s) : 3,000 – 4,500 | Pot life @ 25oC (minutes) : 60 – 80

Posted in PO PM Industry

Lapox ASH-11 | aerospace, curing agent, sulfone, 3,3′-Diaminodiphenyl sulfone, more reactive, fast curing, high productivity, powder

Chemistry : 3,3′-Diaminodiphenyl sulfone | Appearance : White to brownish white powder | Melting point (oC) : 167 – 175

Posted in None

Lapox ASH-10 MIC | aerospace, curing agent, sulfone, 4,4′-Diaminodiphenyl sulfone Micronised, micronised ASH-10, uniform dispersion in solvent-free resin, powder

Chemistry : 4,4′-Diaminodiphenyl sulfone Micronised | Appearance : White to off-white powder | Melting point (oC) : 176 – 180

Posted in None

Lapox ASH-10 FF | aerospace, curing agent, sulfone, 4,4′-Diaminodiphenyl sulfone Free Flow, Free flowin ASH-10, easy operation , easy handling, powder

Chemistry : 4,4′-Diaminodiphenyl sulfone Free Flow | Appearance : White to off-white powder | Melting point (oC) : 176 – 185

Posted in None

Lapox ASH-10 | aerospace, curing agent, sulfone, 4,4′-Diaminodiphenyl sulfone, extremely slow reactivity, prepreg, advance composite, powder

Chemistry : 4,4′-Diaminodiphenyl sulfone | Appearance : White to off-white powder | Melting point (oC) : 176 – 185

Posted in None

Lapox AH-667

Chemistry : 4,4′-Diaminodiphenyl methane | Appearance : Viscous brownish liquid | Viscosity @ 60oC (mPa s) : 1,400 – 2,000

Posted in PO PM Industry

Lapox AH-618 (K-5200)

Appearance : Light yellow to brown liquid | Viscosity @ 25oC (mPa s) : 100 – 300

Posted in PO PM Industry

Lapox AH-442

Chemistry : 4,4′-Diaminodicyclohexyl methane | Appearance : Colourless transparent liquid | Melting point (oC) : 35 – 37

Posted in PO PM Industry

Lapox AH-422

Chemistry : 3,3’-Dimethyl-4,4’-diaminodicyclohexyl methane | Viscosity @ 25oC (mPa s) : 100 – 140

Posted in PO PM Industry

Lapox ARBMI-11 | aerospace, Bismaleimide resin, excellent thermal stability

Colour (Gardner) : Yellow powder | Melting point (oC) : 155 – 158

Posted in PO PM Industry

Lapox ARBZ-11 | aerospace, benzoxazine resin, excellent moisture resistance, low shrinkage, moderate flammability

Colour (Gardner) : Yellow solid | Viscosity @ 125oC (mPa s) : 50 – 500

Posted in PO PM Industry

Lapox ARBZ-10 A 75 | aerospace, benzoxazine resin, 75% solution in acetone

Colour (Gardner) : Yellowish liquid | Solid content (%) : 74 – 76 | Viscosity @ 25oC (mPa s) : 100 – 400

Posted in PO PM Industry

Lapox ARBZ-10 | aerospace, benzoxazine resin, excellent moisture resistance, low shrinkage, moderate flammability

Colour (Gardner) : Yellow solid | Viscosity @ 100oC (mPa s) : 1,000 – 7,000 | Softening point (oC) : 60 – 80

Posted in PO PM Industry

Lapox ARTF-50

Colour (Gardner) : Max 16 | Epoxy value (Eq/kg) : 4.17 – 4.44 | Viscosity @ 85oC (mPa s) : 1,000 – 1,500

Posted in PO PM Industry

Lapox ARTF-38 | aerospace, multifunctional resin, distilled unmodified resin, m-amino phenol based, high performance

Epoxy value (Eq/kg) : 9.80 – 10.6 | Viscosity @ 25oC (mPa s) : 1,500 – 4,800

Posted in PO PM Industry

Lapox ARTF-37 | aerospace, multifunctional resin, unmodified resin, m-amino phenol based, high performance

Epoxy value (Eq/kg) : 9.10 – 9.80 | Viscosity @ 25oC (mPa s) : 7,000 – 13,000

Posted in PO PM Industry

Lapox ARTF-36 | aerospace, multifunctional resin, distilled unmodified resin, p-amino phenol based, high performance

Epoxy value (Eq/kg) : 9.40 – 10.50 | Viscosity @ 25oC (mPa s) : 550 – 850

Posted in PO PM Industry

Lapox ARTF-35 | aerospace, multifunctional resin, unmodified resin, p-amino phenol based, high performance

Epoxy value (Eq/kg) : 8.70 – 9.50 | Viscosity @ 25oC (mPa s) : 2,000 – 5,000

Posted in PO PM Industry

Lapox ARTF-34 | aerospace, multifunctional resin, specialty resin, triphenol methane based, high performance

Colour (Gardner) : Max 13 | Epoxy value (Eq/kg) : 5.88 – 6.66 | Viscosity @ 150oC (mPa s) : 30 – 55

Posted in PO PM Industry

Lapox ARTF-33 | aerospace, multifunctional resin, specialty resin, ethyl substituted MDA based, high performance

Colour (Gardner) : Max 7 | Epoxy value (Eq/kg) : 7.52 – 8.47 | Viscosity @ 25oC (mPa s) : 7,000 – 12,000

Posted in PO PM Industry

Lapox ARTF-23

Colour (Gardner) : Max 12 | Epoxy value (Eq/kg) : 8.55 – 9.00 | Viscosity @ 50oC (mPa s) : 3,000 – 6,000

Posted in PO PM Industry

Lapox ARTF-18 | aerospace, multifunctional resin, high viscosity, specialty resin, MDA based, high performance

Colour (Gardner) : Max 12 | Epoxy value (Eq/kg) : 7.46 – 8.55 | Viscosity @ 50oC (mPa s) : 7,000-19,000

Posted in PO PM Industry

Lapox ARTF-17 | aerospace, multifunctional resin, medium viscosity, specialty resin, MDA based, high performance

Colour (Gardner) : Max 12 | Epoxy value (Eq/kg) : 7.46 – 8.55 | Viscosity @ 50oC (mPa s) : 17,000-19,000

Posted in PO PM Industry

Lapox ARTF-16 | aerospace, multifunctional resin, medium viscosity, specialty resin, MDA based, high performance

Colour (Gardner) : Max 12 | Epoxy value (Eq/kg) : 7.46 – 8.55 | Viscosity @ 50oC (mPa s) : 13,000-15,000

Posted in PO PM Industry

Lapox ARTF-14 | aerospace, multifunctional resin, medium viscosity, specialty resin, MDA based, high performance

Colour (Gardner) : Max 12 | Epoxy value (Eq/kg) : 7.46 – 8.55 | Viscosity @ 50oC (mPa s) : 10,000 – 12,000

Posted in PO PM Industry

Lapox ARTF-13 | aerospace, multifunctional resin, medium viscosity, specialty resin, MDA based, high performance

Colour (Gardner) : Max 12 | Epoxy value (Eq/kg) : 7.46 – 8.55 | Viscosity @ 50oC (mPa s) : 7,000 – 11,000

Posted in PO PM Industry

Lapox ARPN-56 | aerospace, Epoxy Phenol Novolac resin, solid resin, functionality of 5.6

Colour (Gardner) : Max 4 | Epoxy value (Eq/kg) : 5.12 – 6.10 | Viscosity @ 50oC (mPa s) : 100 – 350

Posted in None

Lapox ARPN-25 | aerospace, Epoxy Phenol Novolac resin, low viscosity, average functionality, functionality of 2.5

Colour (Gardner) : Max 3 | Epoxy value (Eq/kg) : 5.59 – 5.81 | Viscosity @ 52oC (mPa s) : 1,100 – 1,700

Posted in PO PM Industry

Lapox ARN-16 | aerospace, bifunctional resin, Bisphenol-F based epoxy resin, medium viscosity

Colour (Gardner) : Max 16 | Epoxy value (Eq/kg) : 6.50 – 7.50 | Viscosity @ 50oC (mPa s) : 1,000 – 2,500 | Hycl : Max 0.20

Posted in PO PM Industry

Lapox ARL-15 | aerospace, bifunctional resin, Bisphenol-F based epoxy resin, low viscosity

Colour (APHA) : Max 50 | Epoxy value (Eq/kg) : 5.71 – 5.95 | Viscosity @ 25oC (mPa s) : 4,000 – 5,000

Posted in PO PM Industry

Lapox ARL-12 | aerospace, bifunctional resin, Bisphenol-F based epoxy resin

Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 5.26 – 5.55 | Viscosity @ 25oC (mPa s) : 9,000 – 12,000

Posted in PO PM Industry

Lapox P-5 (ARP-17) | Bisphenol-A based solid resins, type 7, stoving lacquers, can coating, tube coating

Epoxy value (Eq/kg) : 0.53 – 0.59 | Viscosity @ 25oC (mPa s) : 1,800 – 2,600 | Softening point (oC) : 110 – 120

Posted in PO PM Industry

Lapox K-541 (AH-541) | phenalkamine curing agent, high viscosity, marine coating, industrial coatings, protective coatings

Colour (Gardner) : Max 15 | Viscosity @ 25oC (mPa s) : 15,000 – 35,000 | Amine value (mg KOH/g) : 290 – 325 | Pot life @ 25oC (minutes) : 40 – 85 | Mixing ratio (Parts by weight)

Posted in None

Lapox K-540 (AH-540) | phenalkamine curing agent, low viscosity, marine coatng, industrial coating, maintenance coating, protective coatings

Colour (Gardner) : Max 15 | Viscosity @ 25oC (mPa s) : 2,000 – 4,000 | Amine value (mg KOH/g) : 490 – 550 | Pot life @ 25oC (minutes) : 30 – 55 | Mixing ratio (Parts by weight)

Posted in None

Lapox AH-543 (XH-80) | phenalkamine curing agent, low colour, low viscosity, heavy duty anti-corrosive coatings , marine applications, protective coatings

Colour (Gardner) : Max 15 | Viscosity @ 25oC (mPa s) : 2,000 – 5,000 | Amine value (mg KOH/g) : 300 – 350 | Pot life @ 25oC (minutes) : 50 – 65 | Mixing ratio (Parts by weight)

Posted in PO PM Industry

Lapox AH-420 (K-964) | cycloaliphatic amine curing agent, very low viscosity, moderate pot life, flooring, better chemical resistance, protective coatings

Colour (Gardner) : Max 3 | Viscosity @ 25oC (mPa s) : 40 – 60 | Amine value (mg KOH/g) : 320 – 340 | Pot life @ 25oC (minutes) : 25 – 40 | Mixing ratio (Parts by weight)

Posted in PO PM Industry

Lapox AH-411 | unmodified cycloaliphatic amine curing agent, coatings, flooring applications, composite applications, protective coatings

Colour (Gardner) : Max 1 | Viscosity @ 25oC (mPa s) : 10 – 20 | Pot life @ 25oC (minutes) : 90 – 120 | Mixing ratio (Parts by weight) : 23

Posted in PO PM Industry

Lapox XH-61 (AH-321) | modified polyamine adduct solution, solution in xylene and butanol, clear coating, protective coating

Colour : Max 2 | Viscosity @ 25oC (mPa s) : 1,500 – 2,000 | Amine value (Eq/kg) : 165 – 210 | Pot life @ 25oC (hours) : 4 – 6 | Mixing ratio (Parts by weight) : 30

Posted in PO PM Industry

Lapox K-306 | Butylated melamine formaldehyde curing agent, enamel, polyester film coating, protective coating

Colour (Gardner) : Clear liquid | Viscosity @ 25oC (mPa s) : 850 – 1,200 | Mixing ratio (Parts by weight) : 100 (with resin ARL-148)

Posted in PO PM Industry

Lapox K-105 | coal tar modified polyamine adduct, high build coatings, protective coating

Colour (Gardner) : Black | Viscosity @ 25oC (mPa s) : 3,000 – 6,000 | Pot life @ 25oC (minutes) : Min 20 | Mixing ratio (Parts by weight) : 100 (with resin ARB – 28)

Posted in PO PM Industry

Lapox K-54 (AH-356) | modified polyamine adduct, slids coating, mortar, adhesives, protective coating

Colour (Gardner) : Max 2 | Viscosity @ 25oC (mPa s) : 2,900 – 3,600 | Amine value (mg KOH/g) : 398 – 415 | Pot life @ 25oC (minutes) : 15 – 30 | Mixing ratio (Parts by weight)

Posted in PO PM Industry

Lapox K-48 (AH-319) | modified polyamine curing agent, low vapour pressurehigh reactivity, adhesives, composites, castings, coatings, protective coating

Colour (Gardner) : Max 4 | Viscosity @ 25oC (mPa s) : 200 – 300 | Amine value (Eq/kg) : 17.00 – 17.80 | Pot life @ 25oC (minutes) : 25 – 35 | Mixing ratio (Parts by weight) :

Posted in PO PM Industry

Lapox K-7 | unmodified aliphatic polyamine curing agent, adhesives, castings, coatings, composites, protective coating

Colour (Gardner) : Max 5 | Viscosity @ 25oC (mPa s) : Max 10 | Pot life @ 25oC (minutes) : 20 – 25 | Mixing ratio (Parts by weight) : 10 – 12

Posted in PO PM Industry

Lapox K-6 | unmodified aliphatic polyamine curing agent, casting, coatings, composites, protective coating

Colour (Gardner) : Max 3 | Pot life @ 25oC (minutes) : 30 – 40 | Mixing ratio (Parts by weight) : 10 – 12

Posted in PO PM Industry

Lapox AH-371 to AH-373 | modified polyamine curing agent, crack-filling, stone coating, mortar, adhesive, protective coating

Colour (Gardner) : Max 5 | Viscosity @ 25oC (mPa s) : 100 – 550 | Amine value (mg KOH/g) : 500 – 1,000 | Pot life @ 25oC (minutes) : 5 – 30 | Mixing ratio (Parts by weight)

Posted in PO PM Industry

Lapox AH-351 | modified polyamine curing agent, chemical resistance, sulphuric acid resistance, protective coating

Colour (Gardner) : Max 4 | Viscosity @ 25oC (mPa s) : 500 – 1,000 | Amine value (mg KOH/g) : 650 – 750 | Pot life @ 25oC (minutes) : 30 – 40 | Mixing ratio (Parts by weight)

Posted in PO PM Industry

Lapox AH-348 | unmodified aliphatic polyamine curing ag nr, flexible casting, transparent casting, coatings, protective coating

Colour (Gardner) : Max 1 | Viscosity @ 25oC (mPa s) : 5 – 10 | Amine value (mg KOH/g) : 680 – 720 | Pot life @ 25oC (minutes) : 40 – 50 | Mixing ratio (Parts by weight)

Posted in PO PM Industry

Lapox AH-341 | modified aliphatic polyamine curing agent, solids coating, long pot life, protective coating

Colour (Gardner) : Max 2 | Viscosity @ 25oC (mPa s) : 30 – 100 | Amine value (mg KOH/g) : 290 – 320 | Pot life @ 25oC (minutes) : 100 – 125 | Mixing ratio (Parts by weight)

Posted in PO PM Industry

Lapox AH-313 | unmodified aliphatic polyamine curing agent, adhesives, casting, coating, composite applications, protective coating

Colour (Gardner) : Max 4 | Viscosity @ 25oC (mPa s) : 50 – 60 | Pot life @ 25oC (minutes) : 35 – 50 | Mixing ratio (Parts by weight) : 15

Posted in PO PM Industry

Lapox K-92 | Aromatic amine, ambient cure modified curing agent, chemical resistant coating, tank lining, flooring, protective coating

Appearance : Brown liquid | Colour (Gardner) : Max 13 | Viscosity @ 25oC (mPa s) : 5,000 – 7,500 | Amine value (Eq/kg) : 4.40 – 5.10 | Mixing ratio (Parts by weight) : 60

Posted in PO PM Industry

Lapox ARL-143 | AH-335 | industrial, RTM, hand lay-up and infusion systems, moderate viscosity system, varying pot life, fire retardannt application

Mixing ratio (Parts by weight) : 100 : 15 | Mix viscosity @ 25oC (mPa s) : 3,500 – 5,000 | Pot life @ 25oC (minutes) : 85 – 95 | Glass transition temperature (Tg) (oC) : 95 – 105

Posted in PO PM Industry

Lapox ARL-143 | AH-319 | industrial, RTM, hand lay-up and infusion systems, moderate viscosity system, varying pot life, fire retardannt application

Mixing ratio (Parts by weight) : 100 : 15 | Mix viscosity @ 25oC (mPa s) : 3,500 – 5,000 | Pot life @ 25oC (minutes) : 20 – 25 | Glass transition temperature (Tg) (oC) : 95 – 105

Posted in PO PM Industry

Lapox ARCH-13 | Cycloaliphatic resins, higher toughness, outdoor coating, electrical casting, flooring, protective coating

Colour (APHA) : Max 100 | Epoxy value (Eq/kg) : 4.16 – 4.54 | Viscosity @ 25oC (mPa s) : 2,000 – 4,000

Posted in PO PM Industry

Lapox ARF-15 | Bisphenol-F based resin, very low viscosity, distilled version, protective coating

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 6.00 – 6.40 | Viscosity @ 25oC (mPa s) : 1,200 – 1,600

Posted in PO PM Industry

Lapox ARF-14 | Bisphenol-F based resin, high viscosity, constructon, composites, electrical, casting, protective coating

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 5.80 – 6.30 | Viscosity @ 25oC (mPa s) : 5,000 – 7,000

Posted in None

Lapox ARF-13 | Bisphenol-F based resin, medium viscosity, constructon, composites, electrical, casting, protective coating

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 5.80 – 6.10 | Viscosity @ 25oC (mPa s) : 3,300 – 4,100

Posted in None

Lapox ARF-12 | Bisphenol-F based resin, low viscosity, constructon, composites, electrical, casting, protective coating

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 5.80 – 6.10 | Viscosity @ 25oC (mPa s) : 2,000 – 3,000

Posted in None

Lapox ARF-11 (XR-40) | standard Bisphenol-F based resin, constructon, composites, electrical, casting, protective coating

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 5.70 – 6.30 | Viscosity @ 25oC (mPa s) : 2,000 – 5,000

Posted in PO PM Industry

Lapox P-122 (ARP-14 A) | Bisphenol-A based solid resins, functional powder coating, rebar coating, protective coating

Epoxy value (Eq/kg) : 1.07 – 1.16 | Viscosity @ 25oC (mPa s) : 620 – 900 | Softening point (oC) : 100 – 110

Posted in None

Lapox P-62 (ARP-13) | Bisphenol-A based solid resins, standard solid resin, powder coating, protective coating

Epoxy value (Eq/kg) : 1.25 – 1.40 | Viscosity @ 25oC (mPa s) : 500 – 700 | Softening point (oC) : 95 – 101

Posted in PO PM Product

Lapox ARPN-36 | K-86 | industrial, prepregs and laminating systems, compressed laminate system, B-stage prepreg

Mixing ratio (Parts by weight) : 100 : 3-6 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (Tg) (oC) : 165 – 180

Posted in PO PM Industry

Lapox ARPN-36 | K-10 | K-86 | automotive, prepregs and laminating systems, compressed laminate, B-stage prepreg, very high Tg, very high glass transition temperature

Mixing ratio (Parts by weight) : 100 : 32-40 : 1-3 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (Tg) (oC) : 170 – 185

Posted in PO PM Industry

Lapox L-247 | K-918 | K-13 | industrial, filament winding and pultrusion, hot cure system, general purpose system, fire retardant

Mixing ratio (Parts by weight) : 100 : 64 : 1-3 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 110 – 120

Posted in PO PM Industry

Lapox L-12 | K-24 | industrial, filament winding and pultrusion, hot cure system, low viscosity system, long pot life, high chemical resistance, high abrasion resistance

Mixing ratio (Parts by weight) : 100 : 34 | Mix viscosity @ 25oC (mPa s) : 3,500 – 5,000 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) oC : 145 – 155

Posted in PO PM Industry

Lapox L-12 | K-12 K-13 | industrial, filament winding and pultrusion, hot cure system, standard system, fast reactivity

Mixing ratio (Parts by weight) : 100 : 100 : 1-3 | Mix viscosity @ 25oC (mPa s) : 400 – 700 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 95 –

Posted in PO PM Industry

Lapox L-12 | AH-667 | industrial, filament winding and pultrusion, hot cure system, high chemical resistance, high abrasion resistance

Mixing ratio (Parts by weight) : 100 : 27 | Mix viscosity @ 50oC (mPa s) : 3,000 – 5,000 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 150 – 160

Posted in PO PM Industry

Lapox L-12 | AH-113 | K-13 | industrial, filament winding and pultrusion, hot cure system, flame retardancy

Mixing ratio (Parts by weight) : 100 : 95 : 0.5-2.0 | Mix viscosity @ 25oC (mPa s) : 1,900 – 2,100 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 165 –

Posted in PO PM Industry

Lapox ARL-136 | AH-126 | industrial, filament winding and pultrusion, hot cure system, superior fiber wetting, excellent mechanical properties, good surface finish

Mixing ratio (Parts by weight) : 100 : 90 | Mix viscosity @ 25oC (mPa s) : 300 – 600 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 115 – 125

Posted in PO PM Industry

Lapox ARF-11 | K-918 | K-13 | industrial, filament winding and pultrusion, hot cure system, non-crystallisable, excellent chemical resistance

Mixing ratio (Parts by weight) : 100 : 90 : 1-3 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 115 –

Posted in PO PM Industry

Lapox ARCH-11 | K-3 | K-13 | industrial, filament winding and pultrusion, hot cure system, out door application, UV resistance

Mixing ratio (Parts by weight) : 100 : 85 : 1-3 | Mix viscosity @ 25oC (mPa s) : 200 – 500 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 105 –

Posted in PO PM Industry

Lapox L-12 | AH-337 | industrial, filament winding and pultrusion, ambient cure system, high Tg, high glass transition temperature, variable pot life

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 400 – 700 | Pot life @ 25oC (minutes) : 300 – 380 | Glass transition temperature (Tg) oC : 90 – 105

Posted in PO PM Industry

Lapox L-12 | AH-336 | industrial, filament winding and pultrusion, ambient cure system, high Tg, high glass transition temperature, variable pot life

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 600 – 1,200 | Pot life @ 25oC (minutes) : 80 – 100 | Glass transition temperature (Tg) oC : 90 – 105

Posted in PO PM Industry

Lapox L-12 | AH-335 | industrial, filament winding and pultrusion, ambient cure system

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 600 – 1,200 | Pot life @ 25oC (minutes) : 50 – 60 | Glass transition temperature (Tg) oC : 90 – 105

Posted in PO PM Industry

Lapox L-12 | AH-315 | industrial, filament winding and pultrusion, ambient cure system

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 500 – 800 | Pot life @ 25oC (minutes) : 7 – 9 hr | Glass transition temperature (Tg) oC : 85 –

Posted in PO PM Industry

Lapox ARL-12 | AH-714 | industrial, filament winding and pultrusion, ambient cure system, superior adhesion, toughness

Mixing ratio (Parts by weight) : 100 : 50 | Mix viscosity @ 25oC (mPa s) : 1,200 – 1,500 | Pot life @ 25oC (minutes) : 120 – 150 | Glass transition temperature (Tg) oC : 55 – 65

Posted in PO PM Industry

Lapox ARL-125 | AH-332 | aerospace, RTM, hand lay-up, infusion, long pot life, high Tg, high glass transition temperature

Mixing ratio (Parts by weight) : 100:32 | Mix viscosity @ 25oC (mPa s) : 600 – 800 | Pot life @ 25oC (minutes) : 8 – 14 | Glass transition temperature (Tg) (oC) : 80 – 90

Posted in PO PM Industry

Lapox ART-24 | AH-326 | automotive, tooling, gel coat system

Mixing ratio (Parts by weight) : 100 : 20 | Mix viscosity @ 25oC (mPa s) : Paste (colourless) | Pot life @ 25oC (minutes) : 15 – 20 | Glass transition temperature (Tg) (oC) : 95 – 115

Posted in PO PM Industry

Lapox ART-23 | AH-326 | automotive, tooling, gel coat system

Mixing ratio (Parts by weight) : 100 : 10 | Mix viscosity @ 25oC (mPa s) : Paste (blue) | Pot life @ 25oC (minutes) : 15 – 20 | Glass transition temperature (Tg) (oC) : 75 – 85

Posted in PO PM Industry

Lapox ART-21 | AH-326 | automotive, tooling, gel coat system

Mixing ratio (Parts by weight) : 100 : 14 | Mix viscosity @ 25oC (mPa s) : Paste (white) | Pot life @ 25oC (minutes) : 25 – 30 | Glass transition temperature (Tg) (oC) : 75 – 85

Posted in PO PM Industry

Lapox ARL-135 LV | AH-411 | automotive, RTM, hand lay-up and infusion systems, very low viscosity, high Tg, high glass trransition temperature

Mixing ratio (Parts by weight) : 100 : 24 | Mix viscosity @ 25oC (mPa s) : 250 – 400 | Pot life @ 25oC (minutes) : 90 – 120 | Glass transition temperature (Tg) (oC) : 125 – 135

Posted in PO PM Industry

Lapox ARL-135 LV | AH-333 | automotive, RTM, hand lay-up and infusion systems, low viscosity system, variable pot life

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 600 – 750 | Pot life @ 25oC (minutes) : 14 – 20 | Glass transition temperature (Tg) (oC) : 75 – 85

Posted in PO PM Industry

Lapox B-7 | semi-solid, can coating, coil coating, protective coating

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 3.57 – 4.45 | Viscosity @ 25oC (mPa s) : 450 – 800

Posted in None

Lapox ARL-135 LV | AH-332 | automotive, RTM, hand lay-up and infusion systems, low viscosity system, variable pot life

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 600 – 800 | Pot life @ 25oC (minutes) : 8 – 14 | Glass transition temperature (Tg) (oC) : 75 – 85

Posted in PO PM Industry

Lapox P-10 (ARP-14 E) | Bisphenol-A based solid resins, esterifcation, anodic electrodeposition

Epoxy value (Eq/kg) : 1.08 – 1.18 | Viscosity @ 25oC (mPa s) : 430 – 550 | Softening point (oC) : 90 – 100

Posted in PO PM Industry

Lapox ARP-14 HF | Bisphenol-A based solid resins, modified resin, powder coating, better flow

Epoxy value (Eq/kg) : 1.23 – 1.33 | Viscosity @ 25oC (mPa s) : 480 – 580 | Softening point (oC) : 80 – 90

Posted in None

Lapox ARP-13 LV | Bisphenol-A based solid resins, hybrid powder coating

Epoxy value (Eq/kg) : 1.33 – 1.40 | Viscosity @ 25oC (mPa s) : 500 – 600 | Softening point (oC) : 95 – 101

Posted in None

Lapox ARL-160 | AH-359 | automotive, prepreg system, FRP structural component

Mixing ratio (Parts by weight) : 100 : 5 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (Tg) (oC) : 110 – 120

Posted in PO PM Industry

Lapox ARL-159 | AH-357 | AC-22 | automotive, prepreg system, hot melt prepreg system, very high Tg, very high glass transition temperature,

Mixing ratio (Parts by weight) : 100 : 15 : 2 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (Tg) (oC) : 155 – 165

Posted in PO PM Industry

Lapox L-68 | K-66 | K-13 | automotive, prepregs and laminating systems, compressed laminate, B-stage prepreg, FR-4 laminate

Mixing ratio (Parts by weight) : 100 : 32 : 1-3 | Pot life @ 25oC (weeks) : 2 – 3 | Glass transition temperature (Tg) (oC) : 130 – 140

Posted in PO PM Industry

Lapox L-67 | K-66 | K-13 | automotive, prepregs and laminating systems, compressed laminate, B-stage prepreg, G-10 laminate

Mixing ratio (Parts by weight) : 100 : 23 : 0.5-3.0 | Pot life @ 25oC (weeks) : 2 – 3 | Glass transition temperature (Tg) (oC) : 130 – 140

Posted in PO PM Industry

Lapox ARP-13 HT | Bisphenol-A based solid resins, powder coating

Epoxy value (Eq/kg) : 1.25 – 1.35 | Viscosity @ 150oC (mPa s) : 4,500 – 6,500 | Glass transition temperature (Tg) (oC) : 55

Posted in None

Lapox L-12 | K-10 | K-86 | automotive, prepregs and laminating systems, compressed laminate, B-stage prepreg, shelf life upto 6 month, G-11 laminate

Mixing ratio (Parts by weight) : 100 : 35 : 1-3 | Pot life @ 25oC (weeks) : 6 – 8 weeks | Glass transition temperature (Tg) (oC) : 150 – 160

Posted in PO PM Industry

Lapox ARP-12 | Bisphenol-A based solid resins, medium molecular weight, powder coating

Epoxy value (Eq/kg) : 1.42 – 1.53 | Viscosity @ 25oC (mPa s) : 375 – 475 | Softening point (oC) : 80 – 90

Posted in PO PM Industry

Lapox AC-14 (K-65) | accelerator and catalysts, liquid tertiary amine, accelerate anhydrides, accelerate polyamides, accelerate amines

Appearance : Clear yellow liquid | Colour (Gardner) : Max 6 | Viscosity @ 25oC (mPa s) : 150 – 300 | Amine value (mg KOH/g) : 580 – 635

Posted in PO PM Industry

Lapox L-12 | K-5 | automotive, prepregs and laminating systems, compressed laminate, prepreg, shorter shelf life, G-10 laminate, G-11 laminate

Mixing ratio (Parts by weight) : 100 : 27 | Pot life @ 25oC (hours) : > 4 | Glass transition temperature (Tg) (oC) : 150 – 160

Posted in PO PM Industry

Lapox K-302 | modified polyamine, curing agent, self-leveling flooring, solvent-free coating, clear casting

Colour (Gardner) : Max 2 | Viscosity @ 25oC (mPa s) : 300 – 600 | Amine value (mg KOH/g) : 260 – 310 | Pot life @ 25oC (minutes) : 40 – 50 | Mixing ratio (Parts by weight)

Posted in PO PM Industry

Lapox AH-440 | Cycloaliphatic amine, curing agent, accelerated curing agent, solvent-free coating, flooring

Colour (Gardner) : Max 2 | Viscosity @ 25oC (mPa s) : 150 – 300 | Amine value (mg KOH/g) : 335 – 375 | Pot life @ 25oC (minutes) : 25 – 40 | Mixing ratio (Parts by weight)

Posted in PO PM Industry

Lapox AH-428 | Cycloaliphatic amine, curing agent, low viscosity, fast reactivity, self-leveling, high gloss, colour stability

Colour (Gardner) : Max 1 | Viscosity @ 25oC (mPa s) : 50 – 150 | Amine value (mg KOH/g) : 340 – 390 | Pot life @ 25oC (minutes) : 30 – 40 | Mixing ratio (Parts by weight)

Posted in PO PM Industry

Lapox L-12 | K-918 | K-13 | automotive, filament winding and pultrusion system, hot cure

Mixing ratio (Parts by weight) : 100 : 85 : 1-3 | Mix viscosity @ 25oC (mPa s) : 600 – 900 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 130 –

Posted in PO PM Industry

Lapox AH-424 | Cycloaliphatic amine, curing agent, self-leveling flooring, high filler loading

Colour (Gardner) : Max 2 | Amine value (mg KOH/g) : 330 – 360 | Pot life @ 25oC (minutes) : 20 – 50 | Mixing ratio (Parts by weight) : 45

Posted in PO PM Industry

Lapox L-12 | AH-422 | automotive, filament winding and pultrusion system, long pot life, high glass transition temperature, high Tg, ambient cure

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 1,500 – 2,500 | Pot life @ 25oC (minutes) : 300 – 350 | Glass transition temperature (Tg) (oC) : 130 – 140

Posted in PO PM Industry

Lapox AH-416 | Cycloaliphatic amine, curing agent, moderate viscosity, transparent, high gloss, self-leveling flooring

Colour (Gardner) : Max 1 | Viscosity @ 25oC (mPa s) : 400 – 600 | Amine value (mg KOH/g) : 250 – 300 | Pot life @ 25oC (minutes) : 30 – 45 | Mixing ratio (Parts by weight)

Posted in PO PM Industry

Lapox AH-727 | curing agent, Polyamide, curing under wet/damp, excellent adhesion, adhesion with metal, adhesion with concrete, primer, coatings

Colour (Gardner) : Max 12 | Viscosity @ 25oC (mPa s) : 1,000 – 2,000 | Amine value (mg KOH/g) : 280 – 300 | Pot life @ 25oC (minutes) : 46 – 65 | Mixing ratio (Parts by weight)

Posted in PO PM Industry

Lapox AH-716 (K-29) | curing agent, Polyamide, low viscosity, solids coating, primer, floor coating

Colour (Gardner) : Max 10 | Viscosity @ 25oC (mPa s) : 2,500 – 5,500 | Amine value (mg KOH/g) : 202 – 225 | Pot life @ 25oC (minutes) : 80 – 100 | Mixing ratio (Parts by weight)

Posted in PO PM Industry

Lapox ARL-135 LV | AH-337 | automotive, filament winding and pultrusion system, low viscosity, variable pot life, ambient cure

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 200 – 300 | Pot life @ 25oC (minutes) : 300 – 380 | Glass transition temperature (Tg) (oC) : 75 – 85

Posted in PO PM Industry

Lapox AH-714 | curing agent, Polyamide, low viscosity, grout, crack injection, primer, protective coating, tile gap filling, adhesive, mortar

Colour (Gardner) : Max 8 | Viscosity @ 25oC (mPa s) : 500 – 1,000 | Amine value (mg KOH/g) : 425 – 450 | Pot life @ 25oC (minutes) : 120 – 130 | Mixing ratio (Parts by weight)

Posted in PO PM Industry

Lapox ARL-135 LV | AH-336 | automotive, filament winding and pultrusion system, variable pot life, ambient cure

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 300 – 700 | Pot life @ 25oC (minutes) : 80 – 100 | Glass transition temperature (Tg) (oC) : 75 – 85

Posted in PO PM Industry

Lapox AH-713 (K-46) | curing agent, Polyamide, moderate viscosity, solids coating, primer, grout, mortar, adhesive, marine coating, industrial paints

Colour (Gardner) : Max 9 | Viscosity @ 25oC (mPa s) : 12,000 – 18,000 | Amine value (mg KOH/g) : 350 – 400 | Pot life @ 25oC (minutes) : 60 – 80 | Mixing ratio (Parts by weight)

Posted in PO PM Industry

Lapox ARL-135 LV | AH-335 | automotive, filament winding and pultrusion system, variable pot life, ambient cure

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 300 – 700 | Pot life @ 25oC (minutes) : 50 – 60 | Glass transition temperature (Tg) (oC) : 75 – 85

Posted in PO PM Industry

Lapox AH-712 | curing agent, Polyamide, high viscosity, protective coating, adhesive, flooring, marine coating, industrial paint

Colour (Gardner) : Max 9 | Viscosity @ 25oC (mPa s) : 45,000 – 60,000 | Amine value (mg KOH/g) : 290 – 320 | Pot life @ 25oC (minutes) : 110 – 130 | Mixing ratio (Parts by weight)

Posted in PO PM Industry

Lapox ART-22 | AH-326

Mixing ratio (Parts by weight) : 100 : 6 | Mix viscosity @ 25oC (mPa s) : Paste (grey) | Pot life @ 25oC (minutes) : 15 – 20 | Glass transition temperature (Tg) (oC) : 85 – 95

Posted in PO PM Industry

Lapox ARL-140 | AH-419

Mixing ratio (Parts by weight) : 100 : 42 | Mix viscosity @ 25oC (mPa s) : 2,500 – 3,000 | Pot life @ 25oC (minutes) : 600 – 700 | Glass transition temperature (Tg) (oC) : 190 – 220

Posted in PO PM Industry

Lapox ARL-138 | AH-417 | aerospace, tooling, laminating system, low viscosity system, high Tg, high glass transition temperature

Mixing ratio (Parts by weight) : 100 : 30 | Mix viscosity @ 25oC (mPa s) : 200 – 300 | Pot life @ 25oC (minutes) : 90 – 120 | Glass transition temperature (Tg) (oC) : 100 – 110

Posted in PO PM Industry

Lapox AH-711 | curing agent, Polyamide, high viscosity, adhesive, sealant

Colour (Gardner) : Max 9 | Viscosity @ 40oC (mPa s) : 50,000 – 75,000 | Amine value (mg KOH/g) : 210 – 230 | Mixing ratio (Parts by weight) : 100 – 125

Posted in PO PM Industry

Lapox K-49 | Aromatic amine, low viscosity, moderate reactivity, solvent-free coating, chemical resistant coating, floorings, linings

Appearance : Brown liquid | Colour (Gardner) : Max 13 | Viscosity @ 25oC (mPa s) : 700 – 900 | Amine value (Eq/kg) : 4.70 – 5.00 | Mixing ratio (Parts by weight) : 60

Posted in PO PM Industry

Lapox ARL-138 | AH-339 | aerospace, laminating system, high Tg, high glass transition temperature, dimensional stability at high temperature

Mixing ratio (Parts by weight) : 100 : 30 | Mix viscosity @ 25oC (mPa s) : 400 – 600 | Pot life @ 25oC (minutes) : 120 – 180 | Glass transition temperature (Tg) (oC) : 130 – 140

Posted in PO PM Industry

Lapox K-42 | Aromatic amine, curing agent, low viscosity, high reactive

Appearance : Dark brown liquid | Colour (Gardner) : Max 16 | Viscosity @ 25oC (mPa s) : 15,000 – 21,000 | Amine value (Eq/kg) : 4.40 – 4.80 | Mixing ratio (Parts by weight) : 60

Posted in PO PM Industry

Lapox K-41 | Aromatic amine, curing agent, low viscosity, chemical resistant, industrial flooring, coatings, tank linings

Appearance : Brown liquid | Colour (Gardner) : Max 13 | Viscosity @ 25oC (mPa s) : 3,800 – 5,800 | Amine value (Eq/kg) : 4.70 – 5.10 | Mixing ratio (Parts by weight) : 60

Posted in PO PM Industry

Lapox XR-128 | Solvent cut resins, high molecular weight, primer, enamel, flexibility

Epoxy value (Eq/kg) : Max 0.08 | Viscosity @ 25oC (mPa s) : 2,000 – 5,000 | Non-volatile content (%) : 49 – 51 (160oC/2h)

Posted in PO PM Industry

Lapox P-101 HV | Solvent cut resins, type 1 solution, paint and coatings

Epoxy value (Eq/kg) : 1.80 – 2.20 | Viscosity @ 25oC (mPa s) : 14,000 – 20,000 | Non-volatile content (%) : 74 – 76 (150oC/2h)

Posted in PO PM Industry

Lapox P-101 | Solvent cut resins, type 1 solution, paint and coatings

Epoxy value (Eq/kg) : 1.90 – 2.20 | Viscosity @ 25oC (mPa s) : 9,000 – 13,000 | Non-volatile content (%) : 74 – 76 (150oC/2h)

Posted in PO PM Industry

Lapox B-7 X 80 | Solvent cut resins, solids coating, excellent adhesion, gloss, flexibility

Epoxy value (Eq/kg) : 3.10 – 3.40 | Viscosity @ 25oC (mPa s) : 600 – 850 | Non-volatile content (%) : 79 – 81 (150oC/1h)

Posted in PO PM Industry

Lapox ARPN-54 | modified epoxy phenol novolac resins, composite applications, electrical applications, coating applications, industrial coating

Colour (Gardner) : Max 3 | Epoxy value (Eq/kg) : 5.50 – 6.00 | Viscosity @ 25oC (mPa s) : 25,000 – 35,000

Posted in PO PM Industry

Lapox ARPN-36 X 80 | Epoxy phenol novolac resins, epoxy phenol novolac solution, chemical resistant coating, electrical applications, composite applications, industrial coating

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 4.40 – 4.60 | Viscosity @ 25oC (mPa s) : 800 – 1,500 | Non-volatile content (%) :79 – 81 (150oC/1h)

Posted in PO PM Industry

Lapox ARPN-36 M 80 | Epoxy phenol novolac resins, epoxy phenol novolac solution, chemical resistant coating, electrical applications, composite applications, industrial coating

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 4.40 – 4.60 | Viscosity @ 25oC (mPa s) : 150 – 350 | Non-volatile content (%): 79 – 81 (105oC/2h)

Posted in PO PM Industry

Lapox ARL-135 | AH-337 | aerospace, RTM, hand lay-up, infusion, low viscosity system, high Tg, high glass transition temperature

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : 300 – 380 | Glass transition temperature (Tg) (oC) : 75 – 85

Posted in PO PM Industry

Lapox ARL-135 | AH-336

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 500 – 700 | Pot life @ 25oC (minutes) : 80 – 100 | Glass transition temperature (Tg) (oC) : 75 – 85

Posted in PO PM Industry

Lapox ARL-135 | AH-335

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 500 – 700 | Pot life @ 25oC (minutes) : 50 – 60 | Glass transition temperature (Tg) (oC) : 75 – 85

Posted in PO PM Industry

Lapox ARL-135 | AH-334 GL

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 700 – 1200 | Pot life @ 25oC (minutes) : 25 – 35 | Glass transition temperature (Tg) (oC) : 80 – 90

Posted in PO PM Industry

Lapox ARL-135 | AH-333

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 700 – 1200 | Pot life @ 25oC (minutes) : 14 – 20 | Glass transition temperature (Tg) (oC) : 80 – 90

Posted in PO PM Industry

Lapox ARL-135 | AH-332

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 700 – 1200 | Pot life @ 25oC (minutes) : 8 – 14 | Glass transition temperature (Tg) (oC) : 80 – 90

Posted in PO PM Industry

Lapox L-12 | AH-411

Mixing ratio (Parts by weight) : 100 : 22 | Mix viscosity @ 25oC (mPa s) : 800 – 1,200 | Pot life @ 25oC (minutes) : 90 – 120 | Glass transition temperature (Tg) (oC) : 140 – 155

Posted in PO PM Industry

Lapox ARL-158 | AH-419

Mixing ratio (Parts by weight) : 100 : 42 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : 600 – 700 | Glass transition temperature (Tg) (oC) : 170 – 200

Posted in PO PM Industry

Lapox ARL-135 LV | AH-422

Mixing ratio (Parts by weight) : 100 : 35 | Mix viscosity @ 25oC (mPa s) : 400 – 600 | Pot life @ 25oC (minutes) : 300 – 350 | Glass transition temperature (Tg) (oC) : 110 – 120

Posted in PO PM Industry

Lapox ARL-125 | AH-368

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 200 – 300 | Pot life @ 25oC (minutes) : 350 – 450 | Glass transition temperature (Tg) (oC) : 75 – 85

Posted in PO PM Industry

Lapox ARL-125 | AH-367 GL

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 200 – 300 | Pot life @ 25oC (minutes) : 300 – 380 | Glass transition temperature (Tg) (oC) : 75 – 85

Posted in PO PM Industry

Lapox ARL-125 | AH-365 GL

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 300 – 700 | Pot life @ 25oC (minutes) : 50 – 60 | Glass transition temperature (Tg) (oC) : 75 – 85

Posted in PO PM Industry

Lapox ARL-125 | AH-336

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 300 – 700 | Pot life @ 25oC (minutes) : 80 – 100 | Glass transition temperature (Tg) (oC) : 75 – 85

Posted in PO PM Industry

Lapox ARL-125 | AH-335

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 300 – 700 | Pot life @ 25oC (minutes) : 50 – 60 | Glass transition temperature (Tg) (oC) : 75 – 85

Posted in PO PM Industry

Lapox ARL-125 | AH-334

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 600 – 750 | Pot life @ 25oC (minutes) : 25 – 35 | Glass transition temperature (Tg) (oC) : 80 – 90

Posted in PO PM Industry

Lapox ARL-125 | AH-333

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 600 – 750 | Pot life @ 25oC (minutes) : 14 – 20 | Glass transition temperature (Tg) (oC) : 80 – 90

Posted in PO PM Industry

Lapox ARL-160 | AH-357 | AC-22 | aerospace, hot melt prepreg system, structural component, sporting goods, engineering application

Mixing ratio (Parts by weight) : 100 : 15 : 1-3 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (Tg) (oC) : 110 – 120

Posted in PO PM Industry

Lapox ARL-159 | AH-619 | structural component, high temperature performance, defence, engineering application

Mixing ratio (Parts by weight) : 100 : 40 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (Tg) (oC) : 180 – 200

Posted in PO PM Industry

Lapox K-112 | accelerator and catalysts, Modified viscous tertiary amine, accelerate anhydride, accelerate polyamides, accelerate amines, composite, electrical, coating

Appearance : Clear brown liquid | Viscosity @ 25oC (mPa s) : 1,000 – 1,800

Posted in PO PM Industry

Lapox K-86 | accelerator and catalysts, Solid polyamine complex, accelerate aromatic amines

Appearance : White crystalline powder | Melting point (oC) : Min 75

Posted in PO PM Industry

Lapox AC-20 | accelerator and catalysts, accelerate anhydride, accelerate polyamides, accelerate amines, composite, electrical, coating

Appearance : Brown liquid or solid | Viscosity @ 25oC (mPa s) : Max 100 | Melting point (oC) : 36 – 42

Posted in PO PM Industry

Lapox AC-19 | accelerator and catalysts, Liquid low reactive triamine, accelerate anhydride, accelerate polyamides, accelerate amines, composite, electrical, coating

Appearance : Clear liquid | Colour (Gardner) : Max 1 | Viscosity @ 25oC (mPa s) : 10 – 30

Posted in PO PM Industry

Lapox AC-13 | accelerator and catalysts, Liquid triamine, accelerate anhydride, accelerate polyamides, accelerate amines, composite, electrical, coating

Appearance : Clear liquid | Colour (Gardner) : Max 2 | Viscosity @ 25oC (mPa s) : Max 10

Posted in PO PM Industry

Lapox AC-11

Appearance : White crystal | Melting point (oC) : Min 127 – 134

Posted in PO PM Industry

Lapox AC-10

Appearance : White crystal | Melting point (oC) : 154 – 156

Posted in PO PM Industry

Lapox ARPN-36 (L-238) | Epoxy phenol novolac resins, semi-solid, comosites, electrical, chemical resistant coating, floorings, industrial coating

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 5.50 – 5.70 | Viscosity @ 52oC (mPa s) : 20,000 – 50,000

Posted in PO PM Industry

Lapox ARD-59

Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 5.20 – 6.20 | Viscosity @ 25oC (mPa s) : 20 – 50 | HyCl (%) : Max 0.20

Posted in PO PM Industry

Lapox K-450

Chemistry : 3,3′-Diethyl-4,4′-diaminodiphenyl methane| Appearance : Dark brown liquid | Viscosity @ 40oC (mPa s) : 250 – 400

Posted in PO PM Industry

Lapox K-5 | aerospace, curing agent, aromatic amine, elevated temperature curing, high glass transition temperature

Chemistry : 4,4′-Diaminodiphenyl methane | Appearance : White to tan pastilles | Melting point (oC) : 88 – 92

Posted in PO PM Industry

Lapox ARFM-13 (XR-60) | Bisphenol-A/F blends, low viscosity, coating, composites, floor coating, construction

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 5.50 – 5.75 | Viscosity @ 25oC (mPa s) : 4,500 – 6,500

Posted in PO PM Industry

Lapox ARFM-12 (XR-123) | Bisphenol-A/F blends, Medium viscosity, coating, composites, floor coating, construction

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 5.55 – 5.80 | Viscosity @ 25oC (mPa s) : 6,500 – 8,500

Posted in PO PM Industry

Lapox B-47 | Bisphenol-A based modified liquid epoxy resin, high gloss, heavy duty flooring, solids coating, grout, crack-filling

Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 5.20 – 5.50 | Viscosity @ 25oC (mPa s) : 450 – 650

Posted in PO PM Industry

Lapox ARB-33 | Bisphenol-A based modified liquid epoxy resin, primer, mortar, grout, maintenance

Colour (Gardner) : Max 1 | Colour (AHPA) : Max 75 | Epoxy value (Eq/kg) : 5.12 – 5.55 | Viscosity @ 25oC (mPa s) : 500 – 700

Posted in PO PM Industry

Lapox ARB-32 | Bisphenol-A based modified liquid epoxy resin

Colour (Gardner) : Max 1 | Colour (APHA) : Max 150 | Epoxy value (Eq/kg) : 4.65 – 5.12 | Viscosity @ 25oC (mPa s) : 500 – 700

Posted in PO PM Industry

Lapox ARB-30 | Bisphenol-A based modified liquid epoxy resin, primer, mortar, floor coating

Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 5.00 – 5.50 | Viscosity @ 25oC (mPa s) : 4,500 – 5,500

Posted in PO PM Industry

Lapox ARD-60

Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 7.00 – 7.80 | Viscosity @ 25oC (mPa s) : 10 – 22 | HyCl (%) : Max 0.15

Posted in PO PM Industry

Lapox ARB-28 | Bisphenol-A based modified liquid epoxy resin, primer, mortar, floor coating

Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 5.00 – 5.50 | Viscosity @ 25oC (mPa s) : 1,500 – 2,000

Posted in PO PM Industry

Lapox ARB-26 | Bisphenol-A based modified liquid epoxy resin, floor coating, high gloss, defect free surface

Colour (Gardner) : Milky white liquid | Epoxy value (Eq/kg) : 4.80 – 5.10 | Viscosity @ 25oC (mPa s) : 550 – 750

Posted in PO PM Industry

Lapox ARB-22 (XR-118) | Bisphenol-A based modified liquid epoxy resin, primer, mortar, floor coating

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 4.90 – 5.20 | Viscosity @ 25oC (mPa s) : 800 – 1,200

Posted in PO PM Industry

Lapox B-11 | standard viscosity, Bisphenol-A based unmodified liquid epoxy resin, LER, BLR

Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 5.25 – 5.45 | Viscosity @ 25oC (mPa s) : 11,000 – 15,000

Posted in PO PM Industry

Lapox B-9 | low viscosity, Bisphenol-A based unmodified liquid epoxy resin

Colour (APHA) : Max 50 | Epoxy value (Eq/kg) : 5.25 – 5.45 | Viscosity @ 25oC (mPa s) : 8,000 – 11,000

Posted in PO PM Industry

Lapox ARL-141 | high viscosity, Bisphenol-A based unmodified liquid epoxy resin, high reactivity

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 4.30 – 4.70 | Viscosity @ 25oC (mPa s) : 20,000 – 28,000

Posted in PO PM Industry

Lapox AR-101 | standard viscosity, Bisphenol-A based unmodified liquid epoxy resin

Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 5.25 – 5.45 | Viscosity @ 25oC (mPa s) : 11,000 – 15,000

Posted in PO PM Industry

Lapox P-6 (ARP-19) | type 9, can coating, coil coating

Epoxy value (Eq/kg) : 0.34 – 0.42 | Viscosity @ 25oC (mPa s) : 5,000 – 10,000 | Softening point (oC) : 125 – 140

Posted in PO PM Industry

Lapox ASH-11 MIC | curing agent, sulfone, 3,3′-Diaminodiphenyl sulfone Micronised, uniform dispersion in solvent-free resin, micronised ASH-11, powder

Chemistry : 3,3′-Diaminodiphenyl sulfone Micronised | Appearance : Off-white to yellowish brown powder | Melting point (oC) : 167 – 175

Posted in None

Lapox P-4 (ARP-14) | type 4, enamels, can coating, tube coating

Epoxy value (Eq/kg) : 1.12 – 1.20 | Viscosity @ 25oC (mPa s) : 550 – 700 | Softening point (oC) : 90 – 102

Posted in PO PM Industry

Lapox ARA-32 | AH-732

Mixing ratio (Parts by weight) : 100 : 45 | Mix viscosity @ 25oC (mPa s) : Thixotropic paste | Pot life @ 25oC (minutes) : 25 – 35 | Glass transition temperature (Tg) (oC) : 75 – 85

Posted in PO PM Industry

Lapox ARA-32 | AH-733

Mixing ratio (Parts by weight) : 100 : 45 | Mix viscosity @ 25oC (mPa s) : Thixotropic paste | Pot life @ 25oC (minutes) : 50 – 70 | Glass transition temperature (Tg) (oC) : 75 – 85

Posted in PO PM Industry

Lapox ARA-32 | AH-734

Mixing ratio (Parts by weight) : 100 : 45 | Mix viscosity @ 25oC (mPa s) : Thixotropic paste | Pot life @ 25oC (minutes) : 90 – 120 | Glass transition temperature (Tg) (oC) : 75 – 85

Posted in PO PM Industry

Lapox ARA-32 | AH-735

Mixing ratio (Parts by weight) : 100 : 45 | Mix viscosity @ 25oC (mPa s) : Thixotropic paste | Pot life @ 25oC (minutes) : 130 – 170 | Glass transition temperature (Tg) (oC) : 75 – 85

Posted in PO PM Industry

Lapox A-83 | K-83 | standard adhesive, gap filling, construction adhesive

Mixing ratio (Parts by weight) : 100 : 40 | Mix viscosity @ 25oC (mPa s) : Thixotropic | Pot life @ 25oC (minutes) : 35 – 45

Posted in PO PM Industry

Lapox ARA-30 | AH-735 | structural adhesive, high lap shear strength, general purpose

Mixing ratio (Parts by weight) : 100 : 50 | Mix viscosity @ 25oC (mPa s) : 50,000 – 1,00,000 | Pot life @ 25oC (minutes) : 35 – 50

Posted in PO PM Industry

Lapox ARA-17 | AH-354 | toughness, quick, mechanical strength, general purpose

Mixing ratio (Parts by weight) : 100 : 80 | Mix viscosity @ 25oC (mPa s) : 75,000 – 1,25,000 | Pot life @ 25oC (minutes) : 8 – 10

Posted in PO PM Industry

Lapox A-16 | K-6 | marble, crack sealing, bonding, frame, construction adhesive

Mixing ratio (Parts by weight) : 100 : 10 | Mix viscosity @ 25oC (mPa s) : 4,000 – 6,000 | Pot life @ 25oC (minutes) : 20 – 30

Posted in PO PM Industry

Lapox C-51 | K-6 | electrical adhesive

Type of system : Unfilled | Nature : Cold cure / Indoor | Mixing ratio (Parts by weight) : 100 : 10 | Glass transition temperature (Tg) (oC) : 60 – 70

Posted in PO PM Industry

Lapox XR-110 | XH-68 | cable joints, construction adhesive

Mixing ratio (Parts by weight) : 100 : 100 | Mix viscosity @ 25oC (mPa s) : 3,000 – 4,000 | Pot life @ 25oC (minutes) : 25 – 35

Posted in PO PM Industry

Lapox ARA-12 | AH-718 | multi-purpose, zari, speaker, marble, ceramic, construction adhesive

Mixing ratio (Parts by weight) : 100 : 80 | Mix viscosity @ 25oC (mPa s) : 32,000 – 37,000 | Pot life @ 25oC (minutes) : 90 – 105

Posted in PO PM Industry

Lapox A-555 | K-555 | toughness, quick, mechanical strength, construction adhesive

Mixing ratio (Parts by weight) : 100 : 80 | Mix viscosity @ 25oC (mPa s) : 75,000 – 1,25,000 | Pot life @ 25oC (minutes) : 8 – 10

Posted in PO PM Industry

Lapox A-53 | K-6 | marble, steel, metal, construction adhesive

Mixing ratio (Parts by weight) : 100 : 10 | Mix viscosity @ 25oC (mPa s) : 600 – 800 | Pot life @ 25oC (minutes) : 30 – 60

Posted in PO PM Industry

Lapox A-35 | K-35 | solvent based, excellent mechanical properties, construction adhesive

Mixing ratio (Parts by weight) : 100 : 30 | Mix viscosity @ 25oC (mPa s) : 400 – 500 | Pot life @ 25oC (minutes) : > 60

Posted in PO PM Industry

Lapox A-31 | AH-717 | bonding, high shear strength, construction adhesive

Mixing ratio (Parts by weight) : 100 : 80 | Mix viscosity @ 25oC (mPa s) : 25,000 – 40,000 | Pot life @ 25oC (minutes) : 40 – 80

Posted in PO PM Industry

Lapox A-16 | K-5 | joints, hot cure, high temperature, construction adhesive

Mixing ratio (Parts by weight) : 100 : 27 | Pot life @ 25oC (minutes) : 170 – 190

Posted in PO PM Industry

Lapox A-16 | AH-800 | rapid cure, similar substrate, dissimilar substrate, construction adhesive

Mixing ratio (Parts by weight) : 100 : 100 | Mix viscosity @ 25oC (mPa s) : Thixotropic | Pot life @ 25oC (minutes) : 3 – 7

Posted in PO PM Industry

Lapox A-16 | AH-717 | marble, ceramic, metal, concrete, shock resistant, vibration resistant, construction adhesive

Mixing ratio (Parts by weight) : 100 : 80 | Mix viscosity @ 25oC (mPa s) : 15,000 – 20,000 | Pot life @ 25oC (minutes) : 150 – 200

Posted in PO PM Industry

Lapox ARL-143 | AH-335 | industrial; RTM; hand lay-up and infusion systems; moderate viscosity system; varying pot life; fire retardannt application

Mixing ratio (Parts by weight) : 100 : 15 | Pot life @ 25oC (minutes) : 85 – 95 | Mix viscosity @ 25oC (mPa s) : 3,500 – 5,000 | Glass transition temperature (Tg) (oC) : 95 – 105

Posted in PO PM Product

Lapox ARL-143 | AH-319 | industrial; RTM; hand lay-up and infusion systems; moderate viscosity system; varying pot life; fire retardannt application

Mixing ratio (Parts by weight) : 100 : 15 | Mix viscosity @ 25oC (mPa s) : 3,500 – 5,000 | Pot life @ 25oC (minutes) : 20 – 25 | Glass transition temperature (Tg) (oC) : 95 – 105

Posted in PO PM Product

Lapox ARL-135LV | AH-422 | industrial; RTM; hand lay-up and infusion systems; long pot life; high Tg; high glass trransition temperature

Mixing ratio (Parts by weight) : 100 : 35 | Mix viscosity @ 25oC (mPa s) : 400 – 600 | Pot life @ 25oC (minutes) : 300 – 350 | Glass transition temperature (Tg) (oC) : 110 – 120

Posted in PO PM Product

Lapox ARL-135 LV | AH-334 | industrial; RTM; hand lay-up and infusion systems; low viscosity system; variable pot life

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 600 – 750 | Pot life @ 25oC (minutes) : 25 – 35 | Glass transition temperature (Tg) (oC) : 75 – 85

Posted in PO PM Product

Lapox ARL-135 LV | AH-333 | industrial; RTM; hand lay-up and infusion systems; low viscosity system; variable pot life

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 600 – 750 | Pot life @ 25oC (minutes) : 14 – 20 | Glass transition temperature (Tg) (oC) : 75 – 85

Posted in PO PM Product

Lapox ARL-135 LV | AH-332 | industrial; RTM; hand lay-up and infusion systems; low viscosity system; variable pot life

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (m Pas) : 600 – 800 | Pot life @ 25oC (minutes) : 8 – 14 | Glass transition temperature (Tg) (oC) : 75 – 85

Posted in PO PM Product

Lapox ARL-135 | AH-337 | industrial; RTM; hand lay-up and infusion systems; moderate viscosity system; small to large components

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : 300 – 380 | Glass transition temperature (Tg) (oC) : 75 – 85

Posted in PO PM Product

Lapox AC-20 | accelerator and catalysts; accelerate anhydride; accelerate polyamides; accelerate amines; composite; electrical; coating

Appearance : Brown liquid or solid | Viscosity @ 25oC (mPa.s) : Max 100 | Melting point (oC): 36 – 42

Posted in PO PM Product

Lapox AC-19 | accelerator and catalysts; Liquid low reactive triamine; accelerate anhydride; accelerate polyamides; accelerate amines; composite; electrical; coating

Appearance : Clear liquid | Colour (Gardner) : Max 1 | Viscosity @ 25oC (mPa.s) : 10 – 30

Posted in PO PM Product

Lapox ARL-125 | AH-367GL | industrial; RTM; hand lay-up and infusion systems; low viscosity system; vacuum technique; pressure bag technique

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 300 – 700 | Pot life @ 25oC (minutes) : 300 – 380 | Glass transition temperature (Tg) (oC) : 75 – 85

Posted in PO PM Product

Lapox A-16 | AH-717 | marble; ceramic; metal; concrete; shock resistance; vibration resistant; construction adhesive

Mixing ratio (Parts by weight) : 100 : 80 | Mix viscosity @ 25oC (mPa s) : 15,000 – 20,000 | Pot life @ 25oC (minutes) : 150 – 200

Posted in PO PM Product

Lapox ARL-125 | AH-365GL | industrial; RTM; hand lay-up and infusion systems; low viscosity system; vacuum technique; pressure bag technique; GL approved system

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 200 – 300 | Pot life @ 25oC (minutes) : 50 – 60 | Glass transition temperature (Tg) (oC) : 75 – 85

Posted in PO PM Product

Lapox AC-14 (K-65) | accelerator and catalysts; Liquid tertiary amine; accelerate anhydride; accelerate polyamides; accelerate amines; composite; electrical; coating

Appearance : Clear yellow liquid | Colour (Gardner) : Max 6 | Viscosity @ 25oC (mPa.s) : 150 – 300 | Amine value (mg KOH/g) : 580 – 635

Posted in PO PM Product

Lapox AC-13 (K-13) | accelerator and catalysts; Liquid triamine; accelerate anhydride; accelerate polyamides; accelerate amines; composite; electrical; coating

Appearance : Clear liquid | Colour (Gardner) : Max 2 | Viscosity @ 25oC (mPa.s) : Max 10

Posted in PO PM Product

Lapox ARL-160 | AH-359 | industrial; prepreg; FRP; structural component

Mixing ratio (Parts by weight) : 100 : 5 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (oC) : 110 – 120

Posted in PO PM Product

Lapox ARL-160 | AH-357 | AC-22 | industrial; prepreg; hot melt system; structural component; infrastructure; general engineering application

Mixing ratio (Parts by weight) : 100 : 15 : 1-3 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (oC) : 110 – 120

Posted in PO PM Product

Lapox ASH-11 MIC | curing agent; 3,3’-Diaminodiphenyl sulfone Micronised; 3,3′-DDS

Chemistry : 3,3’-Diaminodiphenyl sulfone Micronised | Appearance : Micronised powder | Colour (Gardner) : Off-white to yellowish brown | Melting point (oC) : 167 – 175 | Purity by HPLC (%) : Min 99.0 | Ash content (%) : Max

Posted in PO PM Product

Lapox ASH-11 | curing agent; 3,3’-Diaminodiphenyl sulfone; 3,3′-DDS

Chemistry : 3,3’-Diaminodiphenyl sulfone | Appearance : Crystalline powder | Colour (Gardner) : White to brownish | Melting point (oC) : 167 – 175 | Purity by HPLC (%) : Min 99.0 | Ash content (%) : Max 0.10

Posted in PO PM Product

Lapox ARL-159 | AH-619 | industrial; prepreg; structural component; high temperature performance

Mixing ratio (Parts by weight) : 100 : 40 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (oC) : 180 – 200

Posted in PO PM Product

Lapox A-16 | K-5 | joints; hot cure; high temperature; construction adhesive

Mixing ratio (Parts by weight) : 100 : 27 | Pot life @ 25oC (minutes) : 170 – 190

Posted in PO PM Product

Lapox ASH-10 FF | curing agent; 4,4’-Diaminodiphenyl sulfone Free Flow; 4,4′-DDS

Chemistry : 4,4’-Diaminodiphenyl sulfone Free Flow | Appearance : Crystalline powder | Colour (Gardner) : White to off-white | Melting point (oC) : 176 – 185 | Purity by HPLC (%) : Min 99.0 | Ash content (%) : Max

Posted in PO PM Product

Lapox ARL-159 | AH-357 | AC-22 | industrial; prepreg; hot melt system

Mixing ratio (Parts by weight) : 100 : 15 : 2 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (Tg) (oC) : 155 – 165

Posted in PO PM Product

Lapox ASH-10 MIC | curing agent; 4,4’-Diaminodiphenyl sulfone Micronised; 4,4′-DDS

Chemistry : 4,4’-Diaminodiphenyl sulfone Micronised | Appearance : Micronised powder | Colour (Gardner) : White to off-white | Melting point (oC) : 176 – 180 | Purity by HPLC (%) : Min 99.0 | Ash content (%) : Max 0.10

Posted in PO PM Product

Lapox L-68 | K-66 | K-13 | industrial; prepregs and laminating systems; compressed laminate system; B-stage prepreg; FR-4 laminate

Mixing ratio (Parts by weight) : 100 : 32 : 1-3 | Pot life @ 25oC (weeks) : 2 – 3 | Glass transition temperature (Tg) (oC) : 130 – 140

Posted in PO PM Product

Lapox ASH-10 | curing agent; 4,4’-Diaminodiphenyl sulfone; 4,4′-DDS

Chemistry : 4,4’-Diaminodiphenyl sulfone | Appearance : Crystalline powder | Colour (Gardner) : White to off-white | Melting point (oC) : 176 – 185 | Purity by HPLC (%) : Min 99.0 | Ash content (%) : Max 0.10

Posted in PO PM Product

Lapox L-67 | K-66 | K-13 | industrial; prepregs and laminating systems; compressed laminate system; B-stage prepreg; G-10 laminate

Mixing ratio (Parts by weight) : 100 : 23 : 0.5-3.0 | Pot life @ 25oC (weeks) : 2 – 3 | Glass transition temperature (Tg) (oC) : 130 – 140

Posted in PO PM Product

Lapox AH-727 | Modified polyamide curing agent; curing agent for wet/damp condition; excellent adhesion with metal; excellent adhesion with concrete; flooring; primer

Colour (Gardner) : Max 12 | Viscosity @ 25oC (mPa.s) : 1,000 – 2,000 | Amine value (mg KOH/g) : 280 – 300 | Pot life @ 25oC (minutes) : 46 – 65 | Mixing ratio (Parts by weight) :

Posted in PO PM Product

Lapox A-16 | K-6 | marble; crack sealing; bonding; frames; construction adhesive

Mixing ratio (Parts by weight) : 100 : 10 | Mix viscosity @ 25oC (mPa s) : 4,000 – 6,000 | Pot life @ 25oC (minutes) : 20 – 30

Posted in PO PM Product

Lapox AH-725 | polyamide curing agent; bonding; fast reactivity

Colour (Gardner) : Max 8 | Viscosity @ 25oC (mPa.s) : 7,000 – 11,000 | Amine value (mg KOH/g) : 400 – 450 | Pot life @ 25oC (minutes) : 40 – 50 | Mixing ratio (Parts by weight) :

Posted in PO PM Product

Lapox L-12 | K-10 | K-86 | industrial; prepregs and laminating systems; compressed laminate system; B-stage prepreg; shelf life upto 6 months; G-11 laminate

Mixing ratio (Parts by weight) : 100 : 35 : 1-3 | Pot life @ 25oC (weeks) : 6 – 8 | Glass transition temperature (Tg) (oC) : 150 – 160

Posted in PO PM Product

Lapox AH-716 (K-29) | polyamide curing agent; low viscosity; solids coating; primer; floor coatings; protective coatings

Colour (Gardner) : Max 10 | Viscosity @ 25oC (mPa.s) : 2,500 – 5,500 | Amine value (mg KOH/g) : 202 – 225 | Pot life @ 25oC (minutes) : 80 – 100 | Mixing ratio (Parts by weight) :

Posted in PO PM Product

Lapox L-12 | K-5 | industrial; prepregs and laminating systems; compressed laminate system; prepreg; shorter shelf life; G-10 laminate; G-11 laminate

Mixing ratio (Parts by weight) : 100 : 27 | Pot life @ 25oC (hours) : > 4 | Glass transition temperature (Tg) (oC) : 150 – 160

Posted in PO PM Product

Lapox AH-714 | polyamide curing agent; low viscosity; grouts; crack injection; primer; tile gap filling; mortar

Colour (Gardner) : Max 8 | Viscosity @ 25oC (mPa.s) : 500 – 1,000 | Amine value (mg KOH/g) : 425 – 450 | Pot life @ 25oC (minutes) : 120 – 130 | Mixing ratio (Parts by weight) :

Posted in PO PM Product

Lapox ARPN-36 | K-86 | industrial; prepregs and laminating systems; compressed laminate system; B-stage prepreg

Mixing ratio (Parts by weight) : 100 : 3-6 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (Tg) (oC) : 165 – 180

Posted in PO PM Product

Lapox AH-713 (K-46) | polyamide curing agent; moderate viscosity; solids coating; primer; grouts; mortar; adhesives

Colour (Gardner) : Max 9 | Viscosity @ 25oC (mPa.s) : 12,000 – 18,000 | Amine value (mg KOH/g) : 350 – 400 | Pot life @ 25oC (minutes) : 60 – 80 | Mixing ratio (Parts by weight) :

Posted in PO PM Product

Lapox ARPN-36 | K-10 | K-86 | industrial; prepregs and laminating systems; compressed laminate system; B-stage prepreg; very high Tg; very high glass transition temperature

Mixing ratio (Parts by weight) : 100 : 32-40 : 1-3 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (Tg) (oC) : 170 – 185

Posted in PO PM Product

Lapox A-35 | K-35 | solvent based; excellent mechanical properties; construction adhesive

Mixing ratio (Parts by weight) : 100 : 30 | Mix viscosity @ 25oC (mPa s) : 400 – 500 | Pot life @ 25oC (minutes) : > 60

Posted in PO PM Product

Lapox AH-712 | polyamide curing agent; high viscosity; adhesives; floorings; marine coatings; industrial paints; protective coatings

Colour (Gardner) : Max 9 | Viscosity @ 25oC (mPa.s) : 45,000 – 60,000 | Amine value (mg KOH/g) : 290 – 320 | Pot life @ 25oC (minutes) : 110 – 130 | Mixing ratio (Parts by weight) :

Posted in PO PM Product

Lapox L-247 | K-918 | K-13 | industrial; filament winding and pultrusion; hot cure system; general purpose system; fire retardant

Mix viscosity @ 25oC : 100 : 64 : 1-3 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 110 – 120

Posted in PO PM Product

Lapox A-38 | K-99 | joints; moisture resistance; high adhesion; chemical resistant; construction adhesive

Mixing ratio (Parts by weight) : 100 : 40 | Mix viscosity @ 25oC (mPa s) : 50,000 – 1,00,000 | Pot life @ 25oC (minutes) : 20 – 25

Posted in PO PM Product

Lapox AH-711 | polyamide curing agent; high viscosity; adhesives; sealants

Colour (Gardner) : Max 9 | Viscosity @ 40oC (mPa.s) : 50,000 – 75,000 | Amine value (mg KOH/g) : 210 – 230 | Mixing ratio (Parts by weight) : 100 – 125

Posted in PO PM Product

Lapox L-12 | K-5200 | industrial; filament winding and pultrusion; hot cure system; low viscosity system; long pot life; high chemical resistance; high abrasion resistance

Mixing ratio (Parts by weight) : 100 : 24 | Mix viscosity @ 25oC (m Pas) : 4,000 – 6,000 | Pot life @ 25oC (days) : 2 – 3 | Glass transition temperature (Tg) (oC) : 180 – 190

Posted in PO PM Product

Lapox L-12 | K-918 | K-13 | industrial; filament winding and pultrusion; hot cure system; low viscosity; long pot life system; high chemical resistance; high abrasion resistance

Mixing ratio (Parts by weight) : 100 : 85 : 1-3 | Mix viscosity @ 25oC (m Pas) : 600 – 900 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 130 –

Posted in PO PM Product

Lapox A-53 | K-6 | marble; steel; metal; construction adhesive

Mixing ratio (Parts by weight) : 100 : 10 | Mix viscosity @ 25oC (mPa s) : 600 – 800 | Pot life @ 25oC (minutes) : 30 – 60

Posted in PO PM Product

Lapox L-12 | K-24 | industrial; filament winding and pultrusion; hot cure system; low viscosity system, long pot life,high chemical resistance; high abrasion resistance

Mixing ratio (Parts by weight) : 100 : 34 | Mix viscosity @ 25oC (mPa s) : 3,500 – 5,000 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 145 – 155

Posted in PO PM Product

Lapox L-12 | K-12 | K-13 | industrial; filament winding and pultrusion; hot cure system; standard system; fast reactivity

Mixing ratio (Parts by weight) : 100 : 100 : 1-3 | Mix viscosity @ 25oC (mPa s) : 400 – 700 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 95 –

Posted in PO PM Product

Lapox L-12 | AH-667 | industrial; filament winding and pultrusion; hot cure system; high chemical resistance; high abrasion resistance

Mixing ratio (Parts by weight) : 100 : 27 | Mix viscosity @ 50oC : 3,000 – 5,000 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 150 – 160

Posted in PO PM Product

Lapox A-555 | K-555 | toughness; quick; mechanical strength; construction; adhesive

Mixing ratio (Parts by weight) : 100 : 80 | Mix viscosity @ 25oC (mPa s) : 75,000 – 1,25,000 | Pot life @ 25oC (minutes) : 8 – 10

Posted in PO PM Product

Lapox K-540 (AH-540) | low viscosity curing agent; phenalkamine curing agent; marine coating; industrial; maitenance coating

Colour (Gardner) : Max 15 | Viscosity @ 25oC (mPa s) : 2,000 – 4,000 | Amine value (mg KOH/g) : 490 – 550 | Pot life @ 25oC (minutes) : 30 – 55 | Mixing ratio (Parts by weight)

Posted in None

Lapox L-12 | AH-113 | K-13 | industrial; filament winding and pultrusion; hot cure system; flame retardancy

Mixing ratio (Parts by weight) : 100 : 95 : 0.5-2.0 | Mix viscosity @ 25oC (mPa s) : 1,900 – 2,100 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 165 –

Posted in PO PM Product

Lapox ARA-12 | AH-718 | multi-purpose; zari; speaker; marble; ceramic; construction adhesive

Mixing ratio (Parts by weight) : 100 : 80 | Mix viscosity @ 25oC (mPa s) : 32,000 – 37,000 | Pot life @ 25oC (minutes) : 90 – 105

Posted in PO PM Product

Lapox ARL-136 | AH-126 | industrial; filament winding and pultrusion; hot cure system; superior fiber wetting; excellent mechanical properties; good surface finish

Mixing ratio (Parts by weight) : 100 : 90 | Mix viscosity @ 25oC (mPa s) : 300 – 600 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 115 – 125

Posted in PO PM Product

Lapox AH-543 (XH-80) | low colour; low viscosity; phenalkamine curing agent; anti-corrosive coating; marine coating

Colour (Gardner) : Max 15 | Viscosity @ 25oC (mPa.s): 2,000 – 5,000 | Amine value (mg KOH/g) : 300 – 350 | Pot life @ 25oC (minutes) : 50 – 65 | Mixing ratio (Parts by weight) : 67

Posted in PO PM Product

Lapox ARF-11 | K-918 | K-13 | industrial; filament winding and pultrusion; hot cure system; non-crystallisable; excellent chemical resistance

Mixing ratio (Parts by weight) : 100 : 90 : 1-3 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 115 –

Posted in PO PM Product

Lapox K-302 | modified polyamine; curing agent; self-leveling flooring; solvent-free coating; clear casting; protective coatings

Colour (Gardner) : Max 2 | Viscosity @ 25oC (mPa.s) : 300 – 600 | Amine value (mg KOH/g) : 260 – 310 | Pot life @ 25oC (minutes) : 40 – 50 | Mixing ratio (Parts by weight) :

Posted in PO PM Product

Lapox L-12 | AH-422 | industrial; filament winding and pultrusion; ambient cure system; long pot life; high Tg; high glass transition temperature

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 1,500 – 2,500 | Pot life @ 25oC (minutes) : 300 – 350 | Glass transition temperature (Tg) (oC) : 130 – 140

Posted in PO PM Product

Lapox L-12 | AH-411 | industrial; filament winding and pultrusion; ambient cure system; very high Tg; very high glass transition temperature; moderate viscosity

Mixing ratio (Parts by weight) : 100 : 22 | Mix viscosity @ 25oC (mPa s) : 800 – 1,200 | Pot life @ 25oC (minutes) : 90 – 120 | Glass transition temperature (Tg) (oC) : 140 – 155

Posted in PO PM Product

Lapox AH-440 | Cycloaliphatic amine; curing agent; accelerated curing agent; solvent-free coating; flooring; protective coatings

Colour (Gardner) : Max 2 | Viscosity @ 25oC (mPa.s) : 150 – 300 | Amine value (mg KOH/g) : 335 – 375 | Pot life @ 25oC (minutes) : 25 – 40 | Mixing ratio (Parts by weight) :

Posted in PO PM Product

Lapox ARC-15 | AH-122 | Electrical and Electronics; Bushings; Conventional Vacuum Casting; Pre-filled; Hot cure Indoor

Type of system : Pre-filled | Nature : Hot cure / Indoor| Mixing ratio (Parts by weight) : 100 : 100 | Glass transition temperature (Tg) (oC) : 110 – 120 | Thermal class : H | Applications : Switchgears, Insulators, Bushings

Posted in PO PM Product

Lapox L-12 | AH-337 | industrial; filament winding and pultrusion; ambient cure system; high Tg; high glass transition temperature;variable pot life

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 400 – 700 | Pot life @ 25oC (minutes) : 300 – 380 | Glass transition temperature (Tg) (oC) : 90 – 105

Posted in PO PM Product

Lapox AH-428 | Cycloaliphatic amine; curing agent;low viscosity;fast reactivity;self-leveling;high gloss;colour stability

Colour (Gardner) : Max 1 | Viscosity @ 25oC (mPa.s) : 50 – 150 | Amine value (mg KOH/g) : 340 – 390 | Pot life @ 25oC (minutes) : 30 – 40 | Mixing ratio (Parts by weight) :

Posted in PO PM Product

Lapox L-12 | AH-336 | industrial; filament winding and pultrusion; ambient cure system; high Tg; high glass transition temperature; variable pot life

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 600 – 1,200 | Pot life @ 25oC (minutes) : 80 – 100 | Glass transition temperature (Tg) (oC) : 90 – 105

Posted in PO PM Product

Lapox ARC-16 | AH-118 | ADP-11

Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (Parts by weight) : 100 : 80 : 0 – 8 |  Glass transition temperature (Tg) (oC) : 105 – 115 | Thermal class : F | Applications : Switchgears, Insulators, Bushings, Instrument

Posted in PO PM Product

Lapox L-12 | AH-335 | industrial; filament winding and pultrusion; ambient cure system

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 600 – 1,200 | Pot life @ 25oC (minutes) : 50 – 60 | Glass transition temperature (Tg) (oC) : 90 – 105

Posted in PO PM Product

Lapox AH-424 | Cycloaliphatic amine; curing agent; self-leveling flooring; high filler loading; protective coatings

Colour (Gardner) : Max 2 | Viscosity @ 25oC (mPa.s) : 20 – 50 | Amine value (mg KOH/g) : 330 – 360 | Pot life @ 25oC (minutes) : 25 – 35 | Mixing ratio (Parts by weight) :

Posted in PO PM Product

Lapox L-12 | AH-315 | industrial; filament winding and pultrusion; ambient cure system

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 500 – 800 | Pot life @ 25oC (hours) : 7 – 9 hr | Glass transition temperature (Tg) (oC) : 85 –

Posted in PO PM Product

Lapox AH-422 | Cycloaliphatic amine; unmodified low viscosity; curing agent; high Tg; high glass transition temperature; long pot life

Colour (Gardner) : Max 1 | Viscosity @ 25oC (mPa.s) : 100 – 140 | Pot life @ 25oC (minutes) : 200 – 250 | Mixing ratio (Parts by weight) : 32

Posted in PO PM Product

Lapox ARCH-11 | AH-214 | K-13

Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio (Parts by weight) : 100 : 90 : 0.5 – 2.0 | Glass transition temperature (Tg) (oC) : 100 – 110 | Thermal class : F | Applications : Switchgears, Insulators, Bushings,

Posted in PO PM Product

Lapox ARCH-11 | AH-215

Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio (Parts by weight): 100 : 90 |  Glass transition temperature (Tg) (oC) : 100 – 110 | Thermal class : F | Applications : Switchgears, Insulators, Bushings, Instrument Transformers

Posted in PO PM Product

Lapox AH-420 (K-964) | Cycloaliphatic amine; very low viscosity; moderate pot life; protective coating; flooring; chemical resistance

Colour (Gardner) : Max 3 | Viscosity @ 25oC (mPa.s) : 40 – 60 | Amine value (mg KOH/g) : 320 – 340 | Pot life @ 25oC (minutes) : 25 – 40 | Mixing ratio (Parts by weight) :

Posted in PO PM Product

Lapox ARCH-12 | AH-214 | K-13

Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio (Parts by weight) : 100 : 80 : 0.5 : 2.0 | Glass transition temperature (Tg) (oC) : 75 – 85 | Thermal class :

Posted in PO PM Product

Lapox AH-416 | Cycloaliphatic amine; moderate viscosity; transparent curing agent

Colour (Gardner) : Max 1 | Viscosity @ 25oC (mPa.s) : 400 – 600 | Amine value (mg KOH/g) : 250 – 300 | Pot life @ 25oC (minutes) : 30 – 45 | Mixing ratio (minutes) : 60

Posted in PO PM Product

Lapox ARCH-12 | AH-215

Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio (Parts by weight) : 100 : 80 | Glass transition temperature (Tg) (oC) : 75 – 85 | Thermal class : F | Applications :

Posted in PO PM Product

Lapox AH-412 (K-552) | Cycloaliphatic amine; low viscosity curing agent; excellent mechanical properties

Colour (Gardner) : Max 4 | Viscosity @ 25oC (mPa.s) : 50 – 150 | Pot life @ 25oC (minutes) : 110 – 160 | Mixing ratio (Parts by weight) : 38

Posted in PO PM Product

Lapox AH-411 | unmodified cycloaliphatic amine curing agent; coatings; flooring applications; composite applications; protective coatings

Colour (Gardner) : Max 1 | Viscosity @ 25oC (mPa.s) : 10 – 20 | Pot life @ 25oC (minutes) : 90 – 120 | Mixing ratio (Parts by weight) : 23

Posted in PO PM Product

Lapox ARCH-13 | AH-215

Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio (Parts by weight) : 100 : 70 | Glass transition temperature (Tg) (oC) : 100 – 110 | Thermal class : F | Applications :

Posted in PO PM Product

Lapox ARL-12 | AH-714 | industrial; filament winding and pultrusion; ambient cure system; superior adhesion; toughness

Mixing ratio (Parts by weight) : 100 : 50 | Mix viscosity @ 25oC (mPa s) : 1,200 – 1,500 | Pot life @ 25oC (minutes) : 120 – 150 | Glass transition temperature (Tg) (oC) : 55 – 65

Posted in PO PM Product

Lapox (AH-618) K-5200 | Aromatic amine; Elevated temperature curing curing agent; high Tg,high glass transition temperature;long pot life

Appearance : Yellow to brown liquid | Colour (Gardner) : Max 15 | Viscosity @ 25oC (mPa s) : 100 – 300 | Amine value (mg KOH/g) : 628 – 634 | Mixing ratio (Parts by weight) : 24

Posted in PO PM Product

Lapox K-450 | Aromatic amine; liquid curing agent; very low reactivity; composite

Appearance : Dark brown liquid (solidifies upon storage) | Viscosity @ 40oC (mPa.s) : 250 – 400 | Amine value (mg KOH/g) : 430 – 450 | Mixing ratio (Parts by weight) : 34

Posted in PO PM Product

Lapox K-92 | Aromatic amine; ambient cure modified curing agent; chemical resistant coating; tank lining; flooring; protective coating

Appearance : Brown liquid | Colour (Gardner) : Max 13 | Viscosity @ 25oC (mPa.s) : 5,000 – 7,500 | Amine value (Eq/kg) : 4.40 – 5.10 | Mixing ratio (Parts by weight) : 60

Posted in PO PM Product

Lapox C-17 | K-12 | K-13 | K-14

Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (Parts by weight) : 100 : 100 : 0.5 – 1.5 : 0 – 20 | Glass transition temperature (Tg) (oC) : 85 – 95

Posted in PO PM Product

Lapox K-49 | Aromatic amine; low viscosity; moderate reactivity; solvent-free coating; chemical resistant coating; floorings; linings; curing agent; protective coating

Appearance : Brown liquid | Colour (Gardner) : Max 13 | Viscosity @ 25oC (mPa.s) : 700 – 900 | Amine value (Eq/kg) : 4.70 – 5.00 | Mixing ratio (Parts by weight) : 60

Posted in PO PM Product

Lapox K-112 | accelerator and catalysts; Modified viscous tertiary amine;accelerate anhydride; accelerate polyamides; accelerate amines; composite; electrical; coating

Appearance : Clear brown liquid | Viscosity @ 25oC (mPa.s) : 1,000 – 1,800

Posted in PO PM Product

Lapox C-50 | K-61

Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (Parts by weight) : 100 : 80 | Glass transition temperature (Tg) (oC) : 105 – 125 | Thermal class : H | Applications :

Posted in PO PM Product

Lapox K-42 | Aromatic amine; curing agent; low viscosity; high reactive; protective coating

Appearance : Dark brown liquid | Colour (Gardner) : Max 16 | Viscosity @ 25oC (mPa.s) : 15,000 – 21,000 | Amine value (Eq/kg) : 4.40 – 4.80 | Mixing ratio (Parts by weight) : 60

Posted in PO PM Product

Lapox K-86 | accelerator and catalysts; Solid polyamine complex; accelerate aromatic amines

Appearance : White crystalline powder | Melting Point (oC) : Min 75

Posted in PO PM Product

Lapox C-50 | K-225

Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (Parts by weight) : 100 : 80 | Glass transition temperature (Tg) (oC) : 90 – 105 | Thermal class : H | Applications :

Posted in PO PM Product

Lapox K-41 | Aromatic amine; curing agent; low viscosity; chemical resistant; industrial flooring; coatings; tank linings; protective coating

Appearance : Brown liquid | Colour (Gardner) : Max 13 | Viscosity @ 25oC (mPa.s): 3,800 – 5,800 | Amine value (Eq/kg) : 4.70 – 5.10| Mixing ratio (Parts by weight) : 60

Posted in PO PM Product

Lapox ARC-30 | AH-714

Type of system : Pre-filled | Nature : Cold cure / Indoor | Mixing ratio (Parts by weight) : 100 : 25 | Glass transition temperature (Tg) (oC) : 60 – 70 | Thermal class : B | Applications :

Posted in PO PM Product

Lapox C-2 | K-1

Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (Parts by weight) : 100 : 30 | Glass transition temperature (Tg) (oC) : 115 – 130 | Thermal class : F | Applications :

Posted in PO PM Product

Lapox C-59 | K-1

Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (Parts by weight) : 100 : 30 | Glass transition temperature (Tg) (oC) : 115 – 130 | Thermal class : F | Applications :

Posted in PO PM Product

Lapox K-5 | Aromatic amine; curing agent; Pure 4,4′-diamino diphenyl methane; curing at elevated temperature

Appearance : White to tan pastilles | Mixing ratio (Parts by weight) : 26

Posted in PO PM Product

Lapox ARL-111 | AH-358 | ARS-101

Type of system : Unfilled | Nature : Hot cure Indoor | Mixing ratio (Parts by weight) : 100 : 15 | Glass transition temperature (Tg) (oC) : 80 – 90 | Thermal class : F | Applications : Paper

Posted in PO PM Product

Lapox AH-667 | Aromatic amine; curing agent; DDM based semi solid; composite

Appearance : Brown liquid | Colour (Gardner) : Max 12 | Viscosity @ 80oC (mPa.s) : 80 – 120 | Mixing ratio (Parts by weight) : 28

Posted in PO PM Product