Mixing ratio (Parts by weight) : 100 : 100 | Mix viscosity @ 25oC (mPa s) : 3,000 – 4,000 | Pot life @ 25oC (minutes) : 25 – 35
Updates
Month: June 2017
Lapox A-16 | AH-800 | rapid cure; similar substrate; dissimilar substrate; composite adhesive
Mixing ratio (Parts by weight) : 100 : 100 | Mix viscosity @ 25oC (mPa s) : Thixotropic | Pot life @ 25oC (minutes) : 3 – 7
Posted in PO PM Product
Lapox ARCH-11 | K-3 | K-13 | industrial; filament winding and pultrusion; hot cure system; out door application; UV resistance
Mixing ratio (Parts by weight) : 100 : 85 : 1-3 | Mix viscosity @ 25oC (mPa s) : 200 – 500 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) oC : 105 –…
Posted in PO PM Product
Lapox A-83 | K-83 | gap filling; standard adhesive; composite adhesive
Mixing ratio (Parts by weight) : 100 : 40 | Mix viscosity @ 25oC (mPa s) : Thixotropic | Pot life @ 25oC (minutes) : 35 – 45
Posted in PO PM Product
Lapox B-11 | K-48 | construction; Maintenance; repair; crack-filling; quick setting
Mixing ratio (Parts by weight) : 100 : 18 | Mix viscosity @ 25oC (mPa s) : 5,000 – 7,000 | Pot life @ 25oC (minutes) : 15 – 25
Posted in PO PM Product
Lapox B-47 | K-48 | construction; Maintenance; grouting; quick setting. excellent adhesion; good strength
Mixing ratio (Parts by weight) : 100 : 18 | Mix viscosity @ 25oC (mPa s) : 600 – 700 | Pot life @ 25oC (minutes) : 15 – 25
Posted in PO PM Product
Lapox B-11 | K-49 | construction; Maintenance; chemical resistant flooring; protection of metal structures; protection from corrosive chemicals; protection from alkali; protection from solvents
Mixing ratio (Parts by weight) : 100 : 60 | Mix viscosity @ 25oC (mPa s) : 3,000 – 4,000 | Pot life @ 25oC (minutes) : 100 – 110
Posted in PO PM Product
Lapox B-11 | K-41 | K-42 | construction; Maintenance; chemical resistant flooring; variable potlife system; excellent acid and alkali resistance
Mixing ratio (Parts by weight) : 100 : 60 | Mix viscosity @ 25oC (mPa s) : 6,000 – 8,000 | Pot life @ 25oC (minutes) : 15 – 300
Posted in PO PM Product
Lapox ARPN-54 | K-41 | K-42 | construction; Maintenance; chemical resistant flooring; high viscosity system; variable pot life system; chemical resistance; industrial flooring
Mixing ratio (Parts by weight) : 100 : 65 | Mix viscosity @ 25oC (mPa s) : 8,000 – 10,000 | Pot life @ 25oC (minutes) : 15 – 330
Posted in PO PM Product
Lapox ARPN-42 | AH-105 | construction; Maintenance; chemical resistant flooring; coal tar modified system; coating of pipes; vehile chassis; concrete structure
Mixing ratio (Parts by weight) : 100 : 100 | Mix viscosity @ 25oC (mPa s) : 2,000 – 4,000 | Pot life @ 25oC (minutes) : 30 – 40
Posted in PO PM Product
Lapox B-47 | AH-416 | Maintenance; self-leveling system; low viscosity system; excellent gloss; excellent hardness; moderate chemical resistance
Mixing ratio (Parts by weight) : 100 : 60 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : 40 – 50
Posted in PO PM Product
Lapox B-11 | AH-428 | Maintenance; self-leveling system; moderate viscosity system; excellent gloos; good chemical resistance; construction
Mixing ratio (Parts by weight) : 100 : 45 | Mix viscosity @ 25oC (mPa s) : 800 – 1,200 | Pot life @ 25oC (minutes) : 30 – 40
Posted in PO PM Product
Lapox ARB-26 | AH-416 | Maintenance; self-leveling system; low viscosity system; high gloss finish
Mixing ratio (Parts by weight) : 100 : 60 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : 40 – 50
Posted in PO PM Product
Lapox ARB-22 | AH-428 | Maintenance; self-leveling system; long pot life; excellent mechanical properties; construction
Mixing ratio (Parts by weight) : 100 : 43 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : 30 – 35
Posted in PO PM Product
Lapox ARB-22 | AH-416 | Maintenance; self-leveling system; long pot life; excellent mechanical properties; construction
Mixing ratio (Parts by weight) : 100 : 55 | Mix viscosity @ 25oC (mPa s) : 500 – 700 | Pot life @ 25oC (minutes) : 45 – 60
Posted in PO PM Product
Lapox B-47 | K-41 | K-42 | Maintenance; mortar; screed; varying pot life; excellent chemical resistance; construction
Mixing ratio (Parts by weight) : 100 : 60 | Mix viscosity @ 25oC (mPa s) : 3,000 – 6,000 | Pot life @ 25oC (minutes) : 35 – 330
Posted in PO PM Product
Lapox ARPN-54 | AH-351 | Maintenance; mortar; screed; fast reactive system; excellent chemical resistance; construction
Mix viscosity @ 25oC (mPa s) : 5,000 – 7,000 | Pot life @ 25oC (minutes) : 25 – 35
Posted in PO PM Product
Lapox B-47 | AH-714 | Maintenance; primer; low viscosity primer system; general application; construction
Mix viscosity @ 25oC (mPa s) : 600 – 1,000 | Pot life @ 25oC (minutes) : 130 – 150
Posted in PO PM Product
Lapox B-47 | AH-713 | Maintenance; primer; faster curing; construction
Mixing ratio (Parts by weight) : 100 : 50 | Mix viscosity @ 25oC (mPa s) : 3,500 – 4,500 | Pot life @ 25oC (minutes) : 110 – 130
Posted in PO PM Product
Lapox B-47 | AH-546 | Maintenance; primer; standard system for extreme condition; moist surface; construction
Mixing ratio (Parts by weight) : 100 : 50 | Mix viscosity @ 25oC (mPa s) : 3,000 – 4,500 | Pot life @ 25oC (minutes) : 60 – 80
Posted in PO PM Product
Lapox B-11 | AH-543 | Maintenance; primer; very low temperature curing; curing in high humidity; moist surface; construction
Mixing ratio (Parts by weight) : 100 : 66 | Mix viscosity @ 25oC (mPa s) : 4,500 – 5,500 | Pot life @ 25oC (minutes) : 40 – 50
Posted in PO PM Product
Lapox ARA-30 | AH-735 | structural adhesive; high lap shear strength; composite adhesive
Mixing ratio (Parts by weight) : 100 : 50 | Mix viscosity @ 25oC (mPa s) : 50,000 – 1,00,000 | Pot life @ 25oC (minutes) : 35 – 50
Posted in PO PM Product
Lapox ARA-17 | AH-354 | toughness; quick; composite adhesive
Mixing ratio (Parts by weight) : 100 : 80 | Mix viscosity @ 25oC (mPa s) : 75,000 – 1,25,000 | Pot life @ 25oC (minutes) : 8 – 10
Posted in PO PM Product
Lapox ARL-140 | AH-419 | industrial; tooling; laminating system; high Tg; high glass transition temperature; dimensional stability
Mixing ratio (Parts by weight) : 100 : 42 | Mix viscosity @ 25oC (mPa s) : 2,500 – 3,000 | Pot life @ 25oC (minutes) : 600 – 700 | Glass transition temperature (Tg) (oC) : 190 – 220
Posted in PO PM Product
Lapox ARL-138 | AH-339 | industrial; tooling; laminating system; standard tooling system; excellent Tg; excellent glass transition temperature
Mixing ratio (Parts by weight) : 100 : 30 | Mix viscosity @ 25oC (mPa s) : 400 – 600 | Pot life @ 25oC (minutes) : 120 – 180 | Glass transition temperature (Tg) (oC) : 130 – 140
Posted in PO PM Product
Lapox ART-24 | AH-326 | industrial; tooling; gel coat system; colourless gel coat system
Mixing ratio (Parts by weight) : 100 : 20 | Mix viscosity @ 25oC (mPa s) : Paste (colourless) | Pot life @ 25oC (minutes) : 15 – 20 | Glass transition temperature (Tg) (oC) : 95 – 115
Posted in PO PM Product
Lapox ART-23 | AH-326 | industrial; tooling; gel coat system; high hardness; high abrasion resistance; good finish
Mixing ratio (Parts by weight) : 100 : 10 | Mix viscosity @ 25oC (mPa s) : Paste (blue) | Pot life @ 25oC (minutes) : 15 – 20 | Glass transition temperature (Tg) (oC) : 75 – 85
Posted in PO PM Product
Lapox ART-22 | AH-326 | industrial; tooling; gel coat system; high thermal conductivity; excellent hardness; excellent surface finish
Mixing ratio (Parts by weight) : 100 : 6 | Mix viscosity @ 25oC (mPa s) : Paste (grey) | Pot life @ 25oC (minutes) : 15 – 20 | Glass transition temperature (Tg) (oC) : 85 – 95
Posted in PO PM Product
Lapox ART-21 | AH-326 | industrial; tooling; gel coat system; general purpose
Mixing ratio (Parts by weight) : 100 : 14 | Mix viscosity @ 25oC (mPa s) : Paste (white) | Pot life @ 25oC (minutes) : 25 – 30 | Glass transition temperature (Tg) (oC) : 75 – 85
Posted in PO PM Product
Lapox L-552 | K-552 | industrial; RTM; hand lay-up and infusion system; low viscosity system; high Tg; high glass transition temperature
Mixing ratio (Parts by weight) : 100 : 38 | Mix viscosity @ 25oC (mPa s) : 600 – 700 | Pot life @ 25oC (minutes) : 110 – 160 | Glass transition temperature (Tg) (oC) : 115 – 130
Posted in PO PM Product
Lapox ARTF-15 | aerospace, multifunctional resin, medium viscosity, specialty resin, MDA based
Colour (Gardner) : Max 12 | Epoxy value (Eq/kg) : 7.46 – 8.55 | Viscosity @ 50oC (mPa s) : 111,000 – 13,000
Posted in PO PM Industry
Cresol mixture | Phenol mixture
A cost effective substitute for cresylic acid and phenol.
Posted in Aromatics
TULACTV Navy CC | CAS No. Reactive Blue 250
An economical trichromatic navy dye with good dischargeability. The product is used to develop medium to dark shades.
Posted in Colors
TULACTIV Ultra Carmine CC
A deep red dye used for scarlet, dark red, brown and burgundy shades.
Posted in Colors
TULACTIV Ultra Red CC
A red dye with high tinctorial strength and excellent build-up properties. The product is used to develop medium to dark shades.
Posted in Colors
TULACTIV Ultra Yellow CC
A golden yellow dye with high tinctorial strength used to develop deep shades with good all round fastness properties.
Posted in Colors
TULACTIV Yellow CC
A basic trichromatic golden yellow dye with good dischargeability.
Posted in Colors
TULAREVS Blue LF-R
A blue dye with good light fastness properties used for pale to medium shades.
Posted in Colors
TULAREVS Red LF-2B
A red dye with good light fastness properties used for pale to medium shades.
Posted in Colors
TULAREVS Yellow LF-2R
A yellow dye with good light fastness properties used for pale to medium shades.
Posted in Colors
TULAREVS Black B Conc (133%) | CAS No. Reactive Black 5
An economical navy dye with good build-up properties.
Posted in Colors
TULACTIV Black RL | CAS No. Reactive Black 31
A black dye used to develop black to grey shades. The product has good light fastness properties.
Posted in Colors
TULACTIV Turquoise H2GP | CAS No. Reactive Blue 77
A turquoise dye with good build-up properties.
Posted in Colors
TULACTIV Turquoise G (90%) | CAS No. Reactive Blue 21 133
A turquoise dye with good build-up properties.
Posted in Colors
TULACTIV Blue R (100%) | CAS No. Reactive Blue 19
A brilliant reddish blue dye used to develop bright royal blue shades.
Posted in Colors
TULACTIV Blue BB | CAS No. Reactive Blue 220
A trichromatic blue dye with good fastness properties. The product has good dischargeability.
Posted in Colors
TULACTIV Violet 5R | CAS No. Reactive Violet 5
A bright violet dye used for various shades of violet.
Posted in Colors
TULACTIV Red BS | CAS No. Reactive Red 111
An economical bluish red dye used for medium and dark shades.
Posted in Colors
TULACTIV Red 5 B | CAS No. Reactive Red 35
An economical trichromatic red dye with high tinctorial strength.
Posted in Colors
TULACTIV Orange 3R | CAS No. Reactive Orange 16
A bright orange dye used for orange and scarlet shades.
Posted in Colors
TULACTIV Yellow RNL | CAS No. Reactive Yellow 107
An economical golden yellow dye used in trichromatic combinations.
Posted in Colors
TULACTIV Yellow R | CAS No. Reactive Orange 201
A bright yellow dye used in tertiary combinations with good light fastness properties.
Posted in Colors
TULACTIV Yellow FG | CAS No. Reactive Yellow 42
A yellow dye with all round fastness properties.
Posted in Colors
NOVATIC Grey 2305 MD
An ideal grey component with excellent performance in Exhaust and Continuous dyeing applications by Soft flow and Pad Dry Pad steam techniques. The product has good all round fastness properties. It is available in Microperle and Micro disperse varieties.
Posted in Colors
NOVATIC Navy DS MD
A navy dye with excellent build-up properties used for coloration of workwear and institutional wear. The product is used in combination with Yellow 3R and Jade Green XBN for Exhaust application. It shows minimum shade change when used with flame…
Posted in Colors
Xantho – Hexaconazole 5% EC | Xantho; Hexaconazole
A systemic fungicide with protective and curative action used to control broad spectrum fungal diseases in various field crops and fruits.
Posted in Crop Protection Brands
Rugo – 2,4-D Ethyl Ester 38% EC | 2,4-D | 2,4-D Ethyl ester | Rugo
A selective and systemic post-emergence herbicide readily absorbed by leaves. The product is used to control annual and perennial broad-leaved weeds in a range of crops.
Posted in Crop Protection Brands
para Cresol (UHP- Ultra high purity) | CAS No. 106-44-5 | 4-Methylphenol; p-Hydroxytoluene; p-Methylphenol; 4-Hydroxytoluene
A high purity grade of para Cresol for niche applications.
Posted in Aromatics
para Cresol | CAS No. 106-44-5 | 4-Methylphenol; p-Hydroxytoluene; p-Methylphenol; 4-Hydroxytoluene
A starting ingredient in most versatile phenolic group antioxidants.
Posted in Aromatics
Ambrettolide | CAS No. 28645-51-4 | 9-Hexadecenoic acid; 16-hydroxy-; o-lactone; Oxacycloheptadec-10-en-2-one
A naturally sourced aroma ingredient with a musk-like profile.
Posted in Aromatics
Skatole | CAS No. 83-34-1 | 3-Methyl-1H indole; Beta-methyl indole; 3-Methyl-4; 5-benzopyrrole
A key ingredient in specialty fragrance formulations.
Posted in Aromatics
Phenyl acetic acid | CAS No. 103-82-2 | Phenylethanoic acid; 2-Phenylacetic acid; α-Toluic acid; Benzeneacetic acid
An intermediate widely used by the Pharmaceuticals and Crop Protection Chemicals industry.
Posted in Aromatics
para Anisyl propanal | CAS No. 5462-06-6 | Hydrocinnamaldehyde p-methoxy- α –methyl 4-Methoxy-α-Methylbenzenepropanal 3-(4-methoxyphenyl)-2-methylpropanal 2-Methyl-3-(4-methoxyphenyl)propanal
An aroma ingredient with sweet, floral, fennel and basil-like, mildly fruity odour. The product finds a major application in oral care products, flavours and fragrances.
Posted in Aromatics
para Methoxy phenyl acetic acid | CAS No. 104-01-8 | 4-Methoxybenzeneacetic acid; Homoanisic acid; p-Anisylacetic acid
A key building block for Dextromethorphan, a widely used formulation to treat cough and cold.
Posted in Aromatics
Lapox B-47 | AH-714 | Maintenance, primer , low viscosity primer system, general application, construction
Mixing ratio (Parts by weight) : 100 : 50 | Mix viscosity @ 25oC (mPa s) : 600 – 1,000 | Pot life @ 25oC (minutes) : 130 – 150
Posted in PO PM Industry
Lapox B-11 | AH-543 | Maintenance, primer , very low temperature curing, curing in high humidity, moist surface, construction
Mixing ratio (Parts by weight) : 100 : 66 | Mix viscosity @ 25oC (mPa s) : 4,500 – 5,500 | Pot life @ 25oC (minutes) : 40 – 50
Posted in PO PM Industry
Lapox AH-725 | polyamide curing agent, bonding, fast reactivity
Colour (Gardner) : Max 8 | Viscosity @ 25oC (mPa s) : 7,000 – 11,000 | Amine value (mg KOH/g) : 400 – 450 | Pot life @ 25oC (minutes) : 40 – 50 | Mixing ratio (Parts by weight)…
Posted in PO PM Industry
Lapox ARC-35 AH-676 | Electrical and Electronics, Electronics, Encapsulation, Pre-filled, “Hot cure Indoor”
Type of system : Pre-filled | Nature : Hot cure / Indoor | Mixing ratio (parts by weight) : 100 : 26 | Glass transition temperature (Tg) (oC) : 70 – 80 | Thermal class : F
Posted in PO PM Industry
Lapox ARC-30 | AH-714 | Electrical and Electronics, Vacuum potting, Pre-filled, “Cold cure Indoor”
Type of system : Pre-filled | Nature : Cold cure / Indoor | Mixing ratio (Parts by weight) : 100 : 25 | Glass transition temperature (Tg) (oC) : 60 – 70 | Thermal class : B
Posted in PO PM Industry
Lapox ARL-111 | AH-358 | ARS-101
Type of system : Unfilled | Nature : Hot cure Indoor | Voltage class : MV / HV | Mixing ratio (parts by weight) : 100 : 15 | Glass transition temperature (Tg) (oC) : 80 – 90 | Thermal…
Posted in PO PM Industry
Lapox K-24 | Aromatic amine, curing agent, construction, composite, coatings
Appearance : Yellow liquid | Colour (Gardner) : Max 8 | Viscosity @ 25oC (mPa s) : 1,000 – 2,500 | Amine value (Eq/kg) : 8.00 – 9.00 | Mixing ratio (Parts by weight) : 34
Posted in None
Lapox ARC-31 | AH-114 | AC-13 | Electrical and Electronics, Dry type Distribution Transformer, Encapsulation, Unfilled, “Hot cure Indoor”
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (Parts by weight) : 100 : 100 : 0.0 – 0.2 | Glass transition temperature (Tg) (oC) : 90 – 100 | Thermal class :…
Posted in PO PM Industry
Lapox ARD-58 | aromatic – monofunctional, reactive diluent, cardanol, coating, adhesives, electrical applications
Colour (Gardner) : Max 10 | Epoxy value (Eq/kg) : 2.20 – 2.60 | Viscosity @ 25oC (mPa s) : 20 – 50 | HyCl (%) : Max 1.00
Posted in PO PM Industry
Lapox ARD-15 (K-513) | aromatic – monofunctional, reactive diluent, cardanol, coating, adhesives, electrical applications
Colour (Gardner) : Max 13 | Epoxy value (Eq/kg) : 1.80 – 2.40 | Viscosity @ 25oC (mPa s) : 40 – 70 | HyCl (%) : Max 1.00
Posted in PO PM Industry
Lapox ARD-12 (XR-59) | aromatic – monofunctional, reactive diluent, p-tertiary butyl phenol, high chemical resistance, flooring
Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 4.10 – 4.50 | Viscosity @ 25oC (mPa s) : 20 – 35 | HyCl (%) : Max 0.20
Posted in PO PM Industry
Lapox ARD-11 (K-103) | aromatic – monofunctional, reactive diluent, phenol, flooring, electrical application
Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 5.90 – 6.30 | Viscosity @ 25oC (mPa s) : 6 – 8 | HyCl (%) : Max 0.20
Posted in PO PM Industry
Lapox ARD-10 (K-100) | aromatic – monofunctional, reactive diluent, o-Cresol, high gloss, high mechanical strength, flooring, electrical application
Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 5.30 – 6.00 | Viscosity @ 25oC (mPa s) : 6 – 8 | HyCl (%) : Max 0.20
Posted in PO PM Industry
Lapox C-1 | K-1 | Electrical and Electronics, Bushings, Conventional Vacuum Casting, Unfilled, “Hot cure Indoor”
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (parts by weight) : 100 : 30 | Glass transition temperature (Tg) (oC) : 115 – 130 | Thermal class : F
Posted in PO PM Industry
Lapox C-59 | K-1 | Electrical and Electronics, Bushings, Conventional Vacuum Casting, Unfilled, Hot cure Indoor
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (Parts by weight) : 100 : 30 | Glass transition temperature (Tg) (oC) : 115 – 130 | Thermal class : F
Posted in PO PM Industry
Lapox C-2 | K-1 | Electrical and Electronics, Bushings, Conventional Vacuum Casting, Unfilled, “Hot cure Indoor”
Type of system : Unfilled | Nature : Hot cure / Indoo | Mixing ratio (parts by weight) : 100 : 30 | Glass transition temperature (Tg) (oC) : 115 – 130 | Thermal class : F
Posted in PO PM Industry
Lapox ARC-18 | AH-123 | Electrical and Electronics, Bushings, Conventional Vacuum Casting, Prefilled, “Hot cure Indoor”
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (parts by weight) : 100 : 25 | Glass transition temperature (Tg) (oC) : 122 – 132 | Thermal class : F
Posted in PO PM Industry
Lapox C-50 | K-225 | Electrical and Electronics, Bushings, Conventional Vacuum Casting, Unfilled, “Hot cure Indoor”
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio : 100 : 80 | Glass transition temperature (Tg) (oC) : 90 – 105 | Thermal class : H
Posted in PO PM Industry
Lapox C-50 | K-61 | Electrical and Electronics, Bushings, Conventional Vacuum Casting, Unfilled, “Hot cure Indoor”
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio : 100 : 80 | Glass transition temperature (Tg) (oC): 105 – 125 | Thermal class : H
Posted in PO PM Industry
Lapox C-17 | K-12 | K-13 | K-14 | Electrical and Electronics, Bushings, Conventional Vacuum Casting, Unfilled, “Hot cure Indoor”
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio : 100 : 100 : 0.5 – 1.5 : 0 – 20 | Glass transition temperature (Tg) (oC): 85 – 95 | Thermal class :…
Posted in PO PM Industry
Lapox ARCH-12 | AH-215 | Electrical and Electronics, Bushings, Conventional Vacuum Casting, Unfilled, “Hot cure Indoor”
Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio : 100 : 80 | Glass transition temperature (Tg) (oC) : 75 – 85 | Thermal class : F
Posted in PO PM Industry
Lapox ARD-65 | aliphatic – trifunctional, reactive diluent, castor oil, concrete, flooring, thermal shock resistance
Colour (Gardner) : Max 6 | Epoxy value (Eq/kg) : 1.54 – 2.00 | Viscosity @ 25oC (mPa s) : 250 – 500
Posted in PO PM Industry
Lapox ARCH-12 | AH-214 | K-13 | Electrical and Electronics, Bushings, Conventional Vacuum Casting, Unfilled, “Hot cure Indoor”
Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio : 100 : 80 : 0.5 – 2.0 | Glass transition temperature (Tg) (oC) : 75 – 85 | Thermal class : F
Posted in PO PM Industry
Lapox ARCH-11 | AH-215 | Electrical and Electronics, Bushings, Conventional Vacuum Casting, Unfilled, “Hot cure Indoor”
Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio (Parts by weight) : 100 : 90 | Glass transition temperature (Tg) (oC): 100 – 110 | Thermal class : F
Posted in PO PM Industry
Lapox ARCH-11 | AH-214 | K-13 | Electrical and Electronics, Bushings, Conventional Vacuum Casting, Unfilled, “Hot cure Indoor”
Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio : 100 : 90 : 0.5 – 2.0 | Mix viscosity : 1,000/80 | Glass transition temperature (Tg) (oC): 100 – 110 | Thermal class…
Posted in PO PM Industry
Lapox ARD-55 (XR-85) | aerospace, reactive diluent, aliphatic-trifunctional, Trimethylol propane based reactive diluent
Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 7.00 – 8.00 | Viscosity @ 25oC (mPa s) : 100 – 200 | HyCl (%) : Max 0.15
Posted in None
Lapox ARC-15 | AH-122 | Electrical and Electronics, Bushings, Conventional Vacuum Casting, Pre-filled, “Hot cure Indoor”
Type of system : Pre-filled | Nature : Hot cure Indoor | Mixing ratio (parts by weight) : 100 : 100 | Glass transition temperature (Tg) (oC) : 110 – 120 | Thermal class : H
Posted in PO PM Industry
Lapox ARD-56 (XR-87)
Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 6.90 – 8.00 | Viscosity @ 25oC (mPa s) : 12 – 18 | HyCl (%) : Max 0.15
Posted in PO PM Industry
Lapox ARD-54 (XR-19)
Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 2.90 – 3.20 | Viscosity @ 25oC (mPa s) : 40 – 90 | HyCl (%) : Max 0.15
Posted in PO PM Industry
Lapox ARD-52 (XR-86) | aliphatic – difunctional, reactive diluent, 1,6-hexane diol, aerospace
Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 6.20 – 6.80 | Viscosity @ 25oC (mPa s) : 15 – 30 | HyCl (%) : Max 0.15
Posted in PO PM Industry
Lapox ARD-51 (K-77) | aliphatic – difunctional, reactive diluent, 1,4-butane diol
Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 7.00 – 7.80 | Viscosity @ 25oC (mPa s) : 10 – 22 | HyCl (%) : Max 0.15
Posted in PO PM Industry
Lapox ARD-14 (XR-83) | aliphatic – monofunctional, reactive diluent, extreme low viscosity, construction, flooring
Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 6.20 – 7.30 | Viscosity @ 25oC (mPa s) : Max 2 | HyCl (%) : Max 0.10
Posted in PO PM Industry
Lapox ARD-13 (XR-80) | aliphatic – monofunctional, reactive diluent, excellent wetting, excellent flexibility, flooring, coating
Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 3.35 – 3.70 | Viscosity @ 25oC (mPa s) : 4 – 12 | HyCl (%) : Max 0.10
Posted in PO PM Industry
Lapox ARCH-11 (XR-34) | Cycloaliphatic resins, electrical casting, potting, UV resistance, outdoor coating
Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 5.50 – 6.30 | Viscosity @ 25oC (mPa s) : 500 – 1,100
Posted in PO PM Industry
Lapox ARFM-14 (XR-106) | Bisphenol-A/F blends, solids coating, construction, floor coating
Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 5.10 – 5.40 | Viscosity @ 25oC (mPa s) : 860 – 960
Posted in PO PM Industry
Lapox A-38 | K-99 | joints, moisture resistance, high adhesion, chemical resistant, construction adhesive
Mixing ratio (Parts by weight) : 100 : 40 | Mix viscosity @ 25oC (mPa s) : 50,000 – 1,00,000 | Pot life @ 25oC (minutes) : 20 – 25
Posted in PO PM Industry
Lapox ARPN-54 | K-41 | K-42 | Maintenance, mortar, screed, excellent chemical resistance, varying pot life, construction
Mixing ratio (Parts by weight) : 100 : 65 | Mix viscosity @ 25oC (mPa s) : 8,000 – 10,000 | Pot life @ 25oC (minutes) : 15 – 330
Posted in PO PM Industry
Lapox ARL-135 LV | Bisphenol-A based modified liquid epoxy resin, FRP , composites
Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 5.40 – 5.90 | Viscosity @ 25oC (mPa s) : 1,000 – 1,500
Posted in PO PM Industry
Lapox ARL-135 | Bisphenol-A based modified liquid epoxy resin, FRP , composites
Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 5.40 – 5.90 | Viscosity @ 25oC (mPa s) : 1,700 – 2,500
Posted in PO PM Industry
Lapox B-11 | K-48 | construction, Maintenance, repair, crack-filling, quick setting
Mixing ratio (Parts by weight) : 100 : 18 | Mix viscosity @ 25oC (mPa s) : 5,000 – 7,000 | Pot life @ 25oC (minutes) : 15 – 25
Posted in PO PM Industry
Lapox B-47 | K-48 | construction, Maintenance, grouting, quick setting, excellent adhesion, good strength
Mixing ratio (Parts by weight) : 100 : 18 | Mix viscosity @ 25oC (mPa s) : 600 – 700 | Pot life @ 25oC (minutes) : 15 – 25
Posted in PO PM Industry
Lapox B-11 | K-49 | construction, Maintenance, chemical resistant flooring, protection of metal structure, protection from corrossive chemicals, protection from alkali, protection from solvents
Mixing ratio (Parts by weight) : 100 : 60 | Mix viscosity @ 25oC (mPa s) : 3,000 – 4,000 | Pot life @ 25oC (minutes) : 100 – 110
Posted in PO PM Industry
Lapox B-11 | K-41 | K-42 | construction, Maintenance, chemical resistant flooring, variable potlife system, excellent acid and alkali resistance
Mixing ratio (Parts by weight) : 100 : 60 | Mix viscosity @ 25oC (mPa s) : 6,000 – 8,000 | Pot life @ 25oC (minutes) : 15 – 300
Posted in PO PM Industry
Lapox ARPN-54 | AH-351 | Maintenance, mortar, screed, fast reactive system, excellent chemical resistance, construction
Mixing ratio (Parts by weight) : 100 : 30 | Mix viscosity @ 25oC (mPa s) : 5,000 – 7,000 | Pot life @ 25oC (minutes) : 25 – 35
Posted in PO PM Industry
Lapox ARPN-42 | AH-105 | construction, Maintenance, chemical resistant flooring, coal tar modified system, coating of pipes, vehile chassis, concrete structure
Mixing ratio (Parts by weight) : 100 : 100 | Mix viscosity @ 25oC (mPa s) : 2,000 – 4,000 | Pot life @ 25oC (minutes) : 30 – 40
Posted in PO PM Industry
Lapox B-47 | AH-416 | Maintenance, self-leveling system, low viscosity system, excellent gloss, excellent hardness, moderate chemical resistance
Mixing ratio (Parts by weight) : 100 : 60 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : 40 – 50
Posted in PO PM Industry
Lapox B-11 | AH-428 | Maintenance, self-leveling system, moderate viscosity system, excellent gloos, good chemical resistance, construction
Mixing ratio (Parts by weight) : 100 : 45 | Mix viscosity @ 25oC (mPa s) : 800 – 1,200 | Pot life @ 25oC (minutes) : 30 – 40
Posted in PO PM Industry
Lapox ARB-26 | AH-416 | Maintenance, self-leveling system, low viscosity system, high gloss finish
Mixing ratio (Parts by weight) :100 : 60 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : 40 – 50
Posted in PO PM Industry
Lapox ARB-22 | AH-428 | Maintenance, self-leveling system, long pot life, excellent mechanical properties, construction
Mixing ratio (Parts by weight) : 100 : 43 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : 30 – 35
Posted in PO PM Industry
Lapox ARB-22 | AH-416 | Maintenance, self-leveling system, long pot life, excellent mechanical properties, construction
Mixing ratio (Parts by weight) : 100 : 55 | Mix viscosity @ 25oC (mPa s) : 500 – 700 | Pot life @ 25oC (minutes) : 45 – 60
Posted in PO PM Industry
Lapox B-47 | K-41 | K-42 | Maintenance, mortar, screed, varying pot life, excellent chemical resistance, construction
Mixing ratio (Parts by weight) : 100 : 60 | Mix viscosity @ 25oC (mPa s) : 3,000 – 6,000 | Pot life @ 25oC (minutes) : 35 – 330
Posted in PO PM Industry
Lapox B-47 | AH-713 | Maintenance, mortar, screed, standard system, system for extreme condition, screed lining, construction
Mixing ratio (Parts by weight) : 100 : 50 | Mix viscosity @ 25oC (mPa s) : 3,500 – 4,500 | Pot life @ 25oC (minutes) : 110 – 130
Posted in PO PM Industry
Lapox B-47 | AH-546 | Maintenance, mortar, screed, standard system, system for extreme condition, moist surface, construction
Mixing ratio (Parts by weight) : 100 : 50 | Mix viscosity @ 25oC (mPa s) : 3,000 – 4,500 | Pot life @ 25oC (minutes) : 60 – 80
Posted in PO PM Industry
Lapox ASH-11 | aerospace, curing agent, sulfone, 3,3′-Diaminodiphenyl sulfone, more reactive, fast curing, high productivity, powder
Chemistry : 3,3′-Diaminodiphenyl sulfone | Appearance : White to brownish white powder | Melting point (oC) : 167 – 175
Posted in None
Lapox ASH-10 MIC | aerospace, curing agent, sulfone, 4,4′-Diaminodiphenyl sulfone Micronised, micronised ASH-10, uniform dispersion in solvent-free resin, powder
Chemistry : 4,4′-Diaminodiphenyl sulfone Micronised | Appearance : White to off-white powder | Melting point (oC) : 176 – 180
Posted in None
Lapox ASH-10 FF | aerospace, curing agent, sulfone, 4,4′-Diaminodiphenyl sulfone Free Flow, Free flowin ASH-10, easy operation , easy handling, powder
Chemistry : 4,4′-Diaminodiphenyl sulfone Free Flow | Appearance : White to off-white powder | Melting point (oC) : 176 – 185
Posted in None
Lapox ASH-10 | aerospace, curing agent, sulfone, 4,4′-Diaminodiphenyl sulfone, extremely slow reactivity, prepreg, advance composite, powder
Chemistry : 4,4′-Diaminodiphenyl sulfone | Appearance : White to off-white powder | Melting point (oC) : 176 – 185
Posted in None
Lapox AH-667
Chemistry : 4,4′-Diaminodiphenyl methane | Appearance : Viscous brownish liquid | Viscosity @ 60oC (mPa s) : 1,400 – 2,000
Posted in PO PM Industry
Lapox AH-618 (K-5200)
Appearance : Light yellow to brown liquid | Viscosity @ 25oC (mPa s) : 100 – 300
Posted in PO PM Industry
Lapox AH-442
Chemistry : 4,4′-Diaminodicyclohexyl methane | Appearance : Colourless transparent liquid | Melting point (oC) : 35 – 37
Posted in PO PM Industry
Lapox AH-422
Chemistry : 3,3’-Dimethyl-4,4’-diaminodicyclohexyl methane | Viscosity @ 25oC (mPa s) : 100 – 140
Posted in PO PM Industry
Lapox ARBMI-11 | aerospace, Bismaleimide resin, excellent thermal stability
Colour (Gardner) : Yellow powder | Melting point (oC) : 155 – 158
Posted in PO PM Industry
Lapox ARBZ-11 | aerospace, benzoxazine resin, excellent moisture resistance, low shrinkage, moderate flammability
Colour (Gardner) : Yellow solid | Viscosity @ 125oC (mPa s) : 50 – 500
Posted in PO PM Industry
Lapox ARBZ-10 A 75 | aerospace, benzoxazine resin, 75% solution in acetone
Colour (Gardner) : Yellowish liquid | Solid content (%) : 74 – 76 | Viscosity @ 25oC (mPa s) : 100 – 400
Posted in PO PM Industry
Lapox ARBZ-10 | aerospace, benzoxazine resin, excellent moisture resistance, low shrinkage, moderate flammability
Colour (Gardner) : Yellow solid | Viscosity @ 100oC (mPa s) : 1,000 – 7,000 | Softening point (oC) : 60 – 80
Posted in PO PM Industry
Lapox ARTF-50
Colour (Gardner) : Max 16 | Epoxy value (Eq/kg) : 4.17 – 4.44 | Viscosity @ 85oC (mPa s) : 1,000 – 1,500
Posted in PO PM Industry
Lapox ARTF-38 | aerospace, multifunctional resin, distilled unmodified resin, m-amino phenol based, high performance
Epoxy value (Eq/kg) : 9.80 – 10.6 | Viscosity @ 25oC (mPa s) : 1,500 – 4,800
Posted in PO PM Industry
Lapox ARTF-37 | aerospace, multifunctional resin, unmodified resin, m-amino phenol based, high performance
Epoxy value (Eq/kg) : 9.10 – 9.80 | Viscosity @ 25oC (mPa s) : 7,000 – 13,000
Posted in PO PM Industry
Lapox ARTF-36 | aerospace, multifunctional resin, distilled unmodified resin, p-amino phenol based, high performance
Epoxy value (Eq/kg) : 9.40 – 10.50 | Viscosity @ 25oC (mPa s) : 550 – 850
Posted in PO PM Industry
Lapox ARTF-35 | aerospace, multifunctional resin, unmodified resin, p-amino phenol based, high performance
Epoxy value (Eq/kg) : 8.70 – 9.50 | Viscosity @ 25oC (mPa s) : 2,000 – 5,000
Posted in PO PM Industry
Lapox ARTF-34 | aerospace, multifunctional resin, specialty resin, triphenol methane based, high performance
Colour (Gardner) : Max 13 | Epoxy value (Eq/kg) : 5.88 – 6.66 | Viscosity @ 150oC (mPa s) : 30 – 55
Posted in PO PM Industry
Lapox ARTF-33 | aerospace, multifunctional resin, specialty resin, ethyl substituted MDA based, high performance
Colour (Gardner) : Max 7 | Epoxy value (Eq/kg) : 7.52 – 8.47 | Viscosity @ 25oC (mPa s) : 7,000 – 12,000
Posted in PO PM Industry
Lapox ARTF-23
Colour (Gardner) : Max 12 | Epoxy value (Eq/kg) : 8.55 – 9.00 | Viscosity @ 50oC (mPa s) : 3,000 – 6,000
Posted in PO PM Industry
Lapox ARTF-18 | aerospace, multifunctional resin, high viscosity, specialty resin, MDA based, high performance
Colour (Gardner) : Max 12 | Epoxy value (Eq/kg) : 7.46 – 8.55 | Viscosity @ 50oC (mPa s) : 7,000-19,000
Posted in PO PM Industry
Lapox ARTF-17 | aerospace, multifunctional resin, medium viscosity, specialty resin, MDA based, high performance
Colour (Gardner) : Max 12 | Epoxy value (Eq/kg) : 7.46 – 8.55 | Viscosity @ 50oC (mPa s) : 17,000-19,000
Posted in PO PM Industry
Lapox ARTF-16 | aerospace, multifunctional resin, medium viscosity, specialty resin, MDA based, high performance
Colour (Gardner) : Max 12 | Epoxy value (Eq/kg) : 7.46 – 8.55 | Viscosity @ 50oC (mPa s) : 13,000-15,000
Posted in PO PM Industry
Lapox ARTF-14 | aerospace, multifunctional resin, medium viscosity, specialty resin, MDA based, high performance
Colour (Gardner) : Max 12 | Epoxy value (Eq/kg) : 7.46 – 8.55 | Viscosity @ 50oC (mPa s) : 10,000 – 12,000
Posted in PO PM Industry
Lapox ARTF-13 | aerospace, multifunctional resin, medium viscosity, specialty resin, MDA based, high performance
Colour (Gardner) : Max 12 | Epoxy value (Eq/kg) : 7.46 – 8.55 | Viscosity @ 50oC (mPa s) : 7,000 – 11,000
Posted in PO PM Industry
Lapox ARPN-56 | aerospace, Epoxy Phenol Novolac resin, solid resin, functionality of 5.6
Colour (Gardner) : Max 4 | Epoxy value (Eq/kg) : 5.12 – 6.10 | Viscosity @ 50oC (mPa s) : 100 – 350
Posted in None
Lapox ARPN-25 | aerospace, Epoxy Phenol Novolac resin, low viscosity, average functionality, functionality of 2.5
Colour (Gardner) : Max 3 | Epoxy value (Eq/kg) : 5.59 – 5.81 | Viscosity @ 52oC (mPa s) : 1,100 – 1,700
Posted in PO PM Industry
Lapox ARN-16 | aerospace, bifunctional resin, Bisphenol-F based epoxy resin, medium viscosity
Colour (Gardner) : Max 16 | Epoxy value (Eq/kg) : 6.50 – 7.50 | Viscosity @ 50oC (mPa s) : 1,000 – 2,500 | Hycl : Max 0.20
Posted in PO PM Industry
Lapox ARL-15 | aerospace, bifunctional resin, Bisphenol-F based epoxy resin, low viscosity
Colour (APHA) : Max 50 | Epoxy value (Eq/kg) : 5.71 – 5.95 | Viscosity @ 25oC (mPa s) : 4,000 – 5,000
Posted in PO PM Industry
Lapox ARL-12 | aerospace, bifunctional resin, Bisphenol-F based epoxy resin
Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 5.26 – 5.55 | Viscosity @ 25oC (mPa s) : 9,000 – 12,000
Posted in PO PM Industry
Lapox P-5 (ARP-17) | Bisphenol-A based solid resins, type 7, stoving lacquers, can coating, tube coating
Epoxy value (Eq/kg) : 0.53 – 0.59 | Viscosity @ 25oC (mPa s) : 1,800 – 2,600 | Softening point (oC) : 110 – 120
Posted in PO PM Industry
Lapox K-541 (AH-541) | phenalkamine curing agent, high viscosity, marine coating, industrial coatings, protective coatings
Colour (Gardner) : Max 15 | Viscosity @ 25oC (mPa s) : 15,000 – 35,000 | Amine value (mg KOH/g) : 290 – 325 | Pot life @ 25oC (minutes) : 40 – 85 | Mixing ratio (Parts by weight)…
Posted in None
Lapox K-540 (AH-540) | phenalkamine curing agent, low viscosity, marine coatng, industrial coating, maintenance coating, protective coatings
Colour (Gardner) : Max 15 | Viscosity @ 25oC (mPa s) : 2,000 – 4,000 | Amine value (mg KOH/g) : 490 – 550 | Pot life @ 25oC (minutes) : 30 – 55 | Mixing ratio (Parts by weight)…
Posted in None
Lapox AH-543 (XH-80) | phenalkamine curing agent, low colour, low viscosity, heavy duty anti-corrosive coatings , marine applications, protective coatings
Colour (Gardner) : Max 15 | Viscosity @ 25oC (mPa s) : 2,000 – 5,000 | Amine value (mg KOH/g) : 300 – 350 | Pot life @ 25oC (minutes) : 50 – 65 | Mixing ratio (Parts by weight)…
Posted in PO PM Industry
Lapox AH-420 (K-964) | cycloaliphatic amine curing agent, very low viscosity, moderate pot life, flooring, better chemical resistance, protective coatings
Colour (Gardner) : Max 3 | Viscosity @ 25oC (mPa s) : 40 – 60 | Amine value (mg KOH/g) : 320 – 340 | Pot life @ 25oC (minutes) : 25 – 40 | Mixing ratio (Parts by weight)…
Posted in PO PM Industry
Lapox AH-411 | unmodified cycloaliphatic amine curing agent, coatings, flooring applications, composite applications, protective coatings
Colour (Gardner) : Max 1 | Viscosity @ 25oC (mPa s) : 10 – 20 | Pot life @ 25oC (minutes) : 90 – 120 | Mixing ratio (Parts by weight) : 23
Posted in PO PM Industry
Lapox XH-61 (AH-321) | modified polyamine adduct solution, solution in xylene and butanol, clear coating, protective coating
Colour : Max 2 | Viscosity @ 25oC (mPa s) : 1,500 – 2,000 | Amine value (Eq/kg) : 165 – 210 | Pot life @ 25oC (hours) : 4 – 6 | Mixing ratio (Parts by weight) : 30…
Posted in PO PM Industry
Lapox K-306 | Butylated melamine formaldehyde curing agent, enamel, polyester film coating, protective coating
Colour (Gardner) : Clear liquid | Viscosity @ 25oC (mPa s) : 850 – 1,200 | Mixing ratio (Parts by weight) : 100 (with resin ARL-148)
Posted in PO PM Industry
Lapox K-105 | coal tar modified polyamine adduct, high build coatings, protective coating
Colour (Gardner) : Black | Viscosity @ 25oC (mPa s) : 3,000 – 6,000 | Pot life @ 25oC (minutes) : Min 20 | Mixing ratio (Parts by weight) : 100 (with resin ARB – 28)
Posted in PO PM Industry
Lapox K-54 (AH-356) | modified polyamine adduct, slids coating, mortar, adhesives, protective coating
Colour (Gardner) : Max 2 | Viscosity @ 25oC (mPa s) : 2,900 – 3,600 | Amine value (mg KOH/g) : 398 – 415 | Pot life @ 25oC (minutes) : 15 – 30 | Mixing ratio (Parts by weight)…
Posted in PO PM Industry
Lapox K-48 (AH-319) | modified polyamine curing agent, low vapour pressurehigh reactivity, adhesives, composites, castings, coatings, protective coating
Colour (Gardner) : Max 4 | Viscosity @ 25oC (mPa s) : 200 – 300 | Amine value (Eq/kg) : 17.00 – 17.80 | Pot life @ 25oC (minutes) : 25 – 35 | Mixing ratio (Parts by weight) :…
Posted in PO PM Industry
Lapox K-7 | unmodified aliphatic polyamine curing agent, adhesives, castings, coatings, composites, protective coating
Colour (Gardner) : Max 5 | Viscosity @ 25oC (mPa s) : Max 10 | Pot life @ 25oC (minutes) : 20 – 25 | Mixing ratio (Parts by weight) : 10 – 12
Posted in PO PM Industry
Lapox K-6 | unmodified aliphatic polyamine curing agent, casting, coatings, composites, protective coating
Colour (Gardner) : Max 3 | Pot life @ 25oC (minutes) : 30 – 40 | Mixing ratio (Parts by weight) : 10 – 12
Posted in PO PM Industry
Lapox AH-371 to AH-373 | modified polyamine curing agent, crack-filling, stone coating, mortar, adhesive, protective coating
Colour (Gardner) : Max 5 | Viscosity @ 25oC (mPa s) : 100 – 550 | Amine value (mg KOH/g) : 500 – 1,000 | Pot life @ 25oC (minutes) : 5 – 30 | Mixing ratio (Parts by weight)…
Posted in PO PM Industry
Lapox AH-351 | modified polyamine curing agent, chemical resistance, sulphuric acid resistance, protective coating
Colour (Gardner) : Max 4 | Viscosity @ 25oC (mPa s) : 500 – 1,000 | Amine value (mg KOH/g) : 650 – 750 | Pot life @ 25oC (minutes) : 30 – 40 | Mixing ratio (Parts by weight)…
Posted in PO PM Industry
Lapox AH-348 | unmodified aliphatic polyamine curing ag nr, flexible casting, transparent casting, coatings, protective coating
Colour (Gardner) : Max 1 | Viscosity @ 25oC (mPa s) : 5 – 10 | Amine value (mg KOH/g) : 680 – 720 | Pot life @ 25oC (minutes) : 40 – 50 | Mixing ratio (Parts by weight)…
Posted in PO PM Industry
Lapox AH-341 | modified aliphatic polyamine curing agent, solids coating, long pot life, protective coating
Colour (Gardner) : Max 2 | Viscosity @ 25oC (mPa s) : 30 – 100 | Amine value (mg KOH/g) : 290 – 320 | Pot life @ 25oC (minutes) : 100 – 125 | Mixing ratio (Parts by weight)…
Posted in PO PM Industry
Lapox AH-313 | unmodified aliphatic polyamine curing agent, adhesives, casting, coating, composite applications, protective coating
Colour (Gardner) : Max 4 | Viscosity @ 25oC (mPa s) : 50 – 60 | Pot life @ 25oC (minutes) : 35 – 50 | Mixing ratio (Parts by weight) : 15
Posted in PO PM Industry
Lapox K-92 | Aromatic amine, ambient cure modified curing agent, chemical resistant coating, tank lining, flooring, protective coating
Appearance : Brown liquid | Colour (Gardner) : Max 13 | Viscosity @ 25oC (mPa s) : 5,000 – 7,500 | Amine value (Eq/kg) : 4.40 – 5.10 | Mixing ratio (Parts by weight) : 60
Posted in PO PM Industry
Lapox ARL-143 | AH-335 | industrial, RTM, hand lay-up and infusion systems, moderate viscosity system, varying pot life, fire retardannt application
Mixing ratio (Parts by weight) : 100 : 15 | Mix viscosity @ 25oC (mPa s) : 3,500 – 5,000 | Pot life @ 25oC (minutes) : 85 – 95 | Glass transition temperature (Tg) (oC) : 95 – 105
Posted in PO PM Industry
Lapox ARL-143 | AH-319 | industrial, RTM, hand lay-up and infusion systems, moderate viscosity system, varying pot life, fire retardannt application
Mixing ratio (Parts by weight) : 100 : 15 | Mix viscosity @ 25oC (mPa s) : 3,500 – 5,000 | Pot life @ 25oC (minutes) : 20 – 25 | Glass transition temperature (Tg) (oC) : 95 – 105
Posted in PO PM Industry
Lapox ARCH-13 | Cycloaliphatic resins, higher toughness, outdoor coating, electrical casting, flooring, protective coating
Colour (APHA) : Max 100 | Epoxy value (Eq/kg) : 4.16 – 4.54 | Viscosity @ 25oC (mPa s) : 2,000 – 4,000
Posted in PO PM Industry
Lapox ARF-15 | Bisphenol-F based resin, very low viscosity, distilled version, protective coating
Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 6.00 – 6.40 | Viscosity @ 25oC (mPa s) : 1,200 – 1,600
Posted in PO PM Industry
Lapox ARF-14 | Bisphenol-F based resin, high viscosity, constructon, composites, electrical, casting, protective coating
Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 5.80 – 6.30 | Viscosity @ 25oC (mPa s) : 5,000 – 7,000
Posted in None
Lapox ARF-13 | Bisphenol-F based resin, medium viscosity, constructon, composites, electrical, casting, protective coating
Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 5.80 – 6.10 | Viscosity @ 25oC (mPa s) : 3,300 – 4,100
Posted in None
Lapox ARF-12 | Bisphenol-F based resin, low viscosity, constructon, composites, electrical, casting, protective coating
Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 5.80 – 6.10 | Viscosity @ 25oC (mPa s) : 2,000 – 3,000
Posted in None
Lapox ARF-11 (XR-40) | standard Bisphenol-F based resin, constructon, composites, electrical, casting, protective coating
Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 5.70 – 6.30 | Viscosity @ 25oC (mPa s) : 2,000 – 5,000
Posted in PO PM Industry
Lapox P-122 (ARP-14 A) | Bisphenol-A based solid resins, functional powder coating, rebar coating, protective coating
Epoxy value (Eq/kg) : 1.07 – 1.16 | Viscosity @ 25oC (mPa s) : 620 – 900 | Softening point (oC) : 100 – 110
Posted in None
Lapox P-62 (ARP-13) | Bisphenol-A based solid resins, standard solid resin, powder coating, protective coating
Epoxy value (Eq/kg) : 1.25 – 1.40 | Viscosity @ 25oC (mPa s) : 500 – 700 | Softening point (oC) : 95 – 101
Posted in PO PM Product
Lapox ARPN-36 | K-86 | industrial, prepregs and laminating systems, compressed laminate system, B-stage prepreg
Mixing ratio (Parts by weight) : 100 : 3-6 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (Tg) (oC) : 165 – 180
Posted in PO PM Industry
Lapox ARPN-36 | K-10 | K-86 | automotive, prepregs and laminating systems, compressed laminate, B-stage prepreg, very high Tg, very high glass transition temperature
Mixing ratio (Parts by weight) : 100 : 32-40 : 1-3 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (Tg) (oC) : 170 – 185
Posted in PO PM Industry
Lapox L-247 | K-918 | K-13 | industrial, filament winding and pultrusion, hot cure system, general purpose system, fire retardant
Mixing ratio (Parts by weight) : 100 : 64 : 1-3 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 110 – 120
Posted in PO PM Industry
Lapox L-12 | K-24 | industrial, filament winding and pultrusion, hot cure system, low viscosity system, long pot life, high chemical resistance, high abrasion resistance
Mixing ratio (Parts by weight) : 100 : 34 | Mix viscosity @ 25oC (mPa s) : 3,500 – 5,000 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) oC : 145 – 155
Posted in PO PM Industry
Lapox L-12 | K-12 K-13 | industrial, filament winding and pultrusion, hot cure system, standard system, fast reactivity
Mixing ratio (Parts by weight) : 100 : 100 : 1-3 | Mix viscosity @ 25oC (mPa s) : 400 – 700 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 95 –…
Posted in PO PM Industry
Lapox L-12 | AH-667 | industrial, filament winding and pultrusion, hot cure system, high chemical resistance, high abrasion resistance
Mixing ratio (Parts by weight) : 100 : 27 | Mix viscosity @ 50oC (mPa s) : 3,000 – 5,000 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 150 – 160
Posted in PO PM Industry
Lapox L-12 | AH-113 | K-13 | industrial, filament winding and pultrusion, hot cure system, flame retardancy
Mixing ratio (Parts by weight) : 100 : 95 : 0.5-2.0 | Mix viscosity @ 25oC (mPa s) : 1,900 – 2,100 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 165 –…
Posted in PO PM Industry
Lapox ARL-136 | AH-126 | industrial, filament winding and pultrusion, hot cure system, superior fiber wetting, excellent mechanical properties, good surface finish
Mixing ratio (Parts by weight) : 100 : 90 | Mix viscosity @ 25oC (mPa s) : 300 – 600 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 115 – 125
Posted in PO PM Industry
Lapox ARF-11 | K-918 | K-13 | industrial, filament winding and pultrusion, hot cure system, non-crystallisable, excellent chemical resistance
Mixing ratio (Parts by weight) : 100 : 90 : 1-3 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 115 –…
Posted in PO PM Industry
Lapox ARCH-11 | K-3 | K-13 | industrial, filament winding and pultrusion, hot cure system, out door application, UV resistance
Mixing ratio (Parts by weight) : 100 : 85 : 1-3 | Mix viscosity @ 25oC (mPa s) : 200 – 500 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 105 –…
Posted in PO PM Industry
Lapox L-12 | AH-337 | industrial, filament winding and pultrusion, ambient cure system, high Tg, high glass transition temperature, variable pot life
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 400 – 700 | Pot life @ 25oC (minutes) : 300 – 380 | Glass transition temperature (Tg) oC : 90 – 105
Posted in PO PM Industry
Lapox L-12 | AH-336 | industrial, filament winding and pultrusion, ambient cure system, high Tg, high glass transition temperature, variable pot life
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 600 – 1,200 | Pot life @ 25oC (minutes) : 80 – 100 | Glass transition temperature (Tg) oC : 90 – 105
Posted in PO PM Industry
Lapox L-12 | AH-335 | industrial, filament winding and pultrusion, ambient cure system
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 600 – 1,200 | Pot life @ 25oC (minutes) : 50 – 60 | Glass transition temperature (Tg) oC : 90 – 105
Posted in PO PM Industry
Lapox L-12 | AH-315 | industrial, filament winding and pultrusion, ambient cure system
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 500 – 800 | Pot life @ 25oC (minutes) : 7 – 9 hr | Glass transition temperature (Tg) oC : 85 –…
Posted in PO PM Industry
Lapox ARL-12 | AH-714 | industrial, filament winding and pultrusion, ambient cure system, superior adhesion, toughness
Mixing ratio (Parts by weight) : 100 : 50 | Mix viscosity @ 25oC (mPa s) : 1,200 – 1,500 | Pot life @ 25oC (minutes) : 120 – 150 | Glass transition temperature (Tg) oC : 55 – 65
Posted in PO PM Industry
Lapox ARL-125 | AH-332 | aerospace, RTM, hand lay-up, infusion, long pot life, high Tg, high glass transition temperature
Mixing ratio (Parts by weight) : 100:32 | Mix viscosity @ 25oC (mPa s) : 600 – 800 | Pot life @ 25oC (minutes) : 8 – 14 | Glass transition temperature (Tg) (oC) : 80 – 90
Posted in PO PM Industry
Lapox ART-24 | AH-326 | automotive, tooling, gel coat system
Mixing ratio (Parts by weight) : 100 : 20 | Mix viscosity @ 25oC (mPa s) : Paste (colourless) | Pot life @ 25oC (minutes) : 15 – 20 | Glass transition temperature (Tg) (oC) : 95 – 115
Posted in PO PM Industry
Lapox ART-23 | AH-326 | automotive, tooling, gel coat system
Mixing ratio (Parts by weight) : 100 : 10 | Mix viscosity @ 25oC (mPa s) : Paste (blue) | Pot life @ 25oC (minutes) : 15 – 20 | Glass transition temperature (Tg) (oC) : 75 – 85
Posted in PO PM Industry
Lapox ART-21 | AH-326 | automotive, tooling, gel coat system
Mixing ratio (Parts by weight) : 100 : 14 | Mix viscosity @ 25oC (mPa s) : Paste (white) | Pot life @ 25oC (minutes) : 25 – 30 | Glass transition temperature (Tg) (oC) : 75 – 85
Posted in PO PM Industry
Lapox ARL-135 LV | AH-411 | automotive, RTM, hand lay-up and infusion systems, very low viscosity, high Tg, high glass trransition temperature
Mixing ratio (Parts by weight) : 100 : 24 | Mix viscosity @ 25oC (mPa s) : 250 – 400 | Pot life @ 25oC (minutes) : 90 – 120 | Glass transition temperature (Tg) (oC) : 125 – 135
Posted in PO PM Industry
Lapox ARL-135 LV | AH-333 | automotive, RTM, hand lay-up and infusion systems, low viscosity system, variable pot life
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 600 – 750 | Pot life @ 25oC (minutes) : 14 – 20 | Glass transition temperature (Tg) (oC) : 75 – 85
Posted in PO PM Industry
Lapox B-7 | semi-solid, can coating, coil coating, protective coating
Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 3.57 – 4.45 | Viscosity @ 25oC (mPa s) : 450 – 800
Posted in None
Lapox ARL-135 LV | AH-332 | automotive, RTM, hand lay-up and infusion systems, low viscosity system, variable pot life
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 600 – 800 | Pot life @ 25oC (minutes) : 8 – 14 | Glass transition temperature (Tg) (oC) : 75 – 85
Posted in PO PM Industry
Lapox P-10 (ARP-14 E) | Bisphenol-A based solid resins, esterifcation, anodic electrodeposition
Epoxy value (Eq/kg) : 1.08 – 1.18 | Viscosity @ 25oC (mPa s) : 430 – 550 | Softening point (oC) : 90 – 100
Posted in PO PM Industry
Lapox ARP-14 HF | Bisphenol-A based solid resins, modified resin, powder coating, better flow
Epoxy value (Eq/kg) : 1.23 – 1.33 | Viscosity @ 25oC (mPa s) : 480 – 580 | Softening point (oC) : 80 – 90
Posted in None
Lapox ARP-13 LV | Bisphenol-A based solid resins, hybrid powder coating
Epoxy value (Eq/kg) : 1.33 – 1.40 | Viscosity @ 25oC (mPa s) : 500 – 600 | Softening point (oC) : 95 – 101
Posted in None
Lapox ARL-160 | AH-359 | automotive, prepreg system, FRP structural component
Mixing ratio (Parts by weight) : 100 : 5 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (Tg) (oC) : 110 – 120
Posted in PO PM Industry
Lapox ARL-159 | AH-357 | AC-22 | automotive, prepreg system, hot melt prepreg system, very high Tg, very high glass transition temperature,
Mixing ratio (Parts by weight) : 100 : 15 : 2 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (Tg) (oC) : 155 – 165
Posted in PO PM Industry
Lapox L-68 | K-66 | K-13 | automotive, prepregs and laminating systems, compressed laminate, B-stage prepreg, FR-4 laminate
Mixing ratio (Parts by weight) : 100 : 32 : 1-3 | Pot life @ 25oC (weeks) : 2 – 3 | Glass transition temperature (Tg) (oC) : 130 – 140
Posted in PO PM Industry
Lapox L-67 | K-66 | K-13 | automotive, prepregs and laminating systems, compressed laminate, B-stage prepreg, G-10 laminate
Mixing ratio (Parts by weight) : 100 : 23 : 0.5-3.0 | Pot life @ 25oC (weeks) : 2 – 3 | Glass transition temperature (Tg) (oC) : 130 – 140
Posted in PO PM Industry
Lapox ARP-13 HT | Bisphenol-A based solid resins, powder coating
Epoxy value (Eq/kg) : 1.25 – 1.35 | Viscosity @ 150oC (mPa s) : 4,500 – 6,500 | Glass transition temperature (Tg) (oC) : 55
Posted in None
Lapox L-12 | K-10 | K-86 | automotive, prepregs and laminating systems, compressed laminate, B-stage prepreg, shelf life upto 6 month, G-11 laminate
Mixing ratio (Parts by weight) : 100 : 35 : 1-3 | Pot life @ 25oC (weeks) : 6 – 8 weeks | Glass transition temperature (Tg) (oC) : 150 – 160
Posted in PO PM Industry
Lapox ARP-12 | Bisphenol-A based solid resins, medium molecular weight, powder coating
Epoxy value (Eq/kg) : 1.42 – 1.53 | Viscosity @ 25oC (mPa s) : 375 – 475 | Softening point (oC) : 80 – 90
Posted in PO PM Industry
Lapox AC-14 (K-65) | accelerator and catalysts, liquid tertiary amine, accelerate anhydrides, accelerate polyamides, accelerate amines
Appearance : Clear yellow liquid | Colour (Gardner) : Max 6 | Viscosity @ 25oC (mPa s) : 150 – 300 | Amine value (mg KOH/g) : 580 – 635
Posted in PO PM Industry
Lapox L-12 | K-5 | automotive, prepregs and laminating systems, compressed laminate, prepreg, shorter shelf life, G-10 laminate, G-11 laminate
Mixing ratio (Parts by weight) : 100 : 27 | Pot life @ 25oC (hours) : > 4 | Glass transition temperature (Tg) (oC) : 150 – 160
Posted in PO PM Industry
Lapox K-302 | modified polyamine, curing agent, self-leveling flooring, solvent-free coating, clear casting
Colour (Gardner) : Max 2 | Viscosity @ 25oC (mPa s) : 300 – 600 | Amine value (mg KOH/g) : 260 – 310 | Pot life @ 25oC (minutes) : 40 – 50 | Mixing ratio (Parts by weight)…
Posted in PO PM Industry
Lapox AH-440 | Cycloaliphatic amine, curing agent, accelerated curing agent, solvent-free coating, flooring
Colour (Gardner) : Max 2 | Viscosity @ 25oC (mPa s) : 150 – 300 | Amine value (mg KOH/g) : 335 – 375 | Pot life @ 25oC (minutes) : 25 – 40 | Mixing ratio (Parts by weight)…
Posted in PO PM Industry
Lapox AH-428 | Cycloaliphatic amine, curing agent, low viscosity, fast reactivity, self-leveling, high gloss, colour stability
Colour (Gardner) : Max 1 | Viscosity @ 25oC (mPa s) : 50 – 150 | Amine value (mg KOH/g) : 340 – 390 | Pot life @ 25oC (minutes) : 30 – 40 | Mixing ratio (Parts by weight)…
Posted in PO PM Industry
Lapox L-12 | K-918 | K-13 | automotive, filament winding and pultrusion system, hot cure
Mixing ratio (Parts by weight) : 100 : 85 : 1-3 | Mix viscosity @ 25oC (mPa s) : 600 – 900 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 130 –…
Posted in PO PM Industry
Lapox AH-424 | Cycloaliphatic amine, curing agent, self-leveling flooring, high filler loading
Colour (Gardner) : Max 2 | Amine value (mg KOH/g) : 330 – 360 | Pot life @ 25oC (minutes) : 20 – 50 | Mixing ratio (Parts by weight) : 45
Posted in PO PM Industry
Lapox L-12 | AH-422 | automotive, filament winding and pultrusion system, long pot life, high glass transition temperature, high Tg, ambient cure
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 1,500 – 2,500 | Pot life @ 25oC (minutes) : 300 – 350 | Glass transition temperature (Tg) (oC) : 130 – 140
Posted in PO PM Industry
Lapox AH-416 | Cycloaliphatic amine, curing agent, moderate viscosity, transparent, high gloss, self-leveling flooring
Colour (Gardner) : Max 1 | Viscosity @ 25oC (mPa s) : 400 – 600 | Amine value (mg KOH/g) : 250 – 300 | Pot life @ 25oC (minutes) : 30 – 45 | Mixing ratio (Parts by weight)…
Posted in PO PM Industry
Lapox AH-727 | curing agent, Polyamide, curing under wet/damp, excellent adhesion, adhesion with metal, adhesion with concrete, primer, coatings
Colour (Gardner) : Max 12 | Viscosity @ 25oC (mPa s) : 1,000 – 2,000 | Amine value (mg KOH/g) : 280 – 300 | Pot life @ 25oC (minutes) : 46 – 65 | Mixing ratio (Parts by weight)…
Posted in PO PM Industry
Lapox AH-716 (K-29) | curing agent, Polyamide, low viscosity, solids coating, primer, floor coating
Colour (Gardner) : Max 10 | Viscosity @ 25oC (mPa s) : 2,500 – 5,500 | Amine value (mg KOH/g) : 202 – 225 | Pot life @ 25oC (minutes) : 80 – 100 | Mixing ratio (Parts by weight)…
Posted in PO PM Industry
Lapox ARL-135 LV | AH-337 | automotive, filament winding and pultrusion system, low viscosity, variable pot life, ambient cure
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 200 – 300 | Pot life @ 25oC (minutes) : 300 – 380 | Glass transition temperature (Tg) (oC) : 75 – 85
Posted in PO PM Industry
Lapox AH-714 | curing agent, Polyamide, low viscosity, grout, crack injection, primer, protective coating, tile gap filling, adhesive, mortar
Colour (Gardner) : Max 8 | Viscosity @ 25oC (mPa s) : 500 – 1,000 | Amine value (mg KOH/g) : 425 – 450 | Pot life @ 25oC (minutes) : 120 – 130 | Mixing ratio (Parts by weight)…
Posted in PO PM Industry
Lapox ARL-135 LV | AH-336 | automotive, filament winding and pultrusion system, variable pot life, ambient cure
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 300 – 700 | Pot life @ 25oC (minutes) : 80 – 100 | Glass transition temperature (Tg) (oC) : 75 – 85
Posted in PO PM Industry
Lapox AH-713 (K-46) | curing agent, Polyamide, moderate viscosity, solids coating, primer, grout, mortar, adhesive, marine coating, industrial paints
Colour (Gardner) : Max 9 | Viscosity @ 25oC (mPa s) : 12,000 – 18,000 | Amine value (mg KOH/g) : 350 – 400 | Pot life @ 25oC (minutes) : 60 – 80 | Mixing ratio (Parts by weight)…
Posted in PO PM Industry
Lapox ARL-135 LV | AH-335 | automotive, filament winding and pultrusion system, variable pot life, ambient cure
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 300 – 700 | Pot life @ 25oC (minutes) : 50 – 60 | Glass transition temperature (Tg) (oC) : 75 – 85
Posted in PO PM Industry
Lapox AH-712 | curing agent, Polyamide, high viscosity, protective coating, adhesive, flooring, marine coating, industrial paint
Colour (Gardner) : Max 9 | Viscosity @ 25oC (mPa s) : 45,000 – 60,000 | Amine value (mg KOH/g) : 290 – 320 | Pot life @ 25oC (minutes) : 110 – 130 | Mixing ratio (Parts by weight)…
Posted in PO PM Industry
Lapox ART-22 | AH-326
Mixing ratio (Parts by weight) : 100 : 6 | Mix viscosity @ 25oC (mPa s) : Paste (grey) | Pot life @ 25oC (minutes) : 15 – 20 | Glass transition temperature (Tg) (oC) : 85 – 95
Posted in PO PM Industry
Lapox ARL-140 | AH-419
Mixing ratio (Parts by weight) : 100 : 42 | Mix viscosity @ 25oC (mPa s) : 2,500 – 3,000 | Pot life @ 25oC (minutes) : 600 – 700 | Glass transition temperature (Tg) (oC) : 190 – 220
Posted in PO PM Industry
Lapox ARL-138 | AH-417 | aerospace, tooling, laminating system, low viscosity system, high Tg, high glass transition temperature
Mixing ratio (Parts by weight) : 100 : 30 | Mix viscosity @ 25oC (mPa s) : 200 – 300 | Pot life @ 25oC (minutes) : 90 – 120 | Glass transition temperature (Tg) (oC) : 100 – 110
Posted in PO PM Industry
Lapox AH-711 | curing agent, Polyamide, high viscosity, adhesive, sealant
Colour (Gardner) : Max 9 | Viscosity @ 40oC (mPa s) : 50,000 – 75,000 | Amine value (mg KOH/g) : 210 – 230 | Mixing ratio (Parts by weight) : 100 – 125
Posted in PO PM Industry
Lapox K-49 | Aromatic amine, low viscosity, moderate reactivity, solvent-free coating, chemical resistant coating, floorings, linings
Appearance : Brown liquid | Colour (Gardner) : Max 13 | Viscosity @ 25oC (mPa s) : 700 – 900 | Amine value (Eq/kg) : 4.70 – 5.00 | Mixing ratio (Parts by weight) : 60
Posted in PO PM Industry
Lapox ARL-138 | AH-339 | aerospace, laminating system, high Tg, high glass transition temperature, dimensional stability at high temperature
Mixing ratio (Parts by weight) : 100 : 30 | Mix viscosity @ 25oC (mPa s) : 400 – 600 | Pot life @ 25oC (minutes) : 120 – 180 | Glass transition temperature (Tg) (oC) : 130 – 140
Posted in PO PM Industry
Lapox K-42 | Aromatic amine, curing agent, low viscosity, high reactive
Appearance : Dark brown liquid | Colour (Gardner) : Max 16 | Viscosity @ 25oC (mPa s) : 15,000 – 21,000 | Amine value (Eq/kg) : 4.40 – 4.80 | Mixing ratio (Parts by weight) : 60
Posted in PO PM Industry
Lapox K-41 | Aromatic amine, curing agent, low viscosity, chemical resistant, industrial flooring, coatings, tank linings
Appearance : Brown liquid | Colour (Gardner) : Max 13 | Viscosity @ 25oC (mPa s) : 3,800 – 5,800 | Amine value (Eq/kg) : 4.70 – 5.10 | Mixing ratio (Parts by weight) : 60
Posted in PO PM Industry
Lapox XR-128 | Solvent cut resins, high molecular weight, primer, enamel, flexibility
Epoxy value (Eq/kg) : Max 0.08 | Viscosity @ 25oC (mPa s) : 2,000 – 5,000 | Non-volatile content (%) : 49 – 51 (160oC/2h)
Posted in PO PM Industry
Lapox P-101 HV | Solvent cut resins, type 1 solution, paint and coatings
Epoxy value (Eq/kg) : 1.80 – 2.20 | Viscosity @ 25oC (mPa s) : 14,000 – 20,000 | Non-volatile content (%) : 74 – 76 (150oC/2h)
Posted in PO PM Industry
Lapox P-101 | Solvent cut resins, type 1 solution, paint and coatings
Epoxy value (Eq/kg) : 1.90 – 2.20 | Viscosity @ 25oC (mPa s) : 9,000 – 13,000 | Non-volatile content (%) : 74 – 76 (150oC/2h)
Posted in PO PM Industry
Lapox B-7 X 80 | Solvent cut resins, solids coating, excellent adhesion, gloss, flexibility
Epoxy value (Eq/kg) : 3.10 – 3.40 | Viscosity @ 25oC (mPa s) : 600 – 850 | Non-volatile content (%) : 79 – 81 (150oC/1h)
Posted in PO PM Industry
Lapox ARPN-54 | modified epoxy phenol novolac resins, composite applications, electrical applications, coating applications, industrial coating
Colour (Gardner) : Max 3 | Epoxy value (Eq/kg) : 5.50 – 6.00 | Viscosity @ 25oC (mPa s) : 25,000 – 35,000
Posted in PO PM Industry
Lapox ARPN-36 X 80 | Epoxy phenol novolac resins, epoxy phenol novolac solution, chemical resistant coating, electrical applications, composite applications, industrial coating
Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 4.40 – 4.60 | Viscosity @ 25oC (mPa s) : 800 – 1,500 | Non-volatile content (%) :79 – 81 (150oC/1h)
Posted in PO PM Industry
Lapox ARPN-36 M 80 | Epoxy phenol novolac resins, epoxy phenol novolac solution, chemical resistant coating, electrical applications, composite applications, industrial coating
Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 4.40 – 4.60 | Viscosity @ 25oC (mPa s) : 150 – 350 | Non-volatile content (%): 79 – 81 (105oC/2h)
Posted in PO PM Industry
Lapox ARL-135 | AH-337 | aerospace, RTM, hand lay-up, infusion, low viscosity system, high Tg, high glass transition temperature
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : 300 – 380 | Glass transition temperature (Tg) (oC) : 75 – 85
Posted in PO PM Industry
Lapox ARL-135 | AH-336
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 500 – 700 | Pot life @ 25oC (minutes) : 80 – 100 | Glass transition temperature (Tg) (oC) : 75 – 85
Posted in PO PM Industry
Lapox ARL-135 | AH-335
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 500 – 700 | Pot life @ 25oC (minutes) : 50 – 60 | Glass transition temperature (Tg) (oC) : 75 – 85
Posted in PO PM Industry
Lapox ARL-135 | AH-334 GL
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 700 – 1200 | Pot life @ 25oC (minutes) : 25 – 35 | Glass transition temperature (Tg) (oC) : 80 – 90
Posted in PO PM Industry
Lapox ARL-135 | AH-333
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 700 – 1200 | Pot life @ 25oC (minutes) : 14 – 20 | Glass transition temperature (Tg) (oC) : 80 – 90
Posted in PO PM Industry
Lapox ARL-135 | AH-332
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 700 – 1200 | Pot life @ 25oC (minutes) : 8 – 14 | Glass transition temperature (Tg) (oC) : 80 – 90
Posted in PO PM Industry
Lapox L-12 | AH-411
Mixing ratio (Parts by weight) : 100 : 22 | Mix viscosity @ 25oC (mPa s) : 800 – 1,200 | Pot life @ 25oC (minutes) : 90 – 120 | Glass transition temperature (Tg) (oC) : 140 – 155
Posted in PO PM Industry
Lapox ARL-158 | AH-419
Mixing ratio (Parts by weight) : 100 : 42 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : 600 – 700 | Glass transition temperature (Tg) (oC) : 170 – 200
Posted in PO PM Industry
Lapox ARL-135 LV | AH-422
Mixing ratio (Parts by weight) : 100 : 35 | Mix viscosity @ 25oC (mPa s) : 400 – 600 | Pot life @ 25oC (minutes) : 300 – 350 | Glass transition temperature (Tg) (oC) : 110 – 120
Posted in PO PM Industry
Lapox ARL-125 | AH-368
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 200 – 300 | Pot life @ 25oC (minutes) : 350 – 450 | Glass transition temperature (Tg) (oC) : 75 – 85
Posted in PO PM Industry
Lapox ARL-125 | AH-367 GL
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 200 – 300 | Pot life @ 25oC (minutes) : 300 – 380 | Glass transition temperature (Tg) (oC) : 75 – 85
Posted in PO PM Industry
Lapox ARL-125 | AH-365 GL
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 300 – 700 | Pot life @ 25oC (minutes) : 50 – 60 | Glass transition temperature (Tg) (oC) : 75 – 85
Posted in PO PM Industry
Lapox ARL-125 | AH-336
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 300 – 700 | Pot life @ 25oC (minutes) : 80 – 100 | Glass transition temperature (Tg) (oC) : 75 – 85
Posted in PO PM Industry
Lapox ARL-125 | AH-335
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 300 – 700 | Pot life @ 25oC (minutes) : 50 – 60 | Glass transition temperature (Tg) (oC) : 75 – 85
Posted in PO PM Industry
Lapox ARL-125 | AH-334
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 600 – 750 | Pot life @ 25oC (minutes) : 25 – 35 | Glass transition temperature (Tg) (oC) : 80 – 90
Posted in PO PM Industry
Lapox ARL-125 | AH-333
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 600 – 750 | Pot life @ 25oC (minutes) : 14 – 20 | Glass transition temperature (Tg) (oC) : 80 – 90
Posted in PO PM Industry
Lapox ARL-160 | AH-357 | AC-22 | aerospace, hot melt prepreg system, structural component, sporting goods, engineering application
Mixing ratio (Parts by weight) : 100 : 15 : 1-3 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (Tg) (oC) : 110 – 120
Posted in PO PM Industry
Lapox ARL-159 | AH-619 | structural component, high temperature performance, defence, engineering application
Mixing ratio (Parts by weight) : 100 : 40 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (Tg) (oC) : 180 – 200
Posted in PO PM Industry
Lapox K-112 | accelerator and catalysts, Modified viscous tertiary amine, accelerate anhydride, accelerate polyamides, accelerate amines, composite, electrical, coating
Appearance : Clear brown liquid | Viscosity @ 25oC (mPa s) : 1,000 – 1,800
Posted in PO PM Industry
Lapox K-86 | accelerator and catalysts, Solid polyamine complex, accelerate aromatic amines
Appearance : White crystalline powder | Melting point (oC) : Min 75
Posted in PO PM Industry
Lapox AC-20 | accelerator and catalysts, accelerate anhydride, accelerate polyamides, accelerate amines, composite, electrical, coating
Appearance : Brown liquid or solid | Viscosity @ 25oC (mPa s) : Max 100 | Melting point (oC) : 36 – 42
Posted in PO PM Industry
Lapox AC-19 | accelerator and catalysts, Liquid low reactive triamine, accelerate anhydride, accelerate polyamides, accelerate amines, composite, electrical, coating
Appearance : Clear liquid | Colour (Gardner) : Max 1 | Viscosity @ 25oC (mPa s) : 10 – 30
Posted in PO PM Industry
Lapox AC-13 | accelerator and catalysts, Liquid triamine, accelerate anhydride, accelerate polyamides, accelerate amines, composite, electrical, coating
Appearance : Clear liquid | Colour (Gardner) : Max 2 | Viscosity @ 25oC (mPa s) : Max 10
Posted in PO PM Industry
Lapox AC-11
Appearance : White crystal | Melting point (oC) : Min 127 – 134
Posted in PO PM Industry
Lapox ARPN-36 (L-238) | Epoxy phenol novolac resins, semi-solid, comosites, electrical, chemical resistant coating, floorings, industrial coating
Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 5.50 – 5.70 | Viscosity @ 52oC (mPa s) : 20,000 – 50,000
Posted in PO PM Industry
Lapox ARD-59
Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 5.20 – 6.20 | Viscosity @ 25oC (mPa s) : 20 – 50 | HyCl (%) : Max 0.20
Posted in PO PM Industry
Lapox K-450
Chemistry : 3,3′-Diethyl-4,4′-diaminodiphenyl methane| Appearance : Dark brown liquid | Viscosity @ 40oC (mPa s) : 250 – 400
Posted in PO PM Industry
Lapox K-5 | aerospace, curing agent, aromatic amine, elevated temperature curing, high glass transition temperature
Chemistry : 4,4′-Diaminodiphenyl methane | Appearance : White to tan pastilles | Melting point (oC) : 88 – 92
Posted in PO PM Industry
Lapox ARFM-13 (XR-60) | Bisphenol-A/F blends, low viscosity, coating, composites, floor coating, construction
Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 5.50 – 5.75 | Viscosity @ 25oC (mPa s) : 4,500 – 6,500
Posted in PO PM Industry
Lapox ARFM-12 (XR-123) | Bisphenol-A/F blends, Medium viscosity, coating, composites, floor coating, construction
Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 5.55 – 5.80 | Viscosity @ 25oC (mPa s) : 6,500 – 8,500
Posted in PO PM Industry
Lapox B-47 | Bisphenol-A based modified liquid epoxy resin, high gloss, heavy duty flooring, solids coating, grout, crack-filling
Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 5.20 – 5.50 | Viscosity @ 25oC (mPa s) : 450 – 650
Posted in PO PM Industry
Lapox ARB-33 | Bisphenol-A based modified liquid epoxy resin, primer, mortar, grout, maintenance
Colour (Gardner) : Max 1 | Colour (AHPA) : Max 75 | Epoxy value (Eq/kg) : 5.12 – 5.55 | Viscosity @ 25oC (mPa s) : 500 – 700
Posted in PO PM Industry
Lapox ARB-32 | Bisphenol-A based modified liquid epoxy resin
Colour (Gardner) : Max 1 | Colour (APHA) : Max 150 | Epoxy value (Eq/kg) : 4.65 – 5.12 | Viscosity @ 25oC (mPa s) : 500 – 700
Posted in PO PM Industry
Lapox ARB-30 | Bisphenol-A based modified liquid epoxy resin, primer, mortar, floor coating
Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 5.00 – 5.50 | Viscosity @ 25oC (mPa s) : 4,500 – 5,500
Posted in PO PM Industry
Lapox ARD-60
Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 7.00 – 7.80 | Viscosity @ 25oC (mPa s) : 10 – 22 | HyCl (%) : Max 0.15
Posted in PO PM Industry
Lapox ARB-28 | Bisphenol-A based modified liquid epoxy resin, primer, mortar, floor coating
Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 5.00 – 5.50 | Viscosity @ 25oC (mPa s) : 1,500 – 2,000
Posted in PO PM Industry
Lapox ARB-26 | Bisphenol-A based modified liquid epoxy resin, floor coating, high gloss, defect free surface
Colour (Gardner) : Milky white liquid | Epoxy value (Eq/kg) : 4.80 – 5.10 | Viscosity @ 25oC (mPa s) : 550 – 750
Posted in PO PM Industry
Lapox ARB-22 (XR-118) | Bisphenol-A based modified liquid epoxy resin, primer, mortar, floor coating
Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 4.90 – 5.20 | Viscosity @ 25oC (mPa s) : 800 – 1,200
Posted in PO PM Industry
Lapox B-11 | standard viscosity, Bisphenol-A based unmodified liquid epoxy resin, LER, BLR
Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 5.25 – 5.45 | Viscosity @ 25oC (mPa s) : 11,000 – 15,000
Posted in PO PM Industry
Lapox B-9 | low viscosity, Bisphenol-A based unmodified liquid epoxy resin
Colour (APHA) : Max 50 | Epoxy value (Eq/kg) : 5.25 – 5.45 | Viscosity @ 25oC (mPa s) : 8,000 – 11,000
Posted in PO PM Industry
Lapox ARL-141 | high viscosity, Bisphenol-A based unmodified liquid epoxy resin, high reactivity
Colour (Gardner) : Max 2 | Epoxy value (Eq/kg) : 4.30 – 4.70 | Viscosity @ 25oC (mPa s) : 20,000 – 28,000
Posted in PO PM Industry
Lapox AR-101 | standard viscosity, Bisphenol-A based unmodified liquid epoxy resin
Colour (Gardner) : Max 1 | Epoxy value (Eq/kg) : 5.25 – 5.45 | Viscosity @ 25oC (mPa s) : 11,000 – 15,000
Posted in PO PM Industry
Lapox P-6 (ARP-19) | type 9, can coating, coil coating
Epoxy value (Eq/kg) : 0.34 – 0.42 | Viscosity @ 25oC (mPa s) : 5,000 – 10,000 | Softening point (oC) : 125 – 140
Posted in PO PM Industry
Lapox ASH-11 MIC | curing agent, sulfone, 3,3′-Diaminodiphenyl sulfone Micronised, uniform dispersion in solvent-free resin, micronised ASH-11, powder
Chemistry : 3,3′-Diaminodiphenyl sulfone Micronised | Appearance : Off-white to yellowish brown powder | Melting point (oC) : 167 – 175
Posted in None
Lapox P-4 (ARP-14) | type 4, enamels, can coating, tube coating
Epoxy value (Eq/kg) : 1.12 – 1.20 | Viscosity @ 25oC (mPa s) : 550 – 700 | Softening point (oC) : 90 – 102
Posted in PO PM Industry
Lapox ARA-32 | AH-732
Mixing ratio (Parts by weight) : 100 : 45 | Mix viscosity @ 25oC (mPa s) : Thixotropic paste | Pot life @ 25oC (minutes) : 25 – 35 | Glass transition temperature (Tg) (oC) : 75 – 85
Posted in PO PM Industry
Lapox ARA-32 | AH-733
Mixing ratio (Parts by weight) : 100 : 45 | Mix viscosity @ 25oC (mPa s) : Thixotropic paste | Pot life @ 25oC (minutes) : 50 – 70 | Glass transition temperature (Tg) (oC) : 75 – 85
Posted in PO PM Industry
Lapox ARA-32 | AH-734
Mixing ratio (Parts by weight) : 100 : 45 | Mix viscosity @ 25oC (mPa s) : Thixotropic paste | Pot life @ 25oC (minutes) : 90 – 120 | Glass transition temperature (Tg) (oC) : 75 – 85
Posted in PO PM Industry
Lapox ARA-32 | AH-735
Mixing ratio (Parts by weight) : 100 : 45 | Mix viscosity @ 25oC (mPa s) : Thixotropic paste | Pot life @ 25oC (minutes) : 130 – 170 | Glass transition temperature (Tg) (oC) : 75 – 85
Posted in PO PM Industry
Lapox A-83 | K-83 | standard adhesive, gap filling, construction adhesive
Mixing ratio (Parts by weight) : 100 : 40 | Mix viscosity @ 25oC (mPa s) : Thixotropic | Pot life @ 25oC (minutes) : 35 – 45
Posted in PO PM Industry
Lapox ARA-30 | AH-735 | structural adhesive, high lap shear strength, general purpose
Mixing ratio (Parts by weight) : 100 : 50 | Mix viscosity @ 25oC (mPa s) : 50,000 – 1,00,000 | Pot life @ 25oC (minutes) : 35 – 50
Posted in PO PM Industry
Lapox ARA-17 | AH-354 | toughness, quick, mechanical strength, general purpose
Mixing ratio (Parts by weight) : 100 : 80 | Mix viscosity @ 25oC (mPa s) : 75,000 – 1,25,000 | Pot life @ 25oC (minutes) : 8 – 10
Posted in PO PM Industry
Lapox A-16 | K-6 | marble, crack sealing, bonding, frame, construction adhesive
Mixing ratio (Parts by weight) : 100 : 10 | Mix viscosity @ 25oC (mPa s) : 4,000 – 6,000 | Pot life @ 25oC (minutes) : 20 – 30
Posted in PO PM Industry
Lapox C-51 | K-6 | electrical adhesive
Type of system : Unfilled | Nature : Cold cure / Indoor | Mixing ratio (Parts by weight) : 100 : 10 | Glass transition temperature (Tg) (oC) : 60 – 70
Posted in PO PM Industry
Lapox XR-110 | XH-68 | cable joints, construction adhesive
Mixing ratio (Parts by weight) : 100 : 100 | Mix viscosity @ 25oC (mPa s) : 3,000 – 4,000 | Pot life @ 25oC (minutes) : 25 – 35
Posted in PO PM Industry
Lapox ARA-12 | AH-718 | multi-purpose, zari, speaker, marble, ceramic, construction adhesive
Mixing ratio (Parts by weight) : 100 : 80 | Mix viscosity @ 25oC (mPa s) : 32,000 – 37,000 | Pot life @ 25oC (minutes) : 90 – 105
Posted in PO PM Industry
Lapox A-555 | K-555 | toughness, quick, mechanical strength, construction adhesive
Mixing ratio (Parts by weight) : 100 : 80 | Mix viscosity @ 25oC (mPa s) : 75,000 – 1,25,000 | Pot life @ 25oC (minutes) : 8 – 10
Posted in PO PM Industry
Lapox A-53 | K-6 | marble, steel, metal, construction adhesive
Mixing ratio (Parts by weight) : 100 : 10 | Mix viscosity @ 25oC (mPa s) : 600 – 800 | Pot life @ 25oC (minutes) : 30 – 60
Posted in PO PM Industry
Lapox A-35 | K-35 | solvent based, excellent mechanical properties, construction adhesive
Mixing ratio (Parts by weight) : 100 : 30 | Mix viscosity @ 25oC (mPa s) : 400 – 500 | Pot life @ 25oC (minutes) : > 60
Posted in PO PM Industry
Lapox A-31 | AH-717 | bonding, high shear strength, construction adhesive
Mixing ratio (Parts by weight) : 100 : 80 | Mix viscosity @ 25oC (mPa s) : 25,000 – 40,000 | Pot life @ 25oC (minutes) : 40 – 80
Posted in PO PM Industry
Lapox A-16 | K-5 | joints, hot cure, high temperature, construction adhesive
Mixing ratio (Parts by weight) : 100 : 27 | Pot life @ 25oC (minutes) : 170 – 190
Posted in PO PM Industry
Lapox A-16 | AH-800 | rapid cure, similar substrate, dissimilar substrate, construction adhesive
Mixing ratio (Parts by weight) : 100 : 100 | Mix viscosity @ 25oC (mPa s) : Thixotropic | Pot life @ 25oC (minutes) : 3 – 7
Posted in PO PM Industry
Lapox A-16 | AH-717 | marble, ceramic, metal, concrete, shock resistant, vibration resistant, construction adhesive
Mixing ratio (Parts by weight) : 100 : 80 | Mix viscosity @ 25oC (mPa s) : 15,000 – 20,000 | Pot life @ 25oC (minutes) : 150 – 200
Posted in PO PM Industry
Lapox ARL-143 | AH-335 | industrial; RTM; hand lay-up and infusion systems; moderate viscosity system; varying pot life; fire retardannt application
Mixing ratio (Parts by weight) : 100 : 15 | Pot life @ 25oC (minutes) : 85 – 95 | Mix viscosity @ 25oC (mPa s) : 3,500 – 5,000 | Glass transition temperature (Tg) (oC) : 95 – 105
Posted in PO PM Product
Lapox ARL-143 | AH-319 | industrial; RTM; hand lay-up and infusion systems; moderate viscosity system; varying pot life; fire retardannt application
Mixing ratio (Parts by weight) : 100 : 15 | Mix viscosity @ 25oC (mPa s) : 3,500 – 5,000 | Pot life @ 25oC (minutes) : 20 – 25 | Glass transition temperature (Tg) (oC) : 95 – 105
Posted in PO PM Product
Lapox ARL-135LV | AH-422 | industrial; RTM; hand lay-up and infusion systems; long pot life; high Tg; high glass trransition temperature
Mixing ratio (Parts by weight) : 100 : 35 | Mix viscosity @ 25oC (mPa s) : 400 – 600 | Pot life @ 25oC (minutes) : 300 – 350 | Glass transition temperature (Tg) (oC) : 110 – 120
Posted in PO PM Product
Lapox ARL-135LV | AH-411 | industrial; RTM; hand lay-up and infusion systems; very low viscosity; high Tg; high glass trransition temperature
Mixing ratio (Parts by weight) : 100 : 24 | Mix viscosity @ 25oC (mPa s) : 250 – 400 | Pot life @ 25oC (minutes) : 90 – 120 | Glass transition temperature (Tg) (oC) : 125 – 135
Posted in PO PM Product
Lapox ARL-135 LV | AH-334 | industrial; RTM; hand lay-up and infusion systems; low viscosity system; variable pot life
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (m Pas) : 600 – 750 | Pot life @ 25oC (minutes) : 25 – 35 | Glass transition temperature (Tg) (oC) : 75 – 85
Posted in PO PM Product
Lapox ARL-135 LV | AH-333 | industrial; RTM; hand lay-up and infusion systems; low viscosity system; variable pot life
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 700 – 1,200 | Pot life @ 25oC (minutes) : 14 – 20 | Glass transition temperature (Tg) (oC) : 80 – 90
Posted in PO PM Product
Lapox ARL-135 LV | AH-332 | industrial; RTM; hand lay-up and infusion systems; low viscosity system; variable pot life
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (m Pas) : 600 – 800 | Pot life @ 25oC (minutes) : 8 – 14 | Glass transition temperature (Tg) (oC) : 75 – 85
Posted in PO PM Product
Lapox ARL-135 | AH-337 | industrial; RTM; hand lay-up and infusion systems; moderate viscosity system; small to large components
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : 300 – 380 | Glass transition temperature (Tg) (oC) : 75 – 85
Posted in PO PM Product
Lapox ARL-135 | AH-336 | industrial; RTM; hand lay-up and infusion systems; moderate viscosity system
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 500 – 700 | Pot life @ 25oC (minutes) : 80 – 100 | Glass transition temperature (Tg) (oC) : 75 – 85
Posted in PO PM Product
Lapox ARL-135 | AH-335 | industrial; RTM; hand lay-up and infusion systems; moderate viscosity system; small to large components
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 500 – 700 | Pot life @ 25oC (minutes) : 50 – 60 | Glass transition temperature (Tg) (oC) : 75 – 85
Posted in PO PM Product
Lapox AC-20 | accelerator and catalysts; accelerate anhydride; accelerate polyamides; accelerate amines; composite; electrical; coating
Appearance : Brown liquid or solid | Viscosity @ 25oC (mPa s) : Max 100 | Melting point (oC): 36 – 42
Posted in PO PM Product
Lapox ARL-135 | AH-334GL | industrial; RTM; hand lay-up and infusion systems; moderate viscosity system; small to large components
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 700 – 1,200 | Pot life @ 25oC (minutes) : 25 – 35 | Glass transition temperature (Tg) (oC) : 80 – 90
Posted in PO PM Product
Lapox AC-19 | accelerator and catalysts; Liquid low reactive triamine; accelerate anhydride; accelerate polyamides; accelerate amines; composite; electrical; coating
Appearance : Clear liquid | Colour (Gardner) : Max 1 | Viscosity @ 25oC (mPa s) : 10 – 30
Posted in PO PM Product
Lapox ARL-125 | AH-367GL | industrial; RTM; hand lay-up and infusion systems; low viscosity system; vacuum technique; pressure bag technique
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 300 – 700 | Pot life @ 25oC (minutes) : 300 – 380 | Glass transition temperature (Tg) (oC) : 75 – 85
Posted in PO PM Product
Lapox A-16 | AH-717 | marble; ceramic; metal; concrete; shock resistance; vibration resistant; construction adhesive
Mixing ratio (Parts by weight) : 100 : 80 | Mix viscosity @ 25oC (mPa s) : 15,000 – 20,000 | Pot life @ 25oC (minutes) : 150 – 200
Posted in PO PM Product
Lapox ARL-125 | AH-365GL | industrial; RTM; hand lay-up and infusion systems; low viscosity system; vacuum technique; pressure bag technique; GL approved system
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 200 – 300 | Pot life @ 25oC (minutes) : 50 – 60 | Glass transition temperature (Tg) (oC) : 75 – 85
Posted in PO PM Product
Lapox AC-14 (K-65) | accelerator and catalysts; Liquid tertiary amine; accelerate anhydride; accelerate polyamides; accelerate amines; composite; electrical; coating
Appearance : Clear yellow liquid | Colour (Gardner) : Max 6 | Viscosity @ 25oC (mPa s) : 150 – 300 | Amine value (mg KOH/g) : 580 – 635
Posted in PO PM Product
Lapox AC-13 (K-13) | accelerator and catalysts; Liquid triamine; accelerate anhydride; accelerate polyamides; accelerate amines; composite; electrical; coating
Appearance : Clear liquid | Colour (Gardner) : Max 2 | Viscosity @ 25oC (mPa s) : Max 10
Posted in PO PM Product
Lapox ARL-160 | AH-359 | industrial; prepreg; FRP; structural component
Mixing ratio (Parts by weight) : 100 : 5 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (oC) : 110 – 120
Posted in PO PM Product
Lapox ARL-160 | AH-357 | AC-22 | industrial; prepreg; hot melt system; structural component; infrastructure; general engineering application
Mixing ratio (Parts by weight) : 100 : 15 : 1-3 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (oC) : 110 – 120
Posted in PO PM Product
Lapox ASH-11 MIC | curing agent; 3,3’-Diaminodiphenyl sulfone Micronised; 3,3′-DDS
Chemistry : 3,3’-Diaminodiphenyl sulfone Micronised | Appearance : Off-white to yellowish brown powder | Melting point (oC) : 167 – 175 | Purity by HPLC (%) : Min 99.0 | Ash content (%) : Max 0.10
Posted in PO PM Product
Lapox ASH-11 | curing agent; 3,3’-Diaminodiphenyl sulfone; 3,3′-DDS
Chemistry : 3,3’-Diaminodiphenyl sulfone | Appearance : White to brownish white powder | Melting point (oC) : 167 – 175 | Purity by HPLC (%) : Min 99.0 | Ash content (%) : Max 0.10
Posted in PO PM Product
Lapox ARL-159 | AH-619 | industrial; prepreg; structural component; high temperature performance
Mixing ratio (Parts by weight) : 100 : 40 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (oC) : 180 – 200
Posted in PO PM Product
Lapox A-16 | K-5 | joints; hot cure; high temperature; construction adhesive
Mixing ratio (Parts by weight) : 100 : 27 | Pot life @ 25oC (minutes) : 170 – 190
Posted in PO PM Product
Lapox ASH-10 FF | curing agent; 4,4’-Diaminodiphenyl sulfone Free Flow; 4,4′-DDS
Chemistry : 4,4’-Diaminodiphenyl sulfone Free Flow | Appearance : White to off-white powder | Melting point (oC) : 176 – 185 | Purity by HPLC (%) : Min 99.0 | Ash content (%) : Max 0.10
Posted in PO PM Product
Lapox ARL-159 | AH-357 | AC-22 | industrial; prepreg; hot melt system
Mixing ratio (Parts by weight) : 100 : 15 : 2 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (Tg) (oC) : 155 – 165
Posted in PO PM Product
Lapox ASH-10 MIC | curing agent; 4,4’-Diaminodiphenyl sulfone Micronised; 4,4′-DDS
Chemistry : 4,4’-Diaminodiphenyl sulfone Micronised | Appearance : White to off-white powder | Melting point (oC) : 176 – 180 | Purity by HPLC (%) : Min 99.0 | Ash content (%) : Max 0.10
Posted in PO PM Product
Lapox L-68 | K-66 | K-13 | industrial; prepregs and laminating systems; compressed laminate system; B-stage prepreg; FR-4 laminate
Mixing ratio (Parts by weight) : 100 : 32 : 1-3 | Pot life @ 25oC (weeks) : 2 – 3 | Glass transition temperature (Tg) (oC) : 130 – 140
Posted in PO PM Product
Lapox ASH-10 | curing agent; 4,4’-Diaminodiphenyl sulfone; 4,4′-DDS
Chemistry : 4,4’-Diaminodiphenyl sulfone | Appearance : White to off-white powder | Melting point (oC) : 176 – 185 | Purity by HPLC (%) : Min 99.0 | Ash content (%) : Max 0.10
Posted in PO PM Product
Lapox L-67 | K-66 | K-13 | industrial; prepregs and laminating systems; compressed laminate system; B-stage prepreg; G-10 laminate
Mixing ratio (Parts by weight) : 100 : 23 : 0.5-3.0 | Pot life @ 25oC (weeks) : 2 – 3 | Glass transition temperature (Tg) (oC) : 130 – 140
Posted in PO PM Product
Lapox AH-727 | Modified polyamide curing agent; curing agent for wet/damp condition; excellent adhesion with metal; excellent adhesion with concrete; flooring; primer
Colour (Gardner) : Max 12 | Viscosity @ 25oC (mPa s) : 1,000 – 2,000 | Amine value (mg KOH/g) : 280 – 300 | Pot life @ 25oC (minutes) : 46 – 65 | Mixing ratio (Parts by weight)…
Posted in PO PM Product
Lapox A-16 | K-6 | marble; crack sealing; bonding; frames; construction adhesive
Mixing ratio (Parts by weight) : 100 : 10 | Mix viscosity @ 25oC (mPa s) : 4,000 – 6,000 | Pot life @ 25oC (minutes) : 20 – 30
Posted in PO PM Product
Lapox AH-725 | polyamide curing agent; bonding; fast reactivity
Colour (Gardner) : Max 8 | Viscosity @ 25oC (mPa s) : 7,000 – 11,000 | Amine value (mg KOH/g) : 400 – 450 | Pot life @ 25oC (minutes) : 40 – 50 | Mixing ratio (Parts by weight)…
Posted in PO PM Product
Lapox L-12 | K-10 | K-86 | industrial; prepregs and laminating systems; compressed laminate system; B-stage prepreg; shelf life upto 6 months; G-11 laminate
Mixing ratio (Parts by weight) : 100 : 35 : 1-3 | Pot life @ 25oC (weeks) : 6 – 8 | Glass transition temperature (Tg) (oC) : 150 – 160
Posted in PO PM Product
Lapox AH-716 (K-29) | polyamide curing agent; low viscosity; solids coating; primer; floor coatings; protective coatings
Colour (Gardner) : Max 10 | Viscosity @ 25oC (mPa s) : 2,500 – 5,500 | Amine value (mg KOH/g) : 202 – 225 | Pot life @ 25oC (minutes) : 80 – 100 | Mixing ratio (Parts by weight)…
Posted in PO PM Product
Lapox L-12 | K-5 | industrial; prepregs and laminating systems; compressed laminate system; prepreg; shorter shelf life; G-10 laminate; G-11 laminate
Mixing ratio (Parts by weight) : 100 : 27 | Pot life @ 25oC (hours) : > 4 | Glass transition temperature (Tg) (oC) : 150 – 160
Posted in PO PM Product
Lapox AH-714 | polyamide curing agent; low viscosity; grouts; crack injection; primer; tile gap filling; mortar
Colour (Gardner) : Max 8 | Viscosity @ 25oC (mPa s) : 500 – 1,000 | Amine value (mg KOH/g) : 425 – 450 | Pot life @ 25oC (minutes) : 120 – 130 | Mixing ratio (Parts by weight)…
Posted in PO PM Product
Lapox ARPN-36 | K-86 | industrial; prepregs and laminating systems; compressed laminate system; B-stage prepreg
Mixing ratio (Parts by weight) : 100 : 3-6 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (Tg) (oC) : 165 – 180
Posted in PO PM Product
Lapox AH-713 (K-46) | polyamide curing agent; moderate viscosity; solids coating; primer; grouts; mortar; adhesives
Colour (Gardner) : Max 9 | Viscosity @ 25oC (mPa s) : 12,000 – 18,000 | Amine value (mg KOH/g) : 350 – 400 | Pot life @ 25oC (minutes) : 60 – 80 | Mixing ratio (Parts by weight)…
Posted in PO PM Product
Lapox ARPN-36 | K-10 | K-86 | industrial; prepregs and laminating systems; compressed laminate system; B-stage prepreg; very high Tg; very high glass transition temperature
Mixing ratio (Parts by weight) : 100 : 32-40 : 1-3 | Pot life @ 25oC (hours) : > 8 | Glass transition temperature (Tg) (oC) : 170 – 185
Posted in PO PM Product
Lapox A-35 | K-35 | solvent based; excellent mechanical properties; construction adhesive
Mixing ratio (Parts by weight) : 100 : 30 | Mix viscosity @ 25oC (mPa s) : 400 – 500 | Pot life @ 25oC (minutes) : > 60
Posted in PO PM Product
Lapox AH-712 | polyamide curing agent; high viscosity; adhesives; floorings; marine coatings; industrial paints; protective coatings
Colour (Gardner) : Max 9 | Viscosity @ 25oC (mPa s) : 45,000 – 60,000 | Amine value (mg KOH/g) : 290 – 320 | Pot life @ 25oC (minutes) : 110 – 130 | Mixing ratio (Parts by weight)…
Posted in PO PM Product
Lapox L-247 | K-918 | K-13 | industrial; filament winding and pultrusion; hot cure system; general purpose system; fire retardant
Mix viscosity @ 25oC : 100 : 64 : 1-3 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 110 – 120
Posted in PO PM Product
Lapox A-38 | K-99 | joints; moisture resistance; high adhesion; chemical resistant; construction adhesive
Mixing ratio (Parts by weight) : 100 : 40 | Mix viscosity @ 25oC (mPa s) : 50,000 – 1,00,000 | Pot life @ 25oC (minutes) : 20 – 25
Posted in PO PM Product
Lapox AH-711 | polyamide curing agent; high viscosity; adhesives; sealants
Colour (Gardner) : Max 9 | Viscosity @ 40oC (mPa s) : 50,000 – 75,000 | Amine value (mg KOH/g) : 210 – 230 | Mixing ratio (Parts by weight) : 100 – 125
Posted in PO PM Product
Lapox L-12 | K-5200 | industrial; filament winding and pultrusion; hot cure system; low viscosity system; long pot life; high chemical resistance; high abrasion resistance
Mixing ratio (Parts by weight) : 100 : 24 | Mix viscosity @ 25oC (m Pas) : 4,000 – 6,000 | Pot life @ 25oC (days) : 2 – 3 | Glass transition temperature (Tg) (oC) : 180 – 190
Posted in PO PM Product
Lapox L-12 | K-918 | K-13 | industrial; filament winding and pultrusion; hot cure system; low viscosity; long pot life system; high chemical resistance; high abrasion resistance
Mixing ratio (Parts by weight) : 100 : 85 : 1-3 | Mix viscosity @ 25oC (m Pas) : 600 – 900 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 130 –…
Posted in PO PM Product
Lapox K-541 (AH-541) | high viscosity curing agent; phenalkamine curing agent; marine coating; industrial coating
Colour (Gardner) : Max 15 | Viscosity @ 25oC (mPa s) : 15,000 – 35,000 | Amine value (mg KOH/g) : 290 – 325 | Pot life @ 25oC (minutes) : 40 – 85 | Mixing ratio (Parts by weight)…
Posted in None
Lapox A-53 | K-6 | marble; steel; metal; construction adhesive
Mixing ratio (Parts by weight) : 100 : 10 | Mix viscosity @ 25oC (mPa s) : 600 – 800 | Pot life @ 25oC (minutes) : 30 – 60
Posted in PO PM Product
Lapox L-12 | K-24 | industrial; filament winding and pultrusion; hot cure system; low viscosity system, long pot life,high chemical resistance; high abrasion resistance
Mixing ratio (Parts by weight) : 100 : 34 | Mix viscosity @ 25oC (mPa s) : 3,500 – 5,000 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 145 – 155
Posted in PO PM Product
Lapox L-12 | K-12 | K-13 | industrial; filament winding and pultrusion; hot cure system; standard system; fast reactivity
Mixing ratio (Parts by weight) : 100 : 100 : 1-3 | Mix viscosity @ 25oC (mPa s) : 400 – 700 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 95 –…
Posted in PO PM Product
Lapox L-12 | AH-667 | industrial; filament winding and pultrusion; hot cure system; high chemical resistance; high abrasion resistance
Mixing ratio (Parts by weight) : 100 : 27 | Mix viscosity @ 50oC (mPa s) : 3,000 – 5,000 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 150 – 160
Posted in PO PM Product
Lapox A-555 | K-555 | toughness; quick; mechanical strength; construction; adhesive
Mixing ratio (Parts by weight) : 100 : 80 | Mix viscosity @ 25oC (mPa s) : 75,000 – 1,25,000 | Pot life @ 25oC (minutes) : 8 – 10
Posted in PO PM Product
Lapox K-540 (AH-540) | low viscosity curing agent; phenalkamine curing agent; marine coating; industrial; maitenance coating
Colour (Gardner) : Max 15 | Viscosity @ 25oC (mPa s) : 2,000 – 4,000 | Amine value (mg KOH/g) : 490 – 550 | Pot life @ 25oC (minutes) : 30 – 55 | Mixing ratio (Parts by weight)…
Posted in None
Lapox L-12 | AH-113 | K-13 | industrial; filament winding and pultrusion; hot cure system; flame retardancy
Mixing ratio (Parts by weight) : 100 : 95 : 0.5-2.0 | Mix viscosity @ 25oC (mPa s) : 1,900 – 2,100 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 165 –…
Posted in PO PM Product
Lapox ARA-12 | AH-718 | multi-purpose; zari; speaker; marble; ceramic; construction adhesive
Mixing ratio (Parts by weight) : 100 : 80 | Mix viscosity @ 25oC (mPa s) : 32,000 – 37,000 | Pot life @ 25oC (minutes) : 90 – 105
Posted in PO PM Product
Lapox ARL-136 | AH-126 | industrial; filament winding and pultrusion; hot cure system; superior fiber wetting; excellent mechanical properties; good surface finish
Mixing ratio (Parts by weight) : 100 : 90 | Mix viscosity @ 25oC (mPa s) : 300 – 600 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 115 – 125
Posted in PO PM Product
Lapox AH-543 (XH-80) | low colour; low viscosity; phenalkamine curing agent; anti-corrosive coating; marine coating
Colour (Gardner) : Max 15 | Viscosity @ 25oC (mPa s): 2,000 – 5,000 | Amine value (mg KOH/g) : 300 – 350 | Pot life @ 25oC (minutes) : 50 – 65 | Mixing ratio (Parts by weight) :…
Posted in PO PM Product
Lapox ARF-11 | K-918 | K-13 | industrial; filament winding and pultrusion; hot cure system; non-crystallisable; excellent chemical resistance
Mixing ratio (Parts by weight) : 100 : 90 : 1-3 | Mix viscosity @ 25oC (mPa s) : 300 – 500 | Pot life @ 25oC (minutes) : > 8 | Glass transition temperature (Tg) (oC) : 115 –…
Posted in PO PM Product
Lapox K-302 | modified polyamine; curing agent; self-leveling flooring; solvent-free coating; clear casting; protective coatings
Colour (Gardner) : Max 2 | Viscosity @ 25oC (mPa s) : 300 – 600 | Amine value (mg KOH/g) : 260 – 310 | Pot life @ 25oC (minutes) : 40 – 50 | Mixing ratio (Parts by weight)…
Posted in PO PM Product
Lapox L-12 | AH-422 | industrial; filament winding and pultrusion; ambient cure system; long pot life; high Tg; high glass transition temperature
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 1,500 – 2,500 | Pot life @ 25oC (minutes) : 300 – 350 | Glass transition temperature (Tg) (oC) : 130 – 140
Posted in PO PM Product
Lapox L-12 | AH-411 | industrial; filament winding and pultrusion; ambient cure system; very high Tg; very high glass transition temperature; moderate viscosity
Mixing ratio (Parts by weight) : 100 : 22 | Mix viscosity @ 25oC (mPa s) : 800 – 1,200 | Pot life @ 25oC (minutes) : 90 – 120 | Glass transition temperature (Tg) (oC) : 140 – 155
Posted in PO PM Product
Lapox AH-440 | Cycloaliphatic amine; curing agent; accelerated curing agent; solvent-free coating; flooring; protective coatings
Colour (Gardner) : Max 2 | Viscosity @ 25oC (mPa s) : 150 – 300 | Amine value (mg KOH/g) : 335 – 375 | Pot life @ 25oC (minutes) : 25 – 40 | Mixing ratio (Parts by weight)…
Posted in PO PM Product
Lapox ARC-15 | AH-122 | Electrical and Electronics; Bushings; Conventional Vacuum Casting; Pre-filled; Hot cure Indoor
Type of system : Pre-filled | Nature : Hot cure / Indoor| Mixing ratio (Parts by weight) : 100 : 100 | Glass transition temperature (Tg) (oC) : 110 – 120 | Thermal class : H | Applications : Switchgears, Insulators, Bushings
Posted in PO PM Product
Lapox L-12 | AH-337 | industrial; filament winding and pultrusion; ambient cure system; high Tg; high glass transition temperature;variable pot life
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 400 – 700 | Pot life @ 25oC (minutes) : 300 – 380 | Glass transition temperature (Tg) (oC) : 90 – 105
Posted in PO PM Product
Lapox AH-428 | Cycloaliphatic amine; curing agent;low viscosity;fast reactivity;self-leveling;high gloss;colour stability
Colour (Gardner) : Max 1 | Viscosity @ 25oC (mPa s) : 50 – 150 | Amine value (mg KOH/g) : 340 – 390 | Pot life @ 25oC (minutes) : 30 – 40 | Mixing ratio (Parts by weight)…
Posted in PO PM Product
Lapox L-12 | AH-336 | industrial; filament winding and pultrusion; ambient cure system; high Tg; high glass transition temperature; variable pot life
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 600 – 1,200 | Pot life @ 25oC (minutes) : 80 – 100 | Glass transition temperature (Tg) (oC) : 90 – 105
Posted in PO PM Product
Lapox ARC-16 | AH-118 | ADP-11
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (Parts by weight) : 100 : 80 : 0 – 8 | Glass transition temperature (Tg) (oC) : 105 – 115 | Thermal class : F | Applications : Switchgears, Insulators, Bushings, Instrument…
Posted in PO PM Product
Lapox L-12 | AH-335 | industrial; filament winding and pultrusion; ambient cure system
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 600 – 1,200 | Pot life @ 25oC (minutes) : 50 – 60 | Glass transition temperature (Tg) (oC) : 90 – 105
Posted in PO PM Product
Lapox AH-424 | Cycloaliphatic amine; curing agent; self-leveling flooring; high filler loading; protective coatings
Colour (Gardner) : Max 2 | Viscosity @ 25oC (mPa s) : 20 – 50 | Amine value (mg KOH/g) : 330 – 360 | Pot life @ 25oC (minutes) : 25 – 35 | Mixing ratio (Parts by weight)…
Posted in PO PM Product
Lapox L-12 | AH-315 | industrial; filament winding and pultrusion; ambient cure system
Mixing ratio (Parts by weight) : 100 : 32 | Mix viscosity @ 25oC (mPa s) : 500 – 800 | Pot life @ 25oC (hours) : 7 – 9 hr | Glass transition temperature (Tg) (oC) : 85 –…
Posted in PO PM Product
Lapox AH-422 | Cycloaliphatic amine; unmodified low viscosity; curing agent; high Tg; high glass transition temperature; long pot life
Colour (Gardner) : Max 1 | Viscosity @ 25oC (mPa s) : 100 – 140 | Pot life @ 25oC (minutes) : 200 – 250 | Mixing ratio (Parts by weight) : 32
Posted in PO PM Product
Lapox ARL-138 | AH-417 | industrial; filament winding and pultrusion; ambient cure system; high Tg; high glass transition temperature
Mix viscosity @ 25oC : 200 – 300 | Pot life @ 25oC (minutes) : 90 – 120 | Glass transition temperature (Tg) (oC) : 100 – 110
Posted in PO PM Product
Lapox ARCH-11 | AH-214 | K-13
Type of system : Unfilled | Nature : Hot cure Outdoor | Mixing ratio (Parts by weight) : 100 : 90 : 0.5 – 2.0 | Glass transition temperature (Tg) (oC) : 100 – 110 | Thermal class : F | Applications : Switchgears, Insulators, Bushings, Instrument…
Posted in PO PM Product
Lapox ARL-135 LV | AH-337 | industrial; filament winding and pultrusion; ambient cure system; low viscosity resin system; variable pot life
Mix viscosity @ 25oC : 200 – 300 | Pot life @ 25oC (minutes) : 300 – 380 | Glass transition temperature (Tg) (oC) : 75 – 85
Posted in PO PM Product
Lapox ARCH-11 | AH-215
Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio (Parts by weight): 100 : 90 | Glass transition temperature (Tg) (oC) : 100 – 110 | Thermal class : F | Applications : Switchgears, Insulators, Bushings, Instrument Transformers
Posted in PO PM Product
Lapox AH-420 (K-964) | Cycloaliphatic amine; very low viscosity; moderate pot life; protective coating; flooring; chemical resistance
Colour (Gardner) : Max 3 | Viscosity @ 25oC (mPa s) : 40 – 60 | Amine value (mg KOH/g) : 320 – 340 | Pot life @ 25oC (minutes) : 25 – 40 | Mixing ratio (Parts by weight)…
Posted in PO PM Product
Lapox ARL-135LV | AH-336 | industrial; filament winding and pultrusion; ambient cure system; low viscosity resin system; variable pot life
Mix viscosity @ 25oC (mPa s) : 300 – 700 | Pot life @ 25oC (minutes) : 80 – 100 | Glass transition temperature (Tg) (oC) : 75 – 85
Posted in PO PM Product
Lapox ARCH-12 | AH-214 | K-13
Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio (Parts by weight) : 100 : 80 : 0.5 : 2.0 | Glass transition temperature (Tg) (oC) : 75 – 85 | Thermal class :…
Posted in PO PM Product
Lapox AH-416 | Cycloaliphatic amine; moderate viscosity; transparent curing agent
Colour (Gardner) : Max 1 | Viscosity @ 25oC (mPa s) : 400 – 600 | Amine value (mg KOH/g) : 250 – 300 | Pot life @ 25oC (minutes) : 30 – 45 | Mixing ratio (minutes) : 60
Posted in PO PM Product
Lapox ARL-135LV | AH-335 | industrial; filament winding and pultrusion; ambient cure system; low viscosity resin system; variable pot life
Mix viscosity @ 25oC (mPa s) : 300 – 700 | Pot life @ 25oC (minutes) : 50 – 60 | Glass transition temperature (Tg) (oC) : 75 – 85
Posted in PO PM Product
Lapox ARCH-12 | AH-215
Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio (Parts by weight) : 100 : 80 | Glass transition temperature (Tg) (oC) : 75 – 85 | Thermal class : F | Applications :…
Posted in PO PM Product
Lapox AH-412 (K-552) | Cycloaliphatic amine; low viscosity curing agent; excellent mechanical properties
Colour (Gardner) : Max 4 | Viscosity @ 25oC (mPa s) : 50 – 150 | Pot life @ 25oC (minutes) : 110 – 160 | Mixing ratio (Parts by weight) : 38
Posted in PO PM Product
Lapox AH-411 | unmodified cycloaliphatic amine curing agent; coatings; flooring applications; composite applications; protective coatings
Colour (Gardner) : Max 1 | Viscosity @ 25oC (mPa s) : 10 – 20 | Pot life @ 25oC (minutes) : 90 – 120 | Mixing ratio (Parts by weight) : 23
Posted in PO PM Product
Lapox ARCH-13 | AH-215
Type of system : Unfilled | Nature : Hot cure / Outdoor | Mixing ratio (Parts by weight) : 100 : 70 | Glass transition temperature (Tg) (oC) : 100 – 110 | Thermal class : F | Applications :…
Posted in PO PM Product
Lapox ARL-12 | AH-714 | industrial; filament winding and pultrusion; ambient cure system; superior adhesion; toughness
Mixing ratio (Parts by weight) : 100 : 50 | Mix viscosity @ 25oC (mPa s) : 1,200 – 1,500 | Pot life @ 25oC (minutes) : 120 – 150 | Glass transition temperature (Tg) (oC) : 55 – 65
Posted in PO PM Product
Lapox (AH-618) K-5200 | Aromatic amine; Elevated temperature curing curing agent; high Tg,high glass transition temperature;long pot life
Appearance : Yellow to brown liquid | Colour (Gardner) : Max 15 | Viscosity @ 25oC (mPa s) : 100 – 300 | Amine value (mg KOH/g) : 628 – 634 | Mixing ratio (Parts by weight) : 24
Posted in PO PM Product
Lapox K-450 | Aromatic amine; liquid curing agent; very low reactivity; composite
Appearance : Dark brown liquid (solidifies upon storage) | Viscosity @ 40oC (mPa s) : 250 – 400 | Amine value (mg KOH/g) : 430 – 450 | Mixing ratio (Parts by weight) : 34
Posted in PO PM Product
Lapox K-92 | Aromatic amine; ambient cure modified curing agent; chemical resistant coating; tank lining; flooring; protective coating
Appearance : Brown liquid | Colour (Gardner) : Max 13 | Viscosity @ 25oC (mPa s) : 5,000 – 7,500 | Amine value (Eq/kg) : 4.40 – 5.10 | Mixing ratio (Parts by weight) : 60
Posted in PO PM Product
Lapox C-17 | K-12 | K-13 | K-14
Type of system : Unfilled | Nature : Hot cure / Indoor | Mixing ratio (Parts by weight) : 100 : 100 : 0.5 – 1.5 : 0 – 20 | Glass transition temperature (Tg) (oC) : 85 – 95…
Posted in PO PM Product