Appearance : Dark violet lumps | Colour (Gardner) : > 18 | Methylol content (%) : 12 – 16 | Softening point (oC): 85 – 105

Appearance : Pale yellow lumps | Colour (Gardner) : Max 6 | Methylol content (%) : 14 – 17 | Softening point (oC) : 90 – 100

Appearance : Pale yellow lumps | Colour (Gardner) : Max 4 | Methylol content (%) : 8 – 12 | Melting point, capillary (oC) : 63 – 75 | Softening point (oC) : 65 – 80

Colour (Gardner) : Max 10 | Epoxy value (Eq/kg) : 7.00 – 8.00 | Viscosity @ 150oC (mPa s) : 2,500 – 4,000

Colour (Gardner) : Max 18 | Epoxy value (Eq/kg) : 7.40 – 8.50 | Viscosity @ 150oC (mPa s) : 2,000 – 4,000

Appearance : Clear colourless solution | Formaldehyde content: 37 ± 0.50 | Methanol content: Max 5 | Specific gravity : 1.095 – 1.115 | pH : 2.80 – 5.00

Colour (APHA) : Max 50 | Epoxy value (Eq/kg) : 5.71 – 5.95 | Viscosity @ 25oC (mPa s) : 4,000 – 5,000

Mixing ratio (Parts by weight) : 100 : 38 | Mix viscosity @ 25oC (mPa s) : 600 – 700 | Pot life @ 25oC (minutes) : 110 – 160 | Glass transition temperature (Tg) (o) : 115 – 130

Colour (Gardner) : Max 16 | Epoxy value (Eq/kg) : 8.15 – 9.50 | Viscosity @ 25oC (mPa s) : 100 – 200

Epoxy value (Eq/kg) : 2.15 – 2.22 | Viscosity @ 25oC (mPa s) : 160 – 190 | Softening point (oC) : 65 – 75 |

Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio (Parts by weight) : 100 : 70 | Glass transition temperature (Tg) (oC) : 100 – 110 | Thermal class : F

Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (parts by weight) : 100 : 80 : 0 – 8 | Glass transition temperature (Tg) (oC) : 105 – 115 | Thermal class :…

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 600 – 750 | Pot life @ 25oC (minutes) : 25 – 35 | Glass transition temperature (Tg) (oC) : 75 – 85

Colour (Gardner) : Max 12 | Epoxy value (Eq/kg) : 7.46 – 8.55 | Viscosity @ 50oC (mPa s) : 111,000 – 13,000

Mixing ratio (Parts by weight) : 100 : 50 | Mix viscosity @ 25oC (mPa s) : 600 – 1,000 | Pot life @ 25oC (minutes) : 130 – 150

Mixing ratio (Parts by weight) : 100 : 66 | Mix viscosity @ 25oC (mPa s) : 4,500 – 5,500 | Pot life @ 25oC (minutes) : 40 – 50

Colour (Gardner) : Max 8 | Viscosity @ 25oC (mPa s) : 7,000 – 11,000 | Amine value (mg KOH/g) : 400 – 450 | Pot life @ 25oC (minutes) : 40 – 50 | Mixing ratio (Parts by weight)…

Type of system : Pre-filled | Nature : Hot cure / Indoor | Mixing ratio (parts by weight) : 100 : 26 | Glass transition temperature (Tg) (oC) : 70 – 80 | Thermal class : F

Type of system : Pre-filled | Nature : Cold cure / Indoor | Mixing ratio (Parts by weight) : 100 : 25 | Glass transition temperature (Tg) (oC) : 60 – 70 | Thermal class : B

Type of system : Unfilled | Nature : Hot cure Indoor | Voltage class : MV / HV | Mixing ratio (parts by weight) : 100 : 15 | Glass transition temperature (Tg) (oC) : 80 – 90 | Thermal…

Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (Parts by weight) : 100 : 100 : 0.0 – 0.2 | Glass transition temperature (Tg) (oC) : 90 – 100 | Thermal class :…

Colour (Gardner) : Max 10 | Epoxy value (Eq/kg) : 2.20 – 2.60 | Viscosity @ 25oC (mPa s) : 20 – 50 | HyCl (%) : Max 1.00

Colour (Gardner) : Max 13 | Epoxy value (Eq/kg) : 1.80 – 2.40 | Viscosity @ 25oC (mPa s) : 40 – 70 | HyCl (%) : Max 1.00

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 4.10 – 4.50 | Viscosity @ 25oC (mPa s) : 20 – 35 | HyCl (%) : Max 0.20

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 5.90 – 6.30 | Viscosity @ 25oC (mPa s) : 6 – 8 | HyCl (%) : Max 0.20

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 5.30 – 6.00 | Viscosity @ 25oC (mPa s) : 6 – 8 | HyCl (%) : Max 0.20

Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (parts by weight) : 100 : 30 | Glass transition temperature (Tg) (oC) : 115 – 130 | Thermal class : F

Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (Parts by weight) : 100 : 30 | Glass transition temperature (Tg) (oC) : 115 – 130 | Thermal class : F

Type of system : Unfilled | Nature : Hot cure / Indoo | Mixing ratio (parts by weight) : 100 : 30 | Glass transition temperature (Tg) (oC) : 115 – 130 | Thermal class : F

Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (parts by weight) : 100 : 25 | Glass transition temperature (Tg) (oC) : 122 – 132 | Thermal class : F

Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio : 100 : 80 | Glass transition temperature (Tg) (oC) : 90 – 105 | Thermal class : H

Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio : 100 : 80 | Glass transition temperature (Tg) (oC): 105 – 125 | Thermal class : H

Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio : 100 : 100 : 0.5 – 1.5 : 0 – 20 | Glass transition temperature (Tg) (oC): 85 – 95 | Thermal class :…

Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio : 100 : 80 | Glass transition temperature (Tg) (oC) : 75 – 85 | Thermal class : F

Colour (Gardner) : Max 6 | Epoxy value (Eq/kg) : 1.54 – 2.00 | Viscosity @ 25oC (mPa s) : 250 – 500

Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio : 100 : 80 : 0.5 – 2.0 | Glass transition temperature (Tg) (oC) : 75 – 85 | Thermal class : F

Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio (Parts by weight) : 100 : 90 | Glass transition temperature (Tg) (oC): 100 – 110 | Thermal class : F

Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio : 100 : 90 : 0.5 – 2.0 | Mix viscosity : 1,000/80 | Glass transition temperature (Tg) (oC): 100 – 110 | Thermal class…

Type of system : Pre-filled | Nature : Hot cure Indoor | Mixing ratio (parts by weight) : 100 : 100 | Glass transition temperature (Tg) (oC) : 110 – 120 | Thermal class : H

Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 6.90 – 8.00 | Viscosity @ 25oC (mPa s) : 12 – 18 | HyCl (%) : Max 0.15

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 2.90 – 3.20 | Viscosity @ 25oC (mPa s) : 40 – 90 | HyCl (%) : Max 0.15

Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 6.20 – 6.80 | Viscosity @ 25oC (mPa s) : 15 – 30 | HyCl (%) : Max 0.15

Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 7.00 – 7.80 | Viscosity @ 25oC (mPa s) : 10 – 22 | HyCl (%) : Max 0.15

Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 6.20 – 7.30 | Viscosity @ 25oC (mPa s) : Max 2 | HyCl (%) : Max 0.10

Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 3.35 – 3.70 | Viscosity @ 25oC (mPa s) : 4 – 12 | HyCl (%) : Max 0.10

Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 5.50 – 6.30 | Viscosity @ 25oC (mPa s) : 500 – 1,100

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 5.10 – 5.40 | Viscosity @ 25oC (mPa s) : 860 – 960

Mixing ratio (Parts by weight) : 100 : 40 | Mix viscosity @ 25oC (mPa s) : 50,000 – 1,00,000 | Pot life @ 25oC (minutes) : 20 – 25

Mixing ratio (Parts by weight) : 100 : 65 | Mix viscosity @ 25oC (mPa s) : 8,000 – 10,000 | Pot life @ 25oC (minutes) : 15 – 330

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 5.40 – 5.90 | Viscosity @ 25oC (mPa s) : 1,000 – 1,500

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 5.40 – 5.90 | Viscosity @ 25oC (mPa s) : 1,700 – 2,500

Mixing ratio (Parts by weight) : 100 : 18 | Mix viscosity @ 25oC (mPa s) : 5,000 – 7,000 | Pot life @ 25oC (minutes) : 15 – 25

Mixing ratio (Parts by weight) : 100 : 18 | Mix viscosity @ 25oC (mPa s) : 600 – 700 | Pot life @ 25oC (minutes) : 15 – 25

Mixing ratio (Parts by weight) : 100 : 60 | Mix viscosity @ 25oC (mPa s) : 3,000 – 4,000 | Pot life @ 25oC (minutes) : 100 – 110

Mixing ratio (Parts by weight) : 100 : 60 | Mix viscosity @ 25oC (mPa s) : 6,000 – 8,000 | Pot life @ 25oC (minutes) : 15 – 300

Mixing ratio (Parts by weight) : 100 : 30 | Mix viscosity @ 25oC (mPa s) : 5,000 – 7,000 | Pot life @ 25oC (minutes) : 25 – 35

Mixing ratio (Parts by weight) : 100 : 100 | Mix viscosity @ 25oC (mPa s) : 2,000 – 4,000 | Pot life @ 25oC (minutes) : 30 – 40

Mixing ratio (Parts by weight) : 100 : 60 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : 40 – 50

Mixing ratio (Parts by weight) : 100 : 45 | Mix viscosity @ 25oC (mPa s) : 800 – 1,200 | Pot life @ 25oC (minutes) : 30 – 40

Mixing ratio (Parts by weight) :100 : 60 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : 40 – 50

Mixing ratio (Parts by weight) : 100 : 43 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : 30 – 35

Mixing ratio (Parts by weight) : 100 : 55 | Mix viscosity @ 25oC (mPa s) : 500 – 700 | Pot life @ 25oC (minutes) : 45 – 60

Mixing ratio (Parts by weight) : 100 : 60 | Mix viscosity @ 25oC (mPa s) : 3,000 – 6,000 | Pot life @ 25oC (minutes) : 35 – 330

Mixing ratio (Parts by weight) : 100 : 50 | Mix viscosity @ 25oC (mPa s) : 3,500 – 4,500 | Pot life @ 25oC (minutes) : 110 – 130

Mixing ratio (Parts by weight) : 100 : 50 | Mix viscosity @ 25oC (mPa s) : 3,000 – 4,500 | Pot life @ 25oC (minutes) : 60 – 80

Chemistry : 4,4′-Diaminodiphenyl methane | Appearance : Viscous brownish liquid | Viscosity @ 60oC (mPa s) : 1,400 – 2,000

Appearance : Light yellow to brown liquid | Viscosity @ 25oC (mPa s) : 100 – 300

Chemistry : 4,4′-Diaminodicyclohexyl methane | Appearance : Colourless transparent liquid | Melting point (oC) : 35 – 37

Chemistry : 3,3’-Dimethyl-4,4’-diaminodicyclohexyl methane | Viscosity @ 25oC (mPa s) : 100 – 140

Colour (Gardner) : Yellow powder | Melting point (oC) : 155 – 158

Colour (Gardner) : Yellow solid | Viscosity @ 125oC (mPa s) : 50 – 500

Colour (Gardner) : Yellowish liquid | Solid content (%) : 74 – 76 | Viscosity @ 25oC (mPa s) : 100 – 400

Colour (Gardner) : Yellow solid | Viscosity @ 100oC (mPa s) : 1,000 – 7,000 | Softening point (oC) : 60 – 80

Colour (Gardner) : Max 16 | Epoxy value (Eq/kg) : 4.17 – 4.44 | Viscosity @ 85oC (mPa s) : 1,000 – 1,500

Epoxy value (Eq/kg) : 9.80 – 10.6 | Viscosity @ 25oC (mPa s) : 1,500 – 4,800

Epoxy value (Eq/kg) : 9.10 – 9.80 | Viscosity @ 25oC (mPa s) : 7,000 – 13,000

Epoxy value (Eq/kg) : 9.40 – 10.50 | Viscosity @ 25oC (mPa s) : 550 – 850

Epoxy value (Eq/kg) : 8.70 – 9.50 | Viscosity @ 25oC (mPa s) : 2,000 – 5,000

Colour (Gardner) : Max 13 | Epoxy value (Eq/kg) : 5.88 – 6.66 | Viscosity @ 150oC (mPa s) : 30 – 55

Colour (Gardner) : Max 7 | Epoxy value (Eq/kg) : 7.52 – 8.47 | Viscosity @ 25oC (mPa s) : 7,000 – 12,000

Colour (Gardner) : Max 12 | Epoxy value (Eq/kg) : 8.55 – 9.00 | Viscosity @ 50oC (mPa s) : 3,000 – 6,000

Colour (Gardner) : Max 12 | Epoxy value (Eq/kg) : 7.46 – 8.55 | Viscosity @ 50oC (mPa s) : 7,000-19,000

Colour (Gardner) : Max 12 | Epoxy value (Eq/kg) : 7.46 – 8.55 | Viscosity @ 50oC (mPa s) : 17,000-19,000

Colour (Gardner) : Max 12 | Epoxy value (Eq/kg) : 7.46 – 8.55 | Viscosity @ 50oC (mPa s) : 13,000-15,000

Colour (Gardner) : Max 12 | Epoxy value (Eq/kg) : 7.46 – 8.55 | Viscosity @ 50oC (mPa s) : 10,000 – 12,000

Colour (Gardner) : Max 12 | Epoxy value (Eq/kg) : 7.46 – 8.55 | Viscosity @ 50oC (mPa s) : 7,000 – 11,000

Colour (Gardner) : Max 3 | Epoxy value (Eq/kg) : 5.59 – 5.81 | Viscosity @ 52oC (mPa s) : 1,100 – 1,700

Colour (Gardner) : Max 16 | Epoxy value (Eq/kg) : 6.50 – 7.50 | Viscosity @ 50oC (mPa s) : 1,000 – 2,500 | Hycl : Max 0.20

Colour (APHA) : Max 50 | Epoxy value (Eq/kg) : 5.71 – 5.95 | Viscosity @ 25oC (mPa s) : 4,000 – 5,000

Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 5.26 – 5.55 | Viscosity @ 25oC (mPa s) : 9,000 – 12,000

Epoxy value (Eq/kg) : 0.53 – 0.59 | Viscosity @ 25oC (mPa s) : 1,800 – 2,600 | Softening point (oC) : 110 – 120

Colour (Gardner) : Max 15 | Viscosity @ 25oC (mPa s) : 2,000 – 5,000 | Amine value (mg KOH/g) : 300 – 350 | Pot life @ 25oC (minutes) : 50 – 65 | Mixing ratio (Parts by weight)…

Colour (Gardner) : Max 3 | Viscosity @ 25oC (mPa s) : 40 – 60 | Amine value (mg KOH/g) : 320 – 340 | Pot life @ 25oC (minutes) : 25 – 40 | Mixing ratio (Parts by weight)…

Colour (Gardner) : Max 1 | Viscosity @ 25oC (mPa s) : 10 – 20 | Pot life @ 25oC (minutes) : 90 – 120 | Mixing ratio (Parts by weight) : 23

Colour : Max 2 | Viscosity @ 25oC (mPa s) : 1,500 – 2,000 | Amine value (Eq/kg) : 165 – 210 | Pot life @ 25oC (hours) : 4 – 6 | Mixing ratio (Parts by weight) : 30…

Colour (Gardner) : Clear liquid | Viscosity @ 25oC (mPa s) : 850 – 1,200 | Mixing ratio (Parts by weight) : 100 (with resin ARL-148)

Colour (Gardner) : Black | Viscosity @ 25oC (mPa s) : 3,000 – 6,000 | Pot life @ 25oC (minutes) : Min 20 | Mixing ratio (Parts by weight) : 100 (with resin ARB – 28)

Colour (Gardner) : Max 2 | Viscosity @ 25oC (mPa s) : 2,900 – 3,600 | Amine value (mg KOH/g) : 398 – 415 | Pot life @ 25oC (minutes) : 15 – 30 | Mixing ratio (Parts by weight)…

Colour (Gardner) : Max 4 | Viscosity @ 25oC (mPa s) : 200 – 300 | Amine value (Eq/kg) : 17.00 – 17.80 | Pot life @ 25oC (minutes) : 25 – 35 | Mixing ratio (Parts by weight) :…

Colour (Gardner) : Max 5 | Viscosity @ 25oC (mPa s) : Max 10 | Pot life @ 25oC (minutes) : 20 – 25 | Mixing ratio (Parts by weight) : 10 – 12

Colour (Gardner) : Max 3 | Pot life @ 25oC (minutes) : 30 – 40 | Mixing ratio (Parts by weight) : 10 – 12

Colour (Gardner) : Max 5 | Viscosity @ 25oC (mPa s) : 100 – 550 | Amine value (mg KOH/g) : 500 – 1,000 | Pot life @ 25oC (minutes) : 5 – 30 | Mixing ratio (Parts by weight)…

Colour (Gardner) : Max 4 | Viscosity @ 25oC (mPa s) : 500 – 1,000 | Amine value (mg KOH/g) : 650 – 750 | Pot life @ 25oC (minutes) : 30 – 40 | Mixing ratio (Parts by weight)…

Colour (Gardner) : Max 1 | Viscosity @ 25oC (mPa s) : 5 – 10 | Amine value (mg KOH/g) : 680 – 720 | Pot life @ 25oC (minutes) : 40 – 50 | Mixing ratio (Parts by weight)…

Colour (Gardner) : Max 2 | Viscosity @ 25oC (mPa s) : 30 – 100 | Amine value (mg KOH/g) : 290 – 320 | Pot life @ 25oC (minutes) : 100 – 125 | Mixing ratio (Parts by weight)…

Colour (Gardner) : Max 4 | Viscosity @ 25oC (mPa s) : 50 – 60 | Pot life @ 25oC (minutes) : 35 – 50 | Mixing ratio (Parts by weight) : 15

Appearance : Brown liquid | Colour (Gardner) : Max 13 | Viscosity @ 25oC (mPa s) : 5,000 – 7,500 | Amine value (Eq/kg) : 4.40 – 5.10 | Mixing ratio (Parts by weight) : 60

Mixing ratio (Parts by weight) : 100 : 15 | Mix viscosity @ 25oC (mPa s) : 3,500 – 5,000 | Pot life @ 25oC (minutes) : 85 – 95 | Glass transition temperature (Tg) (oC) : 95 – 105

Mixing ratio (Parts by weight) : 100 : 15 | Mix viscosity @ 25oC (mPa s) : 3,500 – 5,000 | Pot life @ 25oC (minutes) : 20 – 25 | Glass transition temperature (Tg) (oC) : 95 – 105

Colour (APHA) : Max 100 | Epoxy value (Eq/kg) : 4.16 – 4.54 | Viscosity @ 25oC (mPa s) : 2,000 – 4,000

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 6.00 – 6.40 | Viscosity @ 25oC (mPa s) : 1,200 – 1,600

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 5.70 – 6.30 | Viscosity @ 25oC (mPa s) : 2,000 – 5,000

Mixing ratio (Parts by weight) : 100 : 3-6 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (Tg) (oC) : 165 – 180

Mixing ratio (Parts by weight) : 100 : 32-40 : 1-3 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (Tg) (oC) : 170 – 185

Mixing ratio (Parts by weight) : 100 : 64 : 1-3 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 110 – 120

Mixing ratio (Parts by weight) : 100 : 34 | Mix viscosity @ 25oC (mPa s) : 3,500 – 5,000 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) oC : 145 – 155

Mixing ratio (Parts by weight) : 100 : 100 : 1-3 | Mix viscosity @ 25oC (mPa s) : 400 – 700 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 95 –…

Mixing ratio (Parts by weight) : 100 : 27 | Mix viscosity @ 50oC (mPa s) : 3,000 – 5,000 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 150 – 160

Mixing ratio (Parts by weight) : 100 : 95 : 0.5-2.0 | Mix viscosity @ 25oC (mPa s) : 1,900 – 2,100 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 165 –…

Mixing ratio (Parts by weight) : 100 : 90 | Mix viscosity @ 25oC (mPa s) : 300 – 600 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 115 – 125

Mixing ratio (Parts by weight) : 100 : 90 : 1-3 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 115 –…

Mixing ratio (Parts by weight) : 100 : 85 : 1-3 | Mix viscosity @ 25oC (mPa s) : 200 – 500 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 105 –…

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 400 – 700 | Pot life @ 25oC (minutes) : 300 – 380 | Glass transition temperature (Tg) oC : 90 – 105

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 600 – 1,200 | Pot life @ 25oC (minutes) : 80 – 100 | Glass transition temperature (Tg) oC : 90 – 105

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 600 – 1,200 | Pot life @ 25oC (minutes) : 50 – 60 | Glass transition temperature (Tg) oC : 90 – 105

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 500 – 800 | Pot life @ 25oC (minutes) : 7 – 9 hr | Glass transition temperature (Tg) oC : 85 –…

Mixing ratio (Parts by weight) : 100 : 50 | Mix viscosity @ 25oC (mPa s) : 1,200 – 1,500 | Pot life @ 25oC (minutes) : 120 – 150 | Glass transition temperature (Tg) oC : 55 – 65

Mixing ratio (Parts by weight) : 100:32 | Mix viscosity @ 25oC (mPa s) : 600 – 800 | Pot life @ 25oC (minutes) : 8 – 14 | Glass transition temperature (Tg) (oC) : 80 – 90

Mixing ratio (Parts by weight) : 100 : 20 | Mix viscosity @ 25oC (mPa s) : Paste (colourless) | Pot life @ 25oC (minutes) : 15 – 20 | Glass transition temperature (Tg) (oC) : 95 – 115

Mixing ratio (Parts by weight) : 100 : 10 | Mix viscosity @ 25oC (mPa s) : Paste (blue) | Pot life @ 25oC (minutes) : 15 – 20 | Glass transition temperature (Tg) (oC) : 75 – 85

Mixing ratio (Parts by weight) : 100 : 14 | Mix viscosity @ 25oC (mPa s) : Paste (white) | Pot life @ 25oC (minutes) : 25 – 30 | Glass transition temperature (Tg) (oC) : 75 – 85

Mixing ratio (Parts by weight) : 100 : 24 | Mix viscosity @ 25oC (mPa s) : 250 – 400 | Pot life @ 25oC (minutes) : 90 – 120 | Glass transition temperature (Tg) (oC) : 125 – 135

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 600 – 750 | Pot life @ 25oC (minutes) : 14 – 20 | Glass transition temperature (Tg) (oC) : 75 – 85

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 600 – 800 | Pot life @ 25oC (minutes) : 8 – 14 | Glass transition temperature (Tg) (oC) : 75 – 85

Epoxy value (Eq/kg) : 1.08 – 1.18 | Viscosity @ 25oC (mPa s) : 430 – 550 | Softening point (oC) : 90 – 100

Mixing ratio (Parts by weight) : 100 : 5 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (Tg) (oC) : 110 – 120

Mixing ratio (Parts by weight) : 100 : 15 : 2 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (Tg) (oC) : 155 – 165

Mixing ratio (Parts by weight) : 100 : 32 : 1-3 | Pot life @ 25oC (weeks) : 2 – 3 | Glass transition temperature (Tg) (oC) : 130 – 140

Mixing ratio (Parts by weight) : 100 : 23 : 0.5-3.0 | Pot life @ 25oC (weeks) : 2 – 3 | Glass transition temperature (Tg) (oC) : 130 – 140

Mixing ratio (Parts by weight) : 100 : 35 : 1-3 | Pot life @ 25oC (weeks) : 6 – 8 weeks | Glass transition temperature (Tg) (oC) : 150 – 160

Epoxy value (Eq/kg) : 1.42 – 1.53 | Viscosity @ 25oC (mPa s) : 375 – 475 | Softening point (oC) : 80 – 90

Appearance : Clear yellow liquid | Colour (Gardner) : Max 6 | Viscosity @ 25oC (mPa s) : 150 – 300 | Amine value (mg KOH/g) : 580 – 635

Mixing ratio (Parts by weight) : 100 : 27 | Pot life @ 25oC (hours) : > 4 | Glass transition temperature (Tg) (oC) : 150 – 160

Colour (Gardner) : Max 2 | Viscosity @ 25oC (mPa s) : 300 – 600 | Amine value (mg KOH/g) : 260 – 310 | Pot life @ 25oC (minutes) : 40 – 50 | Mixing ratio (Parts by weight)…

Colour (Gardner) : Max 2 | Viscosity @ 25oC (mPa s) : 150 – 300 | Amine value (mg KOH/g) : 335 – 375 | Pot life @ 25oC (minutes) : 25 – 40 | Mixing ratio (Parts by weight)…

Colour (Gardner) : Max 1 | Viscosity @ 25oC (mPa s) : 50 – 150 | Amine value (mg KOH/g) : 340 – 390 | Pot life @ 25oC (minutes) : 30 – 40 | Mixing ratio (Parts by weight)…

Mixing ratio (Parts by weight) : 100 : 85 : 1-3 | Mix viscosity @ 25oC (mPa s) : 600 – 900 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 130 –…

Colour (Gardner) : Max 2 | Amine value (mg KOH/g) : 330 – 360 | Pot life @ 25oC (minutes) : 20 – 50 | Mixing ratio (Parts by weight) : 45

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 1,500 – 2,500 | Pot life @ 25oC (minutes) : 300 – 350 | Glass transition temperature (Tg) (oC) : 130 – 140

Colour (Gardner) : Max 1 | Viscosity @ 25oC (mPa s) : 400 – 600 | Amine value (mg KOH/g) : 250 – 300 | Pot life @ 25oC (minutes) : 30 – 45 | Mixing ratio (Parts by weight)…

Colour (Gardner) : Max 12 | Viscosity @ 25oC (mPa s) : 1,000 – 2,000 | Amine value (mg KOH/g) : 280 – 300 | Pot life @ 25oC (minutes) : 46 – 65 | Mixing ratio (Parts by weight)…

Colour (Gardner) : Max 10 | Viscosity @ 25oC (mPa s) : 2,500 – 5,500 | Amine value (mg KOH/g) : 202 – 225 | Pot life @ 25oC (minutes) : 80 – 100 | Mixing ratio (Parts by weight)…

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 200 – 300 | Pot life @ 25oC (minutes) : 300 – 380 | Glass transition temperature (Tg) (oC) : 75 – 85

Colour (Gardner) : Max 8 | Viscosity @ 25oC (mPa s) : 500 – 1,000 | Amine value (mg KOH/g) : 425 – 450 | Pot life @ 25oC (minutes) : 120 – 130 | Mixing ratio (Parts by weight)…

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 300 – 700 | Pot life @ 25oC (minutes) : 80 – 100 | Glass transition temperature (Tg) (oC) : 75 – 85

Colour (Gardner) : Max 9 | Viscosity @ 25oC (mPa s) : 12,000 – 18,000 | Amine value (mg KOH/g) : 350 – 400 | Pot life @ 25oC (minutes) : 60 – 80 | Mixing ratio (Parts by weight)…

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 300 – 700 | Pot life @ 25oC (minutes) : 50 – 60 | Glass transition temperature (Tg) (oC) : 75 – 85

Colour (Gardner) : Max 9 | Viscosity @ 25oC (mPa s) : 45,000 – 60,000 | Amine value (mg KOH/g) : 290 – 320 | Pot life @ 25oC (minutes) : 110 – 130 | Mixing ratio (Parts by weight)…

Mixing ratio (Parts by weight) : 100 : 6 | Mix viscosity @ 25oC (mPa s) : Paste (grey) | Pot life @ 25oC (minutes) : 15 – 20 | Glass transition temperature (Tg) (oC) : 85 – 95

Mixing ratio (Parts by weight) : 100 : 42 | Mix viscosity @ 25oC (mPa s) : 2,500 – 3,000 | Pot life @ 25oC (minutes) : 600 – 700 | Glass transition temperature (Tg) (oC) : 190 – 220

Mixing ratio (Parts by weight) : 100 : 30 | Mix viscosity @ 25oC (mPa s) : 200 – 300 | Pot life @ 25oC (minutes) : 90 – 120 | Glass transition temperature (Tg) (oC) : 100 – 110

Colour (Gardner) : Max 9 | Viscosity @ 40oC (mPa s) : 50,000 – 75,000 | Amine value (mg KOH/g) : 210 – 230 | Mixing ratio (Parts by weight) : 100 – 125

Appearance : Brown liquid | Colour (Gardner) : Max 13 | Viscosity @ 25oC (mPa s) : 700 – 900 | Amine value (Eq/kg) : 4.70 – 5.00 | Mixing ratio (Parts by weight) : 60

Mixing ratio (Parts by weight) : 100 : 30 | Mix viscosity @ 25oC (mPa s) : 400 – 600 | Pot life @ 25oC (minutes) : 120 – 180 | Glass transition temperature (Tg) (oC) : 130 – 140

Appearance : Dark brown liquid | Colour (Gardner) : Max 16 | Viscosity @ 25oC (mPa s) : 15,000 – 21,000 | Amine value (Eq/kg) : 4.40 – 4.80 | Mixing ratio (Parts by weight) : 60

Appearance : Brown liquid | Colour (Gardner) : Max 13 | Viscosity @ 25oC (mPa s) : 3,800 – 5,800 | Amine value (Eq/kg) : 4.70 – 5.10 | Mixing ratio (Parts by weight) : 60

Epoxy value (Eq/kg) : Max 0.08 | Viscosity @ 25oC (mPa s) : 2,000 – 5,000 | Non-volatile content (%) : 49 – 51 (160oC/2h)

Epoxy value (Eq/kg) : 1.80 – 2.20 | Viscosity @ 25oC (mPa s) : 14,000 – 20,000 | Non-volatile content (%) : 74 – 76 (150oC/2h)

Epoxy value (Eq/kg) : 1.90 – 2.20 | Viscosity @ 25oC (mPa s) : 9,000 – 13,000 | Non-volatile content (%) : 74 – 76 (150oC/2h)

Epoxy value (Eq/kg) : 3.10 – 3.40 | Viscosity @ 25oC (mPa s) : 600 – 850 | Non-volatile content (%) : 79 – 81 (150oC/1h)

Colour (Gardner) : Max 3 | Epoxy value (Eq/kg) : 5.50 – 6.00 | Viscosity @ 25oC (mPa s) : 25,000 – 35,000

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 4.40 – 4.60 | Viscosity @ 25oC (mPa s) : 800 – 1,500 | Non-volatile content (%) :79 – 81 (150oC/1h)

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 4.40 – 4.60 | Viscosity @ 25oC (mPa s) : 150 – 350 | Non-volatile content (%): 79 – 81 (105oC/2h)

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : 300 – 380 | Glass transition temperature (Tg) (oC) : 75 – 85

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 500 – 700 | Pot life @ 25oC (minutes) : 80 – 100 | Glass transition temperature (Tg) (oC) : 75 – 85

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 500 – 700 | Pot life @ 25oC (minutes) : 50 – 60 | Glass transition temperature (Tg) (oC) : 75 – 85

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 700 – 1200 | Pot life @ 25oC (minutes) : 25 – 35 | Glass transition temperature (Tg) (oC) : 80 – 90

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 700 – 1200 | Pot life @ 25oC (minutes) : 14 – 20 | Glass transition temperature (Tg) (oC) : 80 – 90

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 700 – 1200 | Pot life @ 25oC (minutes) : 8 – 14 | Glass transition temperature (Tg) (oC) : 80 – 90

Mixing ratio (Parts by weight) : 100 : 22 | Mix viscosity @ 25oC (mPa s) : 800 – 1,200 | Pot life @ 25oC (minutes) : 90 – 120 | Glass transition temperature (Tg) (oC) : 140 – 155

Mixing ratio (Parts by weight) : 100 : 42 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : 600 – 700 | Glass transition temperature (Tg) (oC) : 170 – 200

Mixing ratio (Parts by weight) : 100 : 35 | Mix viscosity @ 25oC (mPa s) : 400 – 600 | Pot life @ 25oC (minutes) : 300 – 350 | Glass transition temperature (Tg) (oC) : 110 – 120

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 200 – 300 | Pot life @ 25oC (minutes) : 350 – 450 | Glass transition temperature (Tg) (oC) : 75 – 85

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 200 – 300 | Pot life @ 25oC (minutes) : 300 – 380 | Glass transition temperature (Tg) (oC) : 75 – 85

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 300 – 700 | Pot life @ 25oC (minutes) : 50 – 60 | Glass transition temperature (Tg) (oC) : 75 – 85

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 300 – 700 | Pot life @ 25oC (minutes) : 80 – 100 | Glass transition temperature (Tg) (oC) : 75 – 85

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 300 – 700 | Pot life @ 25oC (minutes) : 50 – 60 | Glass transition temperature (Tg) (oC) : 75 – 85

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 600 – 750 | Pot life @ 25oC (minutes) : 25 – 35 | Glass transition temperature (Tg) (oC) : 80 – 90

Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 600 – 750 | Pot life @ 25oC (minutes) : 14 – 20 | Glass transition temperature (Tg) (oC) : 80 – 90

Mixing ratio (Parts by weight) : 100 : 15 : 1-3 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (Tg) (oC) : 110 – 120

Mixing ratio (Parts by weight) : 100 : 40 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (Tg) (oC) : 180 – 200

Appearance : Clear brown liquid | Viscosity @ 25oC (mPa s) : 1,000 – 1,800

Appearance : White crystalline powder | Melting point (oC) : Min 75

Appearance : Brown liquid or solid | Viscosity @ 25oC (mPa s) : Max 100 | Melting point (oC) : 36 – 42

Appearance : Clear liquid | Colour (Gardner) : Max 1 | Viscosity @ 25oC (mPa s) : 10 – 30

Appearance : Clear liquid | Colour (Gardner) : Max 2 | Viscosity @ 25oC (mPa s) : Max 10

Appearance : White crystal | Melting point (oC) : Min 127 – 134

Appearance : White crystal | Melting point (oC) : 154 – 156

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 5.50 – 5.70 | Viscosity @ 52oC (mPa s) : 20,000 – 50,000

Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 5.20 – 6.20 | Viscosity @ 25oC (mPa s) : 20 – 50 | HyCl (%) : Max 0.20

Chemistry : 3,3′-Diethyl-4,4′-diaminodiphenyl methane| Appearance : Dark brown liquid | Viscosity @ 40oC (mPa s) : 250 – 400

Chemistry : 4,4′-Diaminodiphenyl methane | Appearance : White to tan pastilles | Melting point (oC) : 88 – 92

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 5.50 – 5.75 | Viscosity @ 25oC (mPa s) : 4,500 – 6,500

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 5.55 – 5.80 | Viscosity @ 25oC (mPa s) : 6,500 – 8,500

Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 5.20 – 5.50 | Viscosity @ 25oC (mPa s) : 450 – 650

Colour (Gardner) : Max 1 | Colour (AHPA) : Max 75 | Epoxy value (Eq/kg) : 5.12 – 5.55 | Viscosity @ 25oC (mPa s) : 500 – 700

Colour (Gardner) : Max 1 | Colour (APHA) : Max 150 | Epoxy value (Eq/kg) : 4.65 – 5.12 | Viscosity @ 25oC (mPa s) : 500 – 700

Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 5.00 – 5.50 | Viscosity @ 25oC (mPa s) : 4,500 – 5,500

Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 7.00 – 7.80 | Viscosity @ 25oC (mPa s) : 10 – 22 | HyCl (%) : Max 0.15

Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 5.00 – 5.50 | Viscosity @ 25oC (mPa s) : 1,500 – 2,000

Colour (Gardner) : Milky white liquid | Epoxy value (Eq/kg) : 4.80 – 5.10 | Viscosity @ 25oC (mPa s) : 550 – 750

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 4.90 – 5.20 | Viscosity @ 25oC (mPa s) : 800 – 1,200

Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 5.25 – 5.45 | Viscosity @ 25oC (mPa s) : 11,000 – 15,000

Colour (APHA) : Max 50 | Epoxy value (Eq/kg) : 5.25 – 5.45 | Viscosity @ 25oC (mPa s) : 8,000 – 11,000

Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 4.30 – 4.70 | Viscosity @ 25oC (mPa s) : 20,000 – 28,000

Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 5.25 – 5.45 | Viscosity @ 25oC (mPa s) : 11,000 – 15,000

Epoxy value (Eq/kg) : 0.34 – 0.42 | Viscosity @ 25oC (mPa s) : 5,000 – 10,000 | Softening point (oC) : 125 – 140

Epoxy value (Eq/kg) : 1.12 – 1.20 | Viscosity @ 25oC (mPa s) : 550 – 700 | Softening point (oC) : 90 – 102

Mixing ratio (Parts by weight) : 100 : 45 | Mix viscosity @ 25oC (mPa s) : Thixotropic paste | Pot life @ 25oC (minutes) : 25 – 35 | Glass transition temperature (Tg) (oC) : 75 – 85

Mixing ratio (Parts by weight) : 100 : 45 | Mix viscosity @ 25oC (mPa s) : Thixotropic paste | Pot life @ 25oC (minutes) : 50 – 70 | Glass transition temperature (Tg) (oC) : 75 – 85

Mixing ratio (Parts by weight) : 100 : 45 | Mix viscosity @ 25oC (mPa s) : Thixotropic paste | Pot life @ 25oC (minutes) : 90 – 120 | Glass transition temperature (Tg) (oC) : 75 – 85

Mixing ratio (Parts by weight) : 100 : 45 | Mix viscosity @ 25oC (mPa s) : Thixotropic paste | Pot life @ 25oC (minutes) : 130 – 170 | Glass transition temperature (Tg) (oC) : 75 – 85

Mixing ratio (Parts by weight) : 100 : 40 | Mix viscosity @ 25oC (mPa s) : Thixotropic | Pot life @ 25oC (minutes) : 35 – 45

Mixing ratio (Parts by weight) : 100 : 50 | Mix viscosity @ 25oC (mPa s) : 50,000 – 1,00,000 | Pot life @ 25oC (minutes) : 35 – 50

Mixing ratio (Parts by weight) : 100 : 80 | Mix viscosity @ 25oC (mPa s) : 75,000 – 1,25,000 | Pot life @ 25oC (minutes) : 8 – 10

Mixing ratio (Parts by weight) : 100 : 10 | Mix viscosity @ 25oC (mPa s) : 4,000 – 6,000 | Pot life @ 25oC (minutes) : 20 – 30

Type of system : Unfilled | Nature : Cold cure / Indoor | Mixing ratio (Parts by weight) : 100 : 10 | Glass transition temperature (Tg) (oC) : 60 – 70

Mixing ratio (Parts by weight) : 100 : 100 | Mix viscosity @ 25oC (mPa s) : 3,000 – 4,000 | Pot life @ 25oC (minutes) : 25 – 35

Mixing ratio (Parts by weight) : 100 : 80 | Mix viscosity @ 25oC (mPa s) : 32,000 – 37,000 | Pot life @ 25oC (minutes) : 90 – 105

Mixing ratio (Parts by weight) : 100 : 80 | Mix viscosity @ 25oC (mPa s) : 75,000 – 1,25,000 | Pot life @ 25oC (minutes) : 8 – 10

Mixing ratio (Parts by weight) : 100 : 10 | Mix viscosity @ 25oC (mPa s) : 600 – 800 | Pot life @ 25oC (minutes) : 30 – 60

Mixing ratio (Parts by weight) : 100 : 30 | Mix viscosity @ 25oC (mPa s) : 400 – 500 | Pot life @ 25oC (minutes) : > 60

Mixing ratio (Parts by weight) : 100 : 80 | Mix viscosity @ 25oC (mPa s) : 25,000 – 40,000 | Pot life @ 25oC (minutes) : 40 – 80

Mixing ratio (Parts by weight) : 100 : 27 | Pot life @ 25oC (minutes) : 170 – 190

Mixing ratio (Parts by weight) : 100 : 100 | Mix viscosity @ 25oC (mPa s) : Thixotropic | Pot life @ 25oC (minutes) : 3 – 7

Mixing ratio (Parts by weight) : 100 : 80 | Mix viscosity @ 25oC (mPa s) : 15,000 – 20,000 | Pot life @ 25oC (minutes) : 150 – 200

Colour (Gardner) : Max 1 | Viscosity @ 25oC (mPa s) : 5 – 15 | Pot life @ 25oC (hours) : 7 – 9 | Mixing ratio (Parts by weight) : 32